# Embrittlement of an elasto-plastic medium by an inclusion

- 572 Downloads
- 1 Citations

## Abstract

A mathematical model for the embrittlement of a long elastic-plastic crack by a relatively small, misfitting inclusion is presented. The model makes direct contact with the Dugdale–Bilby–Cottrell–Swinden model as a limiting case. The particular case of an oxide inclusion with a triangular cross-section at the tip of an intergranular crack in the Ni-based superalloy RR1000 at \(650\,^{\circ }\hbox {C}\) is considered. The positive misfit of the intrusion provides an additional tensile load on the crack tip and on the plastic zone, raising the local stress intensity factor \(k_I\) and the crack tip opening displacement \({\varDelta } u\) above those when the inclusion is replaced by a dislocation-free zone of the same length. It is shown that for a given misfit strain and inclusion shape, the enhancement of \(k_I\) and \({\varDelta } u\) is controlled by a dimensionless parameter \(\omega = (\sigma /\sigma _1)\sqrt{c/(2l)}\) where \(\sigma \) is the applied stress, \(\sigma _1\) is the yield stress, *c* is the crack length and *l* is the length of the inclusion. The anti-shielding effect of the intrusion is significant only when \(\omega \lesssim 6\). As a result of the anti-shielding effect of the intrusion, the stress singularity at the crack tip always exceeds the compressive normal stress that exists within the thickest part of the intrusion when it is isolated. It is also shown that the gradient of the hydrostatic stress within the intrusion subjected to different applied stresses drives the oxygen diffusion and, hence, assists the oxidation at the grain boundary. The fracture toughness is considerably greater than that of a bulk sample of the oxide particle, which we attribute to the plastic zone.

## Keywords

Fracture Inclusion Embrittlement Dugdale–Bilby–Cottrell–Swinden model Ni-based superalloys## 1 Introduction

When a brittle inclusion forms at a loaded crack tip it may enhance the growth of the crack by providing a path of relatively low fracture energy. An important example is the embrittlement of Ni-based superalloys due to environmental oxygen at temperatures around \(700\,^{\circ }\hbox {C}\) in rotor discs of gas turbine engines. At low temperatures, the fatigue crack growth is transgranular and is caused by localised plastic deformation at the crack tip (Liu and Oshida 1986; Andrieu et al. 1992; Bache et al. 1999; Knowles and Hunt 2002; Li et al. 2015; Cruchley et al. 2015a, b; Németh et al. 2016; Hörnqvist et al. 2014). But at temperatures around \(700\,^{\circ }\hbox {C}\) in an oxidising environment, the mode of fracture changes to intergranular. In this case oxygen enters the crack tip, diffuses along a \(\gamma /\gamma \) or \(\gamma /\gamma '\) interface and reacts to produce an oxide particle called an intrusion (McMahon and Coffin 1970; Andrieu et al. 1992; Bache et al. 1999; Knowles and Hunt 2002; Li et al. 2015; Cruchley et al. 2015a, b, 2016; Németh et al. 2016, 2017; Hörnqvist et al. 2014; Viskari et al. 2013; Pineau and Antolovich 2009). Crack growth is then enhanced through fracture of the oxide intrusion (McMahon and Coffin 1970; Andrieu et al. 1992; Cruchley et al. 2015a, b; Németh et al. 2016, 2017). The oxide materials of which the intrusion is composed are brittle in comparison to the \(\gamma \)-matrix, with fracture toughnesses typically between 0.4 and 2 MPa m\(^{1/2}\) (Evans 1995).

The stress field of a loaded intergranular crack has been widely assumed to enhance diffusion of oxygen along the grain boundary. This mechanism of failure of Ni-based superalloys at high temperatures has been called stress assisted grain boundary oxidation (SAGBO). It is quite different from the mechanism of Krupp (2005), which assumes the ingress of atomic oxygen weakens bonds at the grain boundary, resulting in decohesion. Németh et al. (2017) studied the temperature dependence of the ductility of a Ni-based superalloy in air between room temperature and \(1000\,^{\circ }\hbox {C}\). They observed a pronounced minimum in the ductility at \(750\,^{\circ }\hbox {C}\) resulting from oxidation along the \(\gamma \) grain boundaries and incoherent interfaces of \(\gamma ^\prime \) particles. This experimental study, together with the experimental work of Kitaguchi et al. (2013), provide compelling evidence that the embrittlement is a result of the formation of oxide particles at grain boundaries rather than grain boundary decohesion due to the ingress of atomic oxygen. In this paper we assume the SAGBO mechanism of failure applies to Ni-based superalloys.

