Abstract
Cellulose mixed esters (CMEs) substituted with two different types of acyl groups are promising polymeric materials with various tunable properties but are arduous to produce. This is because of the insolubility of cellulose in common solvents, and thus, the industrial production of CMEs with desired degrees of substitution (DSs) requires a costly multistep process. To accomplish their facile production, homogeneous reactions have been performed using ionic liquids (ILs) as solvents for cellulose. However, the high viscosity of the cellulose-IL solutions causes insufficient mixing in batch reactors; thereby, favoring low cellulose concentrations with long reaction times (typically hours). Herein, we demonstrate a rapid and scalable production of CMEs by exploiting the excellent shear mixing of a twin-screw extruder as a flow reactor. A co-solvent system comprising an IL, 1-ethyl-3-methylimidazolium acetate, and dimethyl sulfoxide was applied to dissolve cellulose at a high concentration (15 wt.%) via twin-screw extrusion. During continuous extrusion at 80 °C, cellulose reacted with two acyl reagents, isopropenyl acetate (IPAc) and vinyl propionate (VPr) (2.5:0.5, mol/mol), to yield cellulose acetate propionate (CAP) within minutes. The CAP was stably produced during the operation time of 50 min with an average isolated yield of 71%. The DSs of the acetyl and propionyl groups of CAP were 1.77 and 0.50, respectively, corresponding to sufficiently high conversion rates of 70% for IPAc and 100% for VPr.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Cellulose mixed esters (CMEs) are promising polymeric materials with customizable functions controlled by the substitution of at least two distinct types of acyl groups (Glasser 2004). Short acyl chains (carbon number, C < 6) impart solubility (Maim et al. 1951), fatty esters improve thermal processability (Willberg-Keyriläinenet al. 2017), phosphate esters provide flame resistance (Aoki and Nishio 2010; Xiao et al. 2014), and aromatic esters provide UV barrier properties (Song et al. 2017). Some CMEs, such as cellulose acetate propionate (CAP), are commercially available for use in coatings (Edgar 2007), films (Amim 2008), and membranes (Kujawa et al. 2019). However, because of the insolubility of cellulose in common solvents, the industrial production of CMEs with desired degrees of substitution (DSs) requires a costly multistep process, which involves a heterogeneous acylation step, a partial acid-hydrolysis step to adjust the DS, and further per-acylation with another substituent (Cao et al. 2011; Tosh 2014).
Homogeneous processes are more advantageous because of the superior control over the DSs of CMEs, compared to heterogeneous processes. Although several cellulose solvents, such as 4-methylmorpholine-N-oxide and N,N’-dimethylacetamide/LiCl, have been previously reported, there remain issues with toxicity, low thermal stability, and poor recyclability. Recently, ionic liquids (ILs) have been expected as green solvents to replace them, because cellulose is found to be highly soluble in ILs (> 20 wt.% cellulose) (Dorn et al. 2008; Pinkert et al. 2009) without thorough pretreatments (Wendler et al. 2012). Moreover, ILs are recyclable (Hinner et al. 2016; van Nguyen et al. 2017; Milotskyi et al 2021) and safe to handle, owing to their non-volatility and non-flammability (Gericke et al. 2012). In general, the cellulose-dissolving capacity of ILs is governed by hydrogen-bond basicity of the anions (Fukaya et al. 2008; Kostag et al. 2019). Furthermore, ILs such as 1-ethyl-3-methylimidazolium acetate (EmimOAc) act as both the solvent and catalyst for cellulose acylation (Kakuchi et al. 2015, 2017). However, a typical homogeneous acylation using ILs in batche processes requires low cellulose concentrations: e.g., 1–5 wt.% cellulose, and the total process for completing the dissolution and reaction of cellulose requires approximately 36 h (Schenzel et al. 2014; Wen et al. 2017; Hirose et al. 2019). This is because the high viscosity of the IL-cellulose solution impedes the penetration of anions into hydrogen bond networks between the cellulose chains (Pinkert et al. 2009). The viscosity of the solution can be lowered by adding an aprotic cosolvent (Zhao et al. 2013; Xu et al. 2013; Minnick et al. 2016) and/or by selecting an IL with a lower viscosity (Zhang et al. 2005). Consequently, transesterification reactions with cellulose concentrations of 12 wt.% were achieved in relatively shorter times, but still required several hours (Cao et al. 2010).
