Abstract
In this paper the influence of microstructure on fatigue crack growth was analysed in steel with slightly hypereutectoid composition. A material constituted of pearlite colonies and a thin layer of proeutectoid cementite (pearlitic steel) was studied in its initial condition (as received). In addition, the same material was analyzed after undergoing a spheroidization treatment obtained by an isothermal treatment on pearlitic steel at 700ºC and heating time of 10h. Results indicate that fatigue crack propagation curve in the Paris region is not modified by the spheroidization process. Fractometallographic analysis showed a change in the micromechanism of fatigue, evolving from transcollonial (trying to break pearlite lamellae) in the pearlitic steel to intergranular in the spheroidized steel, where cracking takes place through the layer of proeutectoid cementite.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Astiz M.A. (1986) An incompatible singular elastic element for two- and three-dimensional crack problems. International Journal of Fracture 31(2): 105–124
Chattopadhyay S., Sellars C.M. (1982) Kinetics of pearlite spheroidisation during static annealing and during hot deformation. Acta Metallurgica 30(1): 157–170
Fernández-Vicente A., Carsí M., Peñalba F., Taleff E., Ruano O.A. (2002) Toughness dependence on the microstructural parameters for an ultrahigh carbon steel (1.3 wt.% C). Materials Science and Engineering A 335(1-2): 175–185
Firrao D., Anzalone S.A., Begley J.A. (1984) The influence of carbide morphology on the upper-shelf fracture toughness (JIC) of carbon steels. Metallurgical Science and Technology 2(1): 15–23
Karlsson B., Lindén G. (1975) Plastic deformation of eutectoid steel with different cementite morphologies. Materials Science and Engineering 17(1): 153–164
Kim E.S., Kim I.S. (2000) Effect of spheroidization on the near-threshold fatigue crack growth in ferrite-pearlite steel. Journal of Materials Science Letters 19(5): 367–369
Milligan R. (1974) The role of carbide morphology on low-cycle-fatigue behavior of iron-carbon alloys. Experimental Mechanics 14(5): 190–195
Nagase Y., Kanri T. (1992) Effects of small prestrain on the fatigue behaviour of spheroidal pearlite steel. Fatigue & Fracture of Engineering Materials & Structures 15(2): 213–223
Paris P.C., Erdogan F. (1963) A critical analysis of crack propagation laws. Journal of Basic Engineering 85D: 528–534
Rosenfield A., Hahn G., Embury J. (1972) Fracture of steels containing pearlite. Metallurgical and Materials Transactions B 3(11): 2797–2804
Savrai R., Makarov A., Schastlivtsev V., Tabatchikova T., Yakovleva I., Egorova L. (2010) Behavior of pearlite of various morphologies during cyclic tension. Russian Metallurgy (Metally) 2010(4): 310–315
Toribio J., Matos J.C., González B. (2009) Micro- and macro-approach to the fatigue crack growth in progressively drawn pearlitic steels at different R-ratios. International Journal of Fatigue 31(11-12): 2014–2021
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Toribio, J., González, B. & Matos, JC. Influence of the Microstructure of Eutectoid Steel on the Cyclic Crack Propagation: Pearlite and Spheroidite. Int J Fract 171, 209–215 (2011). https://doi.org/10.1007/s10704-011-9633-7
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10704-011-9633-7