As might be expected in a multi-component superalloy the oxide intrusion is a complex agglomerate of nano-scale crystals in a layered structure (Kitaguchi et al. 2013), reflecting the decreasing chemical potential of oxygen with increasing distance normal to the grain boundary. The middle of the intrusion comprises fast growing oxides such as \(\text {NiO}\) and \(\text {CoO}\), while the more thermodynamically stable oxides such as \(\text {Cr}_2\text {O}_3\) and \(\text {Al}_2\text {O}_3\), which can form at lower oxygen chemical potentials, form in the outer layers of the intrusion. The intrusion is wedge-shaped. It is some tens of nanometres thick adjacent to the crack tip, and it tapers along the grain boundary over a distance of a few microns (McMahon and Coffin 1970; Andrieu et al. 1992; Li et al. 2015; Németh et al. 2016, 2017; Viskari et al. 2013; Kitaguchi et al. 2013, 2015). The length of the intrusion is much less than the length of the crack which is hundreds of microns (Andrieu et al. 1992; Viskari et al. 2013; Németh et al. 2017). In the matrix surrounding the intrusion and crack, slip bands have been observed (Németh et al. 2016; Hörnqvist et al. 2014), indicating that the failure is not purely brittle.

Karabela et al. (2013) simulated using finite elements, fatigue crack growth and oxygen diffusion in the Ni-based superalloy RR1000. They treated the grain microstructure explicitly and adopted a power law relationship for the inelastic strain rate. The diffusion of oxygen was assumed to be primarily along grain boundaries and assisted by stresses calculated using a crystal plasticity finite element model. They optimised the parameters of the simulation using experimental data for RR1000. They then obtained a fatigue failure curve for crack growth depending on both the oxygen concentration and accumulated inelastic strain at the crack tip, which compared well with experimental results. In contrast, the approach we have taken in this paper is theoretical, providing physical insight into the influence of the oxide intrusion on the fracture of the elastic–plastic medium through explicit functional relationships.

Evans et al. (2013) argued that diffusion of oxygen along the grain boundary is enhanced principally by creating a difference in the chemical potential of oxygen vacancies between the *ends* of the intrusion, and that the gradient of stress *within* the intrusion has a negligible effect. But to estimate the enhanced diffusion they assumed the variation of the normal stress within the intrusion ahead of the crack. In this paper we find the assumed variation in Evans et al. (2013) differs significantly from the profile we derive, most notably we find the intrusion adjacent to the crack tip is always loaded in tension for experimentally observed intrusion geometries. In addition, we find the gradient of the hydrostatic stress within the intrusion is consistent with experimental observations (Kitaguchi et al. 2013) of the growth of oxide intrusions under different loading conditions.

Chan (2014) argued that an oxide intrusion, with a larger volume per Ni atom than the Ni-matrix, induces a *compressive* stress in the matrix and thus screens the crack tip. We find the opposite. In addition, Chan’s use of the superposition principle of linear elasticity does not satisfy the boundary condition that the crack faces are free of tractions. In this paper we use the superposition principle in a self-consistent approach that satisfies the boundary conditions on the stress field.

The outline of the paper is as follows. In the next section we describe the geometry of the mathematical model, which includes a long crack, a misfitting intrusion at the crack tip, and a plastic zone ahead of the intrusion tip. In Sect. 3 we calculate the stress field of the isolated misfitting intrusion with a triangular cross-section in an infinite elastic medium with no applied stress. The superposition principle is used in Sect. 4 to add the stress field of the intrusion to the applied normal stress on the long crack. This is done by replacing the long crack by a semi-infinite crack and setting up an integral equation for the Burgers vector density of dislocations representing the crack and the plastic zone. The condition for the normal stress to be bounded at either end of the plastic zone enables the size of the plastic zone to be determined. This condition leads to the solution of the integral equation for the Burgers vector density, from which the crack tip opening displacement, the stress field, the local stress intensity factor at the crack tip, and the associated J-integrals are determined. A dimensionless parameter, which we call \(\omega \), emerges from the analysis. It shows how the applied normal stress, the yield stress, the crack length, and the length of the intrusion conspire to control the influence of the intrusion on the embrittlement of the medium.