Extruders are often used for handling high-viscosity fluids, owing to their excellent-shear mixing. In particular, twin-screws are more efficient than single-screws during mixing (Martínez-Bustos et al. 2012; Guiao et al. 2022). Extruders are also used as flow reactors. This so-called reactive extrusion (REX) has been attempted for the transesterification of concentrated cellulose (~ 20 wt.%) in 1-butyl-3-methylimidazolium chloride to achieve rapid modification. However, the resulting cellulose derivatives exhibited low DSs (< 0.6) (Gibril et al. 2012; Gibril et al. 2013; Zhang et al. 2014). Recently, our group has succeeded in cellulose acylation via REX in EmimOAc/dimethyl sulfoxide (DMSO) using a twin-screw micro-compounder. Cellulose laurate was synthesized with vinyl laurate; high DS (2.7) and conversion (93%) were achieved within 10 min at 120 ℃ (Milotskyi et al. 2021). However, this micro-compounder is a circular batch reactor, and the REX was only applied to mono-acylation of cellulose. Hence, the continuous and scalable production of CMEs using a twin-screw extruder has never been achieved.
In this study, the continuous production of CMEs was first demonstrated using a twin-screw extruder as a flow reactor. For the rapid dissolution of highly concentrated cellulose, a mixed solvent of EmimOAc/DMSO at various ratios was applied. As a co-solvent, DMSO assists cellulose dissolution (Minnick et al. 2016) and facilitates the transesterification reaction catalyzed by EmimOAc (Kakuchi et al. 2017). A mixture of two acyl reagents, isopropenyl acetate (IPAc) and vinyl propionate (VPr), was subsequently introduced into the extruder. These reagents simultaneously reacted with the dissolved cellulose within minutes, resulting in the continuous production of CAP. Each DS was controlled by the molar ratio of IPAc/VPr, and the conversions of acyl reagents were evaluated. The average isolated yield and production rate of CAP (kg/day) were then examined.
Materials and methods
Materials
EmimOAc was purchased from Nippon Nyukazai Co. Ltd. (Tokyo, Japan) and vacuum-dried at room temperature (25 °C) for 3 d prior to use. DMSO, IPAc, VPr, deuterated DMSO-d6 containing 0.05 (v/v) tetramethylsilane (TMS), and trifluoroacetic acid (TFA) were purchased from Tokyo Chemical Industry Co. Ltd. (Tokyo, Japan). Microcrystalline cellulose, Avicel® PH-101, particle size < 50 µm, degree of polymerization (DPn) = 105 (van Nguyen et al. 2017), was purchased from Sigma-Aldrich Co. LLC. (St. Louis, MO, USA), and dried in a vacuum oven at 70 °C for more than 2 h prior to use.
Twin-screw extruder setup
Reactive extrusion (REX) was performed in an open system using a twin-screw extruder (ULTnano20TW-20MG-NH (600), Technovel Corp., Osaka, Japan) with a screw diameter of 20 mm and length to diameter ratio (L/D) of 20. This extrusion system had two individual inlet ports, C1 and C2, from the upstream side. The C1 port was connected to a Q-100-6 T-P-S Smoothflow pump (Tacmina Corp., Osaka, Japan) while the C2 port was connected to a PU-2086 plus dual syringe pump (JASCO Corp., Tokyo, Japan) (see Fig. S1). The extruder was preheated to 80 °C for each experiment, and the screw speed was set to 60 rpm. In such extruder systems, the screws convey, mix, and knead a substance along the length of the extruder before pushing it through the die. The resulting discharged paste-like material is called the extrudate. For continuous processes, “steady state” is the condition that describes when the mass flowing into the extruder is equal to the amount of mass dispelled from the die. All the experiments were performed under the steady state.
