Abstract
The Fe73.5Cu1Nb1Ta2Si13.5B9 samples were measured in as-quenched state and after annealing for 1 h in vacuum from 100 to 700°C. The maximum values of the magnetomechanical coupling coefficient (km=0.38) were obtained after annealing at 450°C. The saturation magnetostriction after annealings up to 450°C was equal to (23–25)×10−6. After annealings above 460°C nanocrystalline structure was observed.
Similar content being viewed by others
References
Y. Yoshizawa, S. Oguma and K. Yamauchi: J. Appl. Phys. 64 (1988) 6044.
Z. Kaczkowski, G. Vlasák and P. Duhaj: Mater. Sci. Eng. A 226–228 (1997) 676.
G. Vlasák, Z. Kaczkowski and P. Duhaj: J. Magn. Magn. Mater. 215–216 (2000) 476.
Z. Kaczkowski: in II Bilateral Polish-German Symposium on Ultrasonic Measurement in Technics in Science & Practice, Gliwice-Ustron, 1994, Upper Silesian Division of the Polish Acoustical Society, Gliwice, 1994, p. 29.
Z. Kaczkowski: Int. J. Appl. Electromagn. Mater. 5 (1994) 229.
Z. Kaczkowski: Mater. Sci. Eng. A 226–228 (1997) 614.
V. Hašlar, L. Kraus, L. Malkinski, K. Zaveta and Z. Kaczkowski: IEEE Trans. Magn. 30 (1994) 510.
C. Modzelewski, H. T. Savage, L. T. Kabacoff and A. E. Clark: IEEE Trans. Magn. MAG-17 (1981) 2837.
Z. Kaczkowski, L. Lanotte, M. Müller and P. Ruuskanen: J. Physique IV, 8 (1998) Pr2–221.
Z. Kaczkowski, G. Vlasák, P. Duhaj and P. Ruuskanen: J. Magn. Magn. Mater. 185 (1998) 112.
Z. Kaczkowski, P. Ruuskanen, M. Müller and L. Lanotte: J. Magn. Magn. Mater. 185 (1998) 115.
Z. Kaczkowski, L. Lanotte and M. Müller: in Rapidly Quenched & Metastable Materials, Supplement, (Eds. P. Duhaj, P. Mrafko, P. Švec), Elsevier, Amsterdam, 1997, p. 276.
Z. Kaczkowski (Ed.): Piezomagnetic Materials and Their Applications, Panstwowe Wydawnictwo Naukowe, Warszawa 1978 (in Polish).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kaczkowski, Z., Vlasák, G., Švec, P. et al. Magnetomechanical coupling in Fe73.5Cu1Nb1Ta2Si13.5B9 alloy. Czech J Phys 52 (Suppl 1), A141–A144 (2002). https://doi.org/10.1007/s10582-002-0033-0
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10582-002-0033-0