## 2 The geometry of the model

*c*in the plane \(y=0\), between \(x=-c\) and \(x=0\), and which is infinitely extended along the

*z*-axis. There is a uniform applied stress \(\sigma _{yy} = \sigma \) at \(y=\pm \,\infty \). The stress intensity factor of the crack is \(K_I = \sigma \sqrt{\pi c}\). Ahead of the crack there is a grain boundary occupying the half-plane \(y=0\), \(x \ge 0\). We assume there is an oxide intrusion at the crack tip with a triangular cross-section, and infinitely long along the

*z*-axis, as shown in Fig. 1. The base of the intrusion is at the crack-tip and has width t, and its tip is at \(x=l\ge 0\). We assume a plastic zone between \(x=l\) and \(x=a>l\), and infinitely extended along the

*z*-axis, in which the stress is constant and equal to the yield stress, \(\sigma _1\). In line with experimental observations we assume the crack is much longer than the intrusion, \(c \gg l\). This is a plane strain model because the strain tensor has non-zero components \(e_{xx}, e_{yy}, e_{xy}\) only. As the length

*l*of the intrusion tends to zero the plastic zone approaches the crack tip and the model becomes equivalent to the DBCS-model (Dugdale 1960; Bilby et al. 1963) with a long crack. As the angle at the tip of the intrusion tends to zero the intrusion vanishes and it is replaced by a dislocation-free zone (DFZ) occupying the region \(0 \le x \le l\). We call this limit the DFZ-model (Chang and Ohr 1981, 1983; Ohr and Chang 1982; Majumdar and Burns 1983; Weertman et al. 1983). These models are instructive limiting cases for comparison to our model.

## 3 The intrusion

### 3.1 The stress tensor

For simplicity we assume the elastic constants of the intrusion are those of the surrounding isotropic elastic medium. The intrusion is assumed to be homogeneous and to be characterised only by its volumetric misfit. Assuming the intrusion is composed of \(\text {NiO}\) the volumetric misfit is \({\varPhi }=1.65\) (Evans 1995). That is, when the intrusion forms its stress-free volume is 1.65 times greater than the volume occupied by the same number of nickel atoms in the superalloy. Assuming the dilatation is isotropic the linear misfit strain is then \(\epsilon _\text {m}=\root 3 \of {{\varPhi }}-1=0.18\).

Let the interface between the intrusion and the matrix be labelled \({\varGamma }\). We associate with \({\varGamma }\) a continuous distribution of dislocations, which generates the elastic field of the intrusion. In Fig. 2 the dimensions of the intrusion are those of a triangular prism of the Ni-matrix before it has been oxidised. The interface \({\varGamma }\) comprises a vertical interface, \({\varGamma }_0\), and two inclined interfaces \({\varGamma }_{+}\) and \({\varGamma }_{-}\) (see Fig. 2). The intrusion semi-angle is \(\theta =\arctan \left[ t/2l\right] \). TEM observations show that \(\theta \ll 1\) (Kitaguchi et al. 2013). Since \(t \ll l\) we assume the 18% misfit along *y* is accommodated elastically. That is, the interface \({\varGamma }\) is in a state of forced elastic coherence along the *y*-axis. This is modelled by a continuous distribution of edge dislocations with infinitesimal Burgers vectors along the negative *y*-axis, and with their lines parallel to *z*, consistent with the FS/RH convention. But since the interface along the *z*-axis is infinitely long we assume it is fully incoherent along *z*, that is there are no dislocations with Burgers vectors along *z*. Similarly, since \(l \gg t\) we assume the interfaces cannot sustain coherency along the *x*-direction and therefore these interfaces do not have dislocations with Burgers vectors parallel to *x*. Figure 2 shows schematically the continuous distribution of interfacial edge dislocations with Burgers vectors along \(-y\) and infinitely long lines parallel to *z* forming loops closed at \(z=\pm \, \infty \). The elastic field of the intrusion is generated by this continuous distribution of dislocations.

### 3.2 The hydrostatic stress along the *x*-axis

*x*-axis, \(\sigma ^I(x,0) = \frac{1}{3}\sum _\alpha \sigma ^I_{\alpha \alpha }(x,0)\):

*H*(

*x*) denotes the Heaviside step function. We note that as \(\theta \rightarrow 0\), \(\sigma ^I(x,0)\rightarrow 0\), as it should because in this limit the intrusion vanishes. But when \(\theta >0\), the hydrostatic stress is discontinuous at \(x=0\). The discontinuity does not depend on the intrusion angle throughout the range \(0<\theta \le \pi /2\):

*x*-axis is plotted in Fig. 3 for RR1000 as an illustration of (5). The hydrostatic stress is tensile on the

*x*-axis at all intrusion angles just outside the intrusion and compressive just inside at \(x=0\). As expected the thickest part of the intrusion is always in compression. At the apex of the intrusion the hydrostatic stress is always tensile both inside and outside the intrusion, diverging logarithmically as the tip is approached from both sides along the

*x*-axis.

### 3.3 The normal stress along the *x*-axis

## 4 The intrusion at the crack tip

In this section we use the stress field of the intrusion to calculate the stress field and related properties of the whole model portrayed in Fig. 1.

