Using X-ray diffraction (XRD) and Mössbauer spectroscopy, we have studied the sequence of phase formations in the solid Mn-doped iron silicide series Fe1−x Mn x Si2, with 0.00 ≤ x ≤ 0.12, in samples prepared by mechanical alloying from the pure elements. The milling was carried out at room temperature in Ar atmosphere in a horizontal mill for 15 h. The XRD patterns display broad lines, which can be ascribed to stable and metastable iron silicides like β-FeSi2, ɛ-FeSi, α-FeSi2, MnSi, and Si. The set of hyperfine parameters obtained support the coexistence of β-FeSi2, α-FeSi2 and ɛ-FeSi, in agreement with the XRD results. No replacement of Fe by Mn atoms in the regular sites of β-FeSi2 has been observed.
Similar content being viewed by others
References
Cho, W.-S., Choi, S.W., Park, K.: Mater. Sci. Eng., B 66, 116 (1999)
Rundqvist, S.: Acta Chem. Scand. 16, 1 (1962)
Powder diffraction files of the Joint Committee on Powder diffraction data. Georgia Institute of Technology, Atlanta, GA (1966)
Desimoni, J., Sánchez, F.H.: Hyperfine Interact. 122, 277 (1999)
Desimoni, J., Sánchez, F.H.: J. Phys., Condens. Matter. 13, 2737 (2001)
Gaffet, E., Malhouroux, N., Abdellaoui, M.: J. Alloys Compd. 194, 339 (1993)
Degroote, S., Kobayashi, T., Dekoster, J., Vantomme, A., Langouche, G.: Mater. Res. Soc. Symp. Proc. 337, 685 (1994)
Santos, D.L., de Souza, J.L., Amaral, L., Boudinov, H.: Nucl. Instrum. Methods Phys. Res., B 103, 56 (1995)
Boer, F.R., Boom, R., Mattens, W.C., Miedema, A.R., Niessen, A.K.: In: Cohesion in Metals. North-Holland, Amsterdam (1988)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Desimoni, J., Cotes, S.M., Taylor, M.A. et al. Formation of Mn-doped iron silicides by ball milling. Hyperfine Interact 168, 959–964 (2006). https://doi.org/10.1007/s10751-006-9396-0
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10751-006-9396-0