Solubility tests for cellulose in EmimOAc/DMSO
The cellulose-dissolving capacity of the EmimOAc/DMSO mixed solvent was investigated using a twin-screw extruder at 80 °C. For 10 wt.% cellulose solutions, dried cellulose was dispensed into the feeder at a feed rate of 0.6 g min−1, and a pre-mixed EmimOAc/DMSO solution was pumped into the C1 port at a flow rate of 5.4 g min−1. In order to collect a sample under the steady state, a small drop of the extrudate was collected 20 min after the first extrudate appeared. Then it was placed between two glass slides and observed using a cross-polarized optical microscope (POM, MT9430L polarizing microscope, Meiji Techno Co. Ltd., Saitama, Japan) at 50 × magnification to confirm the dissolution of cellulose under continuous flow.
Next, the flow rate of the EmimOAc/DMSO mixed solvent was gradually decreased to 3.4 g min−1 and then to 2.8 g min−1. Because the feed rate of cellulose was kept at 0.6 g min−1, the resultant cellulose concentrations increased to 15 and 20 wt.%. For each experiment after the flow rate was changed, the flow was uninterrupted for 20 min to reach the steady state; subsequently, the extrudate samples were analyzed using the POM.
The above process was repeated for each EmimOAc/DMSO solution at different ratios (1:3, 1:2, and 1:1, g/g). In total, a series of experiments were performed under nine conditions, that is, three cellulose concentrations and three ratios of EmimOAc/DMSO (Table 1).
Continuous production of CAP via REX
The homogeneous acylation of cellulose with two substituents (Fig. 1) was performed in the EmimOAc/DMSO mixed solvent using a twin-screw extruder as a flow reactor. After preheating the extruder at 80 °C, cellulose was poured into the feeder at a feed rate of 0.6 g min−1 (3.75 mmol min−1). The EmimOAc/DMSO mixed solvent (1:3, g/g) was introduced into the reactor from the C1 port to produce an extrudate with a cellulose concentration of 15 wt.%. The time gap between the introduction of cellulose/solvent media and the appearance of the first extrudate was recorded to be 10 min. After 20 min passed to afford the steady state, the pre-mixed acyl reagents of IPAc and VPr, 2.5:0.5 molar equiv./anhydroglucose unit (AGU) of cellulose, was introduced into the reactor from the C2 port at 1.1 g min−1. The start of the flow of the mixed acyl reagents was arbitrarily labeled as the collection time (x = 0 min). The flow of cellulose, mixed-solvent, and acyl reagents was continued for total 50 min to verify the steady production of CAP. The extruded reactant mixtures were collected in vials every five min (x = 10, 15, 20, 25, 30, 35, 40, 45, and 50 min) and weighed. A small amount (~ 2.6 g) of the paste-like extrudate from each vial was poured into 100 mL of methanol. The generated precipitate was filtered, washed repeatedly with methanol, and vacuum-dried at 70 °C for 24 h to obtain cellulose acetate propionate (CAPx min).
Batch synthesis of CAP
The similar reaction as the above described was performed in a batch reactor to compare the performance with the twin-screw extruder. It was performed with a low cellulose concentration (5 wt.%). First, 57 g of EmimOAc/DMSO (1:3, g/g) mixed solvent was transferred into a 500 mL Schlenk flask with a stirrer bar, and 3 g of dried cellulose (18.5 mmol) was then added to the solution. The flask was purged with Ar gas and sealed with a rubber top. The mixture was heated at 80 °C and stirred for 2 h to complete the dissolution of cellulose. Pre-mixed acyl reagents (IPAc and VPr, 2.5:0.5 molar equiv./AGU) were then injected into the flask, and the resulting solution was stirred at 80 °C for 4 h to achieve the homogeneous acylation of cellulose. During this batch reaction, 2 mL samples were taken from the reaction mixture at different times (y = 1, 10, 20, 30, 45, 60, 90, 120, and 240 min) and then precipitated into 100 mL of methanol. The precipitate was filtered, washed repeatedly with methanol, and vacuum-dried at 70 °C for 24 h to yield batch-synthesized cellulose acetate propionate (B-CAPy min).
Characterization of CAPs
Fourier transform infrared (FT-IR) spectra of the CAPs were recorded using a Thermo Fisher Scientific Nicolet iS10 (Thermo Fisher Scientific Inc., Tokyo, Japan) spectrophotometer equipped with an attenuated total reflection (ATR) unit. The FT-IR spectra were measured in the 4000 − 400 cm−1 range, and 64 scans were accumulated per spectrum. The resolution was kept as 4 cm−1, and the signal-to-noise ratio (S/N) was 35 000:1.