### 4.1 The approximation of a semi-infinite crack

*y*-axis and lines parallel to the

*z*-axis, consistent with the FS/RH convention. The total traction at any point on the faces of the crack must be zero. The sources of the traction are the stress fields of the dislocations comprising the crack, the applied load \(\sigma \), and the stresses created by the intrusion and dislocations in the plastic zone. The

*xy*-component of the total stress tensor on the crack faces is zero by virtue of the mirror symmetry in the plane \(y=0\). The

*yz*-component of the total stress tensor on the crack faces is zero because the strain field is confined to the \(x-y\) plane. Therefore, only the

*yy*component of the total stress tensor on the crack faces has to be considered. For the plastic zone we assume the

*yy*-component of the total stress tensor is a constant, \(\sigma _1\), which we interpret as the yield stress. Let \(L_c\) denote the set of points along the

*x*-axis occupied by the crack, \(-c\le x\le 0\), and the plastic zone \(l \le x\le a\), where \(c \gg l, a\). In \(L_c\) the Burgers vector density of the dislocations is \(b_c(x)\). Then, at any point

*x*in the crack or plastic zone we require the following singular integral equation to be satisfied:

*x*is in the plastic zone, otherwise it is zero. In this equation the addition of the intrusion stress tensor, \(\sigma _{yy}^I\), to the applied load \(\sigma \) is an application of the superposition principle.

In (8) we see that the integral extends over the entire crack length, *c*, and the plastic zone. But provided *c* is much larger than the intrusion and the plastic zone it is otherwise arbitrary. This dependence on *c* complicates the analysis unnecessarily and it may be removed, as we now show.

We have already noted in Fig. 4 that the stress \(\sigma _{yy}^I(x,0)\) generated by the intrusion is negligible at distances along the *x*-axis from the intrusion of more than twice its length. In small-scale yielding the field of the plastic zone is also short ranged compared to the crack length. Therefore, the intrusion and plastic zone modify the distribution of Burgers vectors in the crack only in the vicinity of its tip at \(x=0\). Conversely, the intrusion and plastic zone are in the near-tip stress field of the crack. Summarising, the Burgers vector density inside the crack is modified by the intrusion and plastic zone near the tip at \(x=0\) only, and the intrusion and plastic zone are located in the stress field \(\sigma _{yy}(x,0)\) of the crack only slightly ahead of this tip.

*c*, occupying \(-2c \le x \le 0\) and \(y=0\), in an infinite elastic medium. The crack is subjected to an applied normal load \(\sigma \) at \(y=\pm \,\infty \), and the intrusion and plastic zone are absent. Our crack of length

*c*will be modelled as half of this crack of length 2

*c*, occupying \(-c \le x \le 0\). We view \(b_{e}(x)\) as an unperturbed Burgers vector density of an elastic crack because it is not disturbed by the plastic zone or intrusion. It is well known, e.g. Lardner (1974), that \(b_{e}(x)\) is as follows:

*c*in (8) with \(b_e^{(0)}(x)\) in a semi-infinite crack we must remove the applied stress \(\sigma \) from the right hand side of the equation. Equation (8) then becomes:

*L*extends from \(x^\prime = -\infty \) to \(x^\prime = 0\) and from \(x^\prime = l\) to \(x^\prime = a\), and

*b*(

*x*) is the Burgers vector density of the dislocations in

*L*. Thus, the removal of the dependence on the crack length

*c*from the equilibrium condition in (8) has been achieved without compromising the accuracy of the model in the crucial region near the crack tip. Attention can now be focused on the Burgers vector density

*b*(

*x*) in this region, where the interaction with the intrusion and plastic zone dominate.

### 4.2 The solution of the integral equation

*m*is the parameter,

*n*is the characteristic, and the amplitude \(\phi =\arctan \left[ \sqrt{\left( \dot{\imath }\tan ^{}\theta -1\right) /\left( 1-\dot{\imath }\,\eta \tan ^{}\theta \right) }\right] \). There is ambiguity in the definitions of the elliptic integrals in the literature. In the Appendix we state the definitions used in this paper for the incomplete and complete elliptic integral of the first, second and third kinds. Here and elsewhere in this paper we assume \(\sigma _0/\sigma _1 = 3\) as in RR1000 at \(650\,^{\circ }\hbox {C}\). The variable \(\omega \equiv (\sigma /\sigma _1)\sqrt{c/(2l)}\) is a ratio of stress intensity factors, combining the applied stress \(\sigma \), the yield stress \(\sigma _1\), the crack length

*c*and the length of the intrusion

*l*into a single dimensionless variable.

*We will show that the conditions under which the intrusion embrittles the material are described by a limited range of values of*\(\omega \).

The solution of (15) for \(\eta \) is plotted in Fig. 5 for four values of the intrusion semi-angle. When \(\theta = 0\) there is no intrusion. The presence of the intrusion increases the size of the plastic zone. As \(\theta \) increases the size of the plastic zone increases for a given value of \(\omega \). We note that even when the applied stress is compressive (so that \(\omega <0\)) there is still a plastic zone ahead of the intrusion. All these features stem from the tensile normal stress ahead of the intrusion seen in Fig. 4, which increases with \(\theta \).

*b*(

*x*) becomes:

*complete*elliptic integral of the third kind. Also, \(j(z)=\dot{\imath }\sqrt{\left[ a(z-a)\right] /\left[ z(z-l)\right] }\).

### 4.3 The crack tip opening displacement

*K*(

*m*) is the complete elliptic integral of the first kind, and \(F(\phi | m)\) and \(E(\phi | m)\) are the incomplete elliptic integrals of the first and second kind, respectively. This expression for \({\varDelta } u\) is plotted in Fig. 6, where it is normalised to the crack tip opening displacement \({\varDelta } u_0= 2 a \sigma _1/(A\pi ^2)\) in the DBCS-model. The length of the plastic zone is \(a\ll c\). When \(\theta =0\), taking the limit as \(l \rightarrow 0\), we recover the DBCS-model and the crack tip opening displacement approaches \({\varDelta } u_0\). But in the presence of an intrusion (i.e. \(\theta > 0\)), the crack tip opening displacement increases with \(\theta \) at a given value of \(\omega \). This is consistent with Fig. 5 where the size of the plastic zone increases with \(\theta \) for a given value of \(\omega \). The asymptotic behaviour of all the curves in Fig. 6 at large values of \(\omega \) reflects the diminishing significance of the intrusion as the intrusion length

*l*decreases relative to the crack length

*c*, and as the applied stress \(\sigma \) increases relative to the yield stress \(\sigma _1\).

### 4.4 The normal stress along the *x*-axis

*b*(

*x*) (16) in the crack and plastic zone, and by the intrusion. The total stress tensor, \(\sigma _{\alpha \beta }(\mathbf{x})\), is given by the superposition principle of linear elasticity:

*x*-axis it is as follows:

It is interesting to compare the solid curve in Fig. 7, showing \(\sigma _{yy}\left( x,0\right) \) when there is no applied stress \((\omega =0)\), with the curve in Fig. 4 for \(\theta = 5^{\circ }\), showing the stress generated by the intrusion only. The presence of the crack tip singularity in Fig. 7, and its absence in Fig. 4, puts *both* ends of the intrusion into normal tension in Fig. 7, although at the thicker end of the intrusion (\(x = 0^+\)) the tensile region is very narrow at the smallest values of \(\omega \). This feature persists even when the applied load is slightly compressive (\(\omega =-\,1\)).

In Fig. 8 we show the normal stress \(\sigma _{yy}\left( x,0\right) \) when \(\omega =4\) for four values of intrusion semi-angle \(\theta \). As the intrusion semi-angle decreases the normal stress \(\sigma _{yy}\left( x,0\right) \) inside the intrusion becomes increasingly tensile; when \(\theta = 5^{\circ }\) there is only a very small part of the *x*-axis where the normal stress is compressive.

### 4.5 The hydrostatic stress along the *x*-axis

*x*-axis, \(\sigma (x,0) = \frac{1}{3}\sum _\alpha \sigma _{\alpha \alpha }(x,0)\):

### 4.6 The local stress intensity factor

In Fig. 10 we plot \(k_\text {I}/K_{\text {I}}\) as a function of \(\omega \) for four values of the intrusion semi-angle \(\theta \). Taking the limit \(l\rightarrow 0\) in (22) we obtain \(k_\text {I}=0\) because the model then becomes equivalent to the DBCS-model where the crack tip is completely screened by the plastic zone. This is also evident in Fig. 10 where \(k_\text {I}/K_{\text {I}}\rightarrow 0\) as \(\omega \rightarrow \infty \).

*l*of the intrusion. The size of the plastic zone increases with increasing \(\omega \), as seen in Fig. 5, which increasingly screens and blunts the crack tip. A more ductile material, characterised by a smaller value of the yield stress \(\sigma _1\), or a larger applied stress \(\sigma \), reduces the stress intensification at the crack tip caused by the intrusion. When \(\theta = 30^{\circ }\) the larger plastic zone screens the crack more effectively and \(k_I\) is lower than that for \(\theta = 5^{\circ }\) and \(15^{\circ }\), as seen in Fig. 10.

### 4.7 J-integrals

## 5 Discussion

By comparing Figs. 4 and 7 it is seen that the normal stresses within the intrusion differ significantly, *even when there is no applied stress*, from a linear superposition of the stress fields of the isolated intrusion (7), and the unloaded crack. It highlights the point made in the Introduction, with reference to the work of Chan (2014), of the necessity of satisfying the boundary conditions of traction free surfaces in the crack and a constant normal stress in the plastic zone, when the normal stress within the intrusion is calculated.