1H and 13C nuclear magnetic resonance (NMR) spectra of the CAPs were recorded using a JNM-ECZ R 600 Hz spectrometer (JEOL Ltd., Tokyo, Japan) in DMSO-d6 at the Advanced Research Center of Kanazawa University. All NMR spectra were analyzed using delta NMR (JEOL Ltd., Tokyo, Japan), and the chemical shifts (δ, ppm) were referenced to TMS (δ = 0 ppm) as an internal standard.
The DS of the propionyl (Pr) and acetyl (Ac) groups in CAP, denoted as DSPr and DSAc, were determined by 1H NMR analysis. A drop of TFA was added to the sample solution in DMSO-d6 to move the chemical shifts of the active hydrogen atoms downfield (Cao et al. 2010). According to the literatures (Aoki and Nishio 2010; Abe et al. 2016), each DS was determined using Eqs. (1) and (2):
where I-Pr(CH3) is the integral ratio of chemical shifts assigned to the methyl protons of the Pr group; I-Ac(CH3)&Pr(CH2) is the integral ratio of the region that includes the overlapping chemical shifts of the methyl protons of the Ac group and the methylene protons of the Pr group. I-cellulose denotes the integral ratio of the chemical shifts caused by the seven protons of the cellulose backbone.
The theoretical yields of the CAPs were calculated based on the resultant DSs, and the isolated yields were determined. The conversion of VPr and IPAc was defined and estimated as follows in Eq. (3):
where DSR is the resultant DS (i.e., DSPr or DSAc); DStarget is the target DS of 0.5 for Pr group and 2.5 for Ac group, based on the molar ratio of the added acyl reagents per AGU.
The molar mass distribution of the CAPs was determined by size exclusion chromatography (SEC, Prominence UFLC system, Shimadzu Co., Tokyo, Japan) based on polystyrene standards. SEC was performed at 40 °C using a TSK gel α-M (Tosoh Co., Tokyo, Japan). Moreover, 0.01 mol L−1 of lithium bromide (LiBr) in dimethylformamide (DMF) was used as an eluent at a flow rate of 0.5 mL min−1.
Results and discussion
Cellulose solubility in EmimOAc/DMSO within the twin-screw extruder
To optimize the ratio of EmimOAc/DMSO for cellulose dissolution using the twin-screw extruder, the solubility of cellulose under three different concentrations (10, 15, and 20 wt.% cellulose) was investigated by POM observation of the extrudates. At 20 wt.% cellulose concentration as shown in Fig. 2 (iii), (vi), and (ix), the POM images show bright particles appeared in the extrudates at all mixed ratios of EmimOAc/DMSO (1:1 − 1:3, g/g). The presence of these particles was attributed to the undissolved cellulose crystals (Ngo 2019), and the number of remaining particles decreased with increasing the EmimOAc content. In contrast, no particles were observed in either 10 or 15 wt.% cellulose solutions, indicating the complete dissolution of cellulose in all mixed ratios of EmimOAc/DMSO. In the FT-IR spectra of the regenerated cellulose obtained after the solubility tests, there was no distinct band that newly appeared from that of pristine cellulose, which indicates that no chemical reaction occurred between the cellulose and EmimOAc during the dissolution process. Moreover, the OH bands in the range from 3000 to 3500 cm−1 broadened (Fig. S2), suggesting that a part of crystalline cellulose became amorphous (Kondo 1997) through the dissolution in EmimOAc/DMSO and subsequent regeneration.
The optimal solvent should dissolve the largest amount of cellulose while containing the least amount of EmimOAc. While DMSO alone cannot dissolve cellulose, it coordinates to the IL cations, which dissociates the ion pairs of the IL and promote cellulose-anion bonding (Minnick et al. 2016). Consequently, the use of the proper amount of DMSO accelerates cellulose dissolution. Therefore, 1:3 (g/g) was considered to be the optimal ratio of EmimOAc/DMSO for the REX with 15 wt.% cellulose, as shown in Fig. 2 (ii), within the examined experimental conditions.