Figures 7 and 8 show the variation of the normal stress within the intrusion subjected to different values of \(\omega \) and to different intrusion semi-angles \(\theta \), respectively. It is seen that for experimentally observed intrusion geometries there is always a positive stress concentration at the crack tip, which generates a tensile region inside the thickest part of the intrusion. This tensile stress decreases with distance from the crack tip and, when \(\omega \) is sufficiently small, it becomes compressive, gradually becoming tensile again towards the intrusion tip. At the intrusion tip the normal stress is tensile and is approximately equal to \(\sigma _1\). This behaviour of the normal stress indicates that at moderate values of \(\omega \) (\(\omega < 4\)) the crack will penetrate the intrusion during crack growth.

Figure 9 shows the variation of the hydrostatic stress within the intrusion subjected to different applied loads. It is seen that when there is no applied load (\(\omega = 0\)) the gradient of the hydrostatic stress within the intrusion encourages the drift of oxygen vacancies from the intrusion tip towards the crack tip, and hence the diffusion of oxygen atoms in the opposite direction. The gradient is reduced to almost zero when \(\omega = 4\) and when \(\omega =40\) its sign is reversed. This suggests that the intrusion will grow to a larger size when there is no applied load, which is supported by the experimental observations of Kitaguchi et al. (2013). In their work on RR1000, the intrusions at static crack tips were examined following two loading conditions each for 5 h at \(650\,^{\circ }\hbox {C}\) in an oxidising environment. One of the loads was close to zero, and the other was slightly less than the threshold for crack-growth. The intrusion formed under almost zero load was significantly longer. In contrast, Evans et al. (2013) suggested that oxygen diffusion is dominated by the stress at the ends of the intrusion (i.e. \(x=0\) and \(x=l\)). But in Fig. 9 we see that if that were true the growth of the intrusion would be independent of the applied load. We conclude that the origin of the enhancement of oxygen diffusion in SAGBO is primarily the gradient of the hydrostatic stress within the intrusion, and not the hydrostatic stresses at the ends of the intrusion.

The local stress intensity factor \(k_I\), normalised to the applied stress intensity factor \(K_I\), is shown in Fig. 10 as a function of \(\omega \) for four values of the intrusion semi-angle \(\theta \). Since an intrusion raises the local stress intensity factor above that of the DFZ-model, which corresponds to \(\theta =0\), it follows that the intrusion always provides an additional tensile load on the crack tip. This additional tensile load is clearly visible in the region \(-2l \lesssim x\le 0\) of Fig. 4. The force acting to advance the crack tip, as determined by \(J_x(S_2)\) in (23), is proportional to \(k_1^2\), and therefore it is also raised by the presence of the intrusion.

If we adopt the fracture criterion that \(k_I\) has to exceed a critical value then as we increase the applied load from zero, fracture of the intrusion will occur so long as \(k_I\) exceeds the critical value. As the crack grows from *c* to \(c+\delta c\), it penetrates the intrusion by \(\delta c\) and the effective length *l* of the intrusion decreases to \(l-\delta c\). At a given applied stress \(\sigma \) and yield stress \(\sigma _1\), the variable \(\omega \) then increases because \(\delta \omega \approx (\omega /(2l))\delta c\), where the approximation assumes \(c\gg l\). Thus if \(\delta c > 0\) then \(\delta \omega >0\) for constant values of \(\sigma \) and \(\sigma _1\).

It follows that if the crack is arrested inside the intrusion further crack growth will resume only when the intrusion has grown by further oxidation, thereby increasing *l* and raising \(k_I\) above the critical value. Thus, we may envisage steady-state crack growth with the crack tip always inside the intrusion, where the rate of crack growth is equal to the rate of growth of the oxide intrusion ahead of the crack.

*compressive*stresses inside the intrusion just ahead of the crack. However, we have seen in Fig. 4 that the intrusion loads the crack in tension. And, as seen in Fig. 7 this tensile loading creates a

*tensile*stress singularity just ahead of the crack, even when there is no externally applied load. We suggest the increased fracture toughness of the oxide intrusion, as compared with bulk samples of oxide material, originates from the plastic zone, which exists even when there is no externally applied load.

## 6 Conclusions

A mathematical model has been developed to provide physical insight into the embrittlement of a long elastic–plastic crack by a relatively small, misfitting inclusion through functional relationships. In particular, we addressed the important example of the embrittlement of the Ni-based superalloys RR1000 at \(650\,^{\circ }\hbox {C}\) caused by an oxide intrusion.