REX for continuous production of CAP
REX was carried out with adding pre-mixed acyl reagents to the 15 wt.% cellulose solution in EmimOAc/DMSO (1:3, g/g) to produce CAPs. Figure 3a shows the FT-IR spectra of pristine cellulose as a reference and CAP15 min as a representative spectrum of all CAPs. The spectrum of cellulose showed characteristic bands at 1029 cm−1 and 898 cm−1, which can be attributed to the C–O–C stretching of the sugar backbone and β-glycosidic linkages, respectively. In addition, a strong broad band was observed at 3330 cm−1, which corresponds to the O–H stretching vibrations of the hydroxy (OH) groups (Yue et al. 2012). In the spectrum of CAP15 min, similar bands derived from the pyranose ring were observed but these bands were sharpened and slightly shifted to 1030 and 900 cm−1, respectively. This might be attributed to the overlap with other bands due to the C–O–C asymmetric stretching vibrations of the introduced ester groups into cellulose. Moreover, there was a significant decrease in the intensity of the OH band at 3477 cm−1. In addition, new bands appeared at 1211 and 1736 cm−1, due to the C–O and C=O stretching of the ester groups, respectively (Fei et al. 2017). The spectra of all the CAPs shared similar traits (Fig. S3). These results suggest that the hydrogen network of pristine cellulose was disturbed due to dissolution in EmimOAc/DMSO, and the exposed OH groups were subsequently acylated via REX 10 min after the start of adding the pre-mixed acyl reagents into the reactor.
The structures of the CAPs were further elucidated using 1H and 13C NMR (Figs. S4 and S5). Figure 3b shows the 1H NMR spectrum of CAP15 min. The chemical shifts of the protons of the cellulose backbone range from 2.8 to 5.4 ppm. The methyl protons of the Ac and Pr groups were observed between 1.9–2.1 and at 1.0 ppm, respectively. The methylene protons of the Pr groups were observed at 2.2 ppm (Huang et al. 2011; Fei et al. 2017; Kujawa et al. 2019). All the other CAPs exhibited similar 1H NMR spectra (Fig. S4), and the carbonyl carbons and the carbons of the cellulose backbone were also identified by 13C NMR (Fig. S5). Hence, it was confirmed that cellulose was successfully modified with both the Ac and Pr groups via REX.
The DSAc and DSPr of CAPs were determined and summarized in Table S1. The CAPs showed the average DSAc of 1.77 ± 0.04 and DSPr of 0.50 ± 0.04 (n = 9), and both the Ac and Pr groups on CAP15min were distributed in the order of 6, 3, and 2 positions of cellulose-OH groups (Fig. S6 and Table S2). These DSs correspond to the sufficiently high conversion rates of 71 ± 2% and 100 ± 6% for IPAc and VPr, respectively. Owing to these high conversion rates, the DSAc and DSPr of CAP can be controlled by adjusting the molar ratio of IPAc to VPr in the mixed reagent solution. Notably, the average total DS (DSTotal) of CAPs reached 2.27 ± 0.07 under mild conditions at 80 °C with the equimolar concentrations of acyl reagents. In contrast, previously reported continuous REXs for the heterogeneous mono-acylation of cellulose yielded extremely low DSs < 0.6 (Gibril et al. 2012, 2013; Zhang et al. 2014). These results suggest that the EmimOAc/DMSO mixed system applied in this study afforded the complete dissolution of cellulose, successfully allowing the excellent catalytic activity of EmimOAc for the subsequent cellulose acylation using the twin-screw extruder.
To evaluate the consistency of this continuous REX process, the mass of the extrudates and their respective CAP yields were measured and plotted against the collection time, as shown in Fig. 4. The yield of each CAP is also summarized in Table S1. The average mass of the extrudates collected (n = 9) was approximately 27.3 ± 0.09 g. Assuming that the cellulose feed rate was constant at 0.6 g min−1, 3.0 g of cellulose was fed into the extruder over 5 min. After purifying the extrudate, it was estimated that approximately 3.7 g of CAP was produced every 5 min during the flow reaction. Thus, the increased weight of the product (~0.7 g) could be attributed to the substitution of cellulose-OH groups with the ester groups. Furthermore, the average isolated yield of CAPs was 77 ± 2% (n = 9). Notably, the respective fluctuations of the DSAc, DSPr, and isolated yield of CAPs were quite small, indicating that CAP production via continuous REX proceeded stably for at least 50 min of flow. Although this first trial was stopped at 50 min because of the subsequent laborious purification, the operation time of this REX process can be further expanded for straightforward scalability.