The dimensionless parameter \(\omega =(\sigma /\sigma _1)/\sqrt{c/(2l)}\) emerges from the analysis, where \(\sigma \) is applied normal stress, \(\sigma _1\) is the yield stress, *c* is the crack length, and *l* is the length of the intrusion. This variable is key to understanding the embrittlement caused by the intrusion. We find the intrusion has a marked influence only when \(\omega \lesssim 6\). At larger values of \(\omega \) the intrusion is too small to have a detrimental effect on the fracture toughness of the alloy.

The intrusion is always ‘anti-shielding’, adding to a tensile applied load on the crack tip. Even in the absence of an externally applied load the tensile load on the crack tip arising from the intrusion creates a square root singularity in the stress field at the crack. In turn this singularity exceeds the compressive normal stress that exists within the thickest part of the intrusion when it is isolated, making it tensile. As a result, the intrusion fails near the crack tip because it is the region where the tensile stress is highest. When the crack advances into the intrusion the local stress intensity factor \(k_I\) on the crack tip decreases with increasing crack length, because the effective length *l* of the intrusion decreases raising \(\omega \) and lowering \(k_I\). Thus, it is possible that this reduction arrests the crack advance inside the intrusion. In that case we may envisage a steady state where the rate of crack growth is equal to the rate of growth of the intrusion ahead of the crack, and the plastic zone is continuously regenerated ahead of the intrusion. As a result of the anti-shielding effect of the intrusion both the local stress intensity factor \(k_I\) and the length of the plastic zone, are increased compared to the case where the intrusion is replaced by a dislocation free zone of the same length. Similarly, the crack tip opening displacement \({\varDelta } u\) is increased. Although the intrusion embrittles the medium, the fracture toughness is larger than that of the bulk oxide because the plastic zone ahead of the intrusion shields the crack tip.

The experimental observations of Kitaguchi et al. (2013) and Fig. 9 support the view that it is the gradient of the hydrostatic stress within the intrusion that is responsible for the enhancement of oxygen diffusion through the intrusion, and hence the increased rate of growth of the intrusion.

## Notes

### Acknowledgements

Useful discussions were held with Professor Hugh Evans of the University of Birmingham, and with Professor Daniele Dini of Imperial College London. LC was supported by the EPSRC Centre for Doctoral Training on Theory and Simulation of Materials at Imperial College London under Grant EP/L015579/1, and by Rolls-Royce plc.