Comparison of REX and batch processes for CAP production
The performance of REX for cellulose acylation was compared with that of a batch process. Because of technical limitations, the batch process could only handle a narrow range of solution viscosities. Thus, 5 wt.% cellulose was applied to the homogeneous batch reaction with IPAc and VPr at 80 °C with varying reaction times. Each reaction was performed in triplicate. The batch-synthesized CAPs (B-CAPs) were identified by FT-IR and 1H NMR (Figs. S7 and S8, respectively). The DSs and isolated yields of the B-CAPs are summarized in Table S3. The average DSAc and DSPr (n = 3) were plotted against the reaction time (1–240 min), as shown in Fig. 5. The DSPr of B-CAPs quickly increased to 0.33 after 1 min and achieved 0.48 after 10 min, demonstrating the rapid completion of propionylation. Meanwhile, acetylation gradually proceeded, and approximately 1 h was required for DSAc to attain an equilibrium at 2.1. This acetylation tendency is consistent with our previous result in which cellulose was acetylated using a batch reactor with an equimolar amount of IPAc ([IPAc]/[OH] = 1) to afford a DS of 2.3 after 1 h (Kakuchi et al. 2015). However, even after 4 h, B-CAP240 min showed a DSPr of 0.46 ± 0.01 and DSAc of 2.09 ± 0.03. The corresponding conversion rates for VPr and IPAc were 92 ± 2% and 84 ± 1%, respectively.
In addition to the inherently lower reactivity of IPAc than that of VPr, the low cellulose concentration in the batch process may be responsible for the slow acetylation rate. However, despite the increased reaction time, the IPAc conversion did not drastically improve. The maximum conversion rate of IPAc in batch was comparable to that in REX (71 ± 2%). This suggests that the incomplete conversion of IPAc in REX was not caused by the reaction system with the short resistance time.
A straightforward comparison between the two processes is difficult because the reaction conditions, such as the cellulose concentration and reaction time, differ. Thus, one batch product, B-CAP20 min, was selected and compared with one REX product, CAP15 min, because their DSs and conversion rates were the most similar among all the REX and batch products. The results for these CAPs are summarized in Table 2. In addition, the weight-average molar mass (Mw) and polydispersity indices (Ð) of B-CAP20 min (Mw = 2.1 × 105 g mol−1 and Ð = 2.3) and CAP15 min (Mw = 2.0 × 105 g mol−1 and Ð = 2.2) were similar (Fig. S9). This similarity in the molar mass distributions of the REX and batch products suggests that no significant depolymerization occurred despite strong shearing via the twin-screw extruder.
As shown in Table 2, the average isolated yields of CAPs in the REX and batch processes were comparably high at 77 and 73%, respectively, however, indicating some loss of the products in both processes. Considering its similarity to the batch process, the loss of products was not attributed to the REX process. Thus, it can be considered that a portion of CAPs (e.g., with low molecular mass and/or excess Pr groups) synthesized in both processes was remained in the methanol filtrate during the precipitation step.
Totally, the CAP production via REX can outpace the batch production due to the continuous flow and higher cellulose concentration applied in the REX, which successfully contributed to the excellent production rate of 1 kg/day. In contrast, the batch reaction can produce CAP only at a gram scale each day. The reaction time could be shortened to some extent, as suggested from Fig. 5, but the batch process still required several hours because of the time-consuming dissolution step of cellulose. On the other hand, REX enabled a much shorter processing time, including both dissolution and subsequent reactions. Although it required an initial stabilization time, CAP was continuously produced within minutes while exhibiting high reaction efficiency, based on its high conversions of acyl reagents. Hence, this REX process can be applied as a facile, rapid, and scalable process for CME production.
Conclusions
A facile, rapid, and scalable production of CME was first demonstrated