## Supplementary material

## References

- Abramowitz M, Stegun IA (eds) (1972) Chapter 17 in Handbook of mathematical functions, 9th printing. Dover, New York, pp 587–607Google Scholar
- Andrieu E, Molins R, Ghonem H, Pineau A (1992) Intergranular crack tip oxidation mechanism in a nickel-based superalloy. Mater Sci Eng A 154:21–28CrossRefGoogle Scholar
- Bache MR, Evans WJ, Hardy MC (1999) The effects of environment and loading waveform on fatigue crack growth in Inconel 718. Int J Fatigue 21:S69–S77CrossRefGoogle Scholar
- Bilby BA, Cottrell AH, Swinden KH (1963) The spread of plastic yield from a notch. Proc R Soc Lond A Math Phys Eng Sci 272:304–314Google Scholar
- Chan KS (2014) Time-dependent crack growth thresholds of Ni-base superalloys. Metall Mater Trans A 45:3454–3466CrossRefGoogle Scholar
- Chang SJ, Ohr SM (1981) Dislocation\(-\)free zone model of fracture. J Appl Phys 52:7174–7181CrossRefGoogle Scholar
- Chang SJ, Ohr SM (1983) Distribution function of dislocations and condition of finite stress for the dislocation-free zone model of fracture. Int J Fracture 23:R3–R6CrossRefGoogle Scholar
- Cruchley S, Li HY, Evans HE, Bowen P, Child DJ, Hardy MC (2015a) The role of oxidation damage in fatigue crack initiation of an advanced Ni-based superalloy. Int J Fatigue 81:265–274CrossRefGoogle Scholar
- Cruchley S, Taylor MP, Li HY, Evans HE, Bowen P, Child DJ, Hardy MC (2015b) Effect of prior oxidation on high cycle fatigue performance of RR1000 and role of oxidation in fatigue crack initiation. Mater High Temp 32:68–73CrossRefGoogle Scholar
- Cruchley S, Evans H, Taylor M (2016) An overview of the oxidation of Ni-based superalloys for turbine disc applications: surface condition, applied load and mechanical performance. Mater High Temp 33:465–475CrossRefGoogle Scholar
- Dugdale DS (1960) Yielding of steel sheets containing slits. J Mech Phys Solids 8:100–104CrossRefGoogle Scholar
- Eshelby JD (1951) The force on an elastic singularity. Philos Trans R Soc Lond A 244:87–111CrossRefGoogle Scholar
- Eshelby JD (1956) The continuum theory of lattice defects. Solid State Phys 3:79–144CrossRefGoogle Scholar
- Evans HE (1995) Stress effects in high temperature oxidation of metals. Int Mater Rev 40:1–40CrossRefGoogle Scholar
- Evans HE, Li HY, Bowen P (2013) A mechanism for stress-aided grain boundary oxidation ahead of cracks. Scr Mater 69:179–182CrossRefGoogle Scholar
- Hörnqvist M, Viskari L, Moore KL, Stiller K (2014) High-temperature crack growth in a Ni-base superalloy during sustained load. Mater Sci Eng A 609:131–140CrossRefGoogle Scholar
- Karabela A, Zhao LG, Lin B, Tong J, Hardy MC (2013) Oxygen diffusion and crack growth for a nickel-based superalloy under fatigue-oxidation conditions. Mater Sci Eng A 567:46–57CrossRefGoogle Scholar
- Kitaguchi HS, Li HY, Evans HE, Ding RG, Jones IP, Baxter G, Bowen P (2013) Oxidation ahead of a crack tip in an advanced Ni-based superalloy. Acta Mater 61:1968–1981CrossRefGoogle Scholar
- Kitaguchi HS, Moody MP, Li HY, Evans HE, Hardy MC, Lozano-Perez S (2015) An atom probe tomography study of the oxide-metal interface of an oxide intrusion ahead of a crack in a polycrystalline Ni-based superalloy. Scr Mater 97:41–44CrossRefGoogle Scholar
- Knowles DM, Hunt DW (2002) The influence of microstructure and environment on the crack growth behavior of powder metallurgy nickel superalloy RR1000. Metall Mater Trans A 33:3165–3172CrossRefGoogle Scholar
- Krupp U (2005) Dynamic embrittlement—time-dependent quasi-brittle intergranular fracture at high temperatures. Int Mater Rev 50:83–97CrossRefGoogle Scholar
- Lardner RW (1974) Mathematical theory of dislocations and fracture. University of Toronto Press, TorontoGoogle Scholar
- Li HY, Sun JF, Hardy MC, Evans HE, Williams SJ, Doel TJ, Bowen P (2015) Effects of microstructure on high temperature dwell fatigue crack growth in a coarse grain PM nickel based superalloy. Acta Mater 90:355–369CrossRefGoogle Scholar
- Liu HW, Oshida Y (1986) Grain boundary oxidation and fatigue crack growth at elevated temperatures. Theor Appl Fract Mech 6:85–94CrossRefGoogle Scholar
- Majumdar BS, Burns SJ (1983) A Griffith crack shielded by a dislocation pile-up. Int J Fracture 21:229–240CrossRefGoogle Scholar
- McMahon CJ, Coffin LF (1970) Mechanisms of damage and fracture in high-temperature, low-cycle fatigue of a cast nickel-based superalloy. Metall Mater Trans B 1:3443–3450Google Scholar
- Németh AA, Crudden DJ, Collins DM, Armstrong DE, Reed RC (2016) Novel techniques to assess environmentally-assisted cracking in a nickel-based superalloy. In: Superalloys 2016: proceedings of the 13th international symposium of superalloys. Wiley, pp 801–810Google Scholar
- Németh AA, Crudden DJ, Armstrong DE, Collins DM, Li K, Wilkinson AJ, Grovenor CR, Reed RC (2017) Environmentally-assisted grain boundary attack as a mechanism of embrittlement in a nickel-based superalloy. Acta Mater 126:361–371CrossRefGoogle Scholar
- Ohr SM, Chang SJ (1982) Dislocation\(-\)free zone model of fracture comparison with experiments. J Appl Phys 53:5645–5651CrossRefGoogle Scholar
- Pineau A, Antolovich SD (2009) High temperature fatigue of nickel-base superalloys—a review with special emphasis on deformation modes and oxidation. Eng Failure Anal 16:2668–2697CrossRefGoogle Scholar
- Rice JR (1968) A path independent integral and the approximate analysis of strain concentration by notches and cracks. J Appl Mech 35:379–386CrossRefGoogle Scholar
- Viskari L, Hörnqvist M, Moore KL, Cao Y, Stiller K (2013) Intergranular crack tip oxidation in a Ni-base superalloy. Acta Mater 61:3630–3639CrossRefGoogle Scholar
- Weertman J, Lin IH, Thomson R (1983) Double slip plane crack model. Acta Metall 31:473–482CrossRefGoogle Scholar

## Copyright information

**OpenAccess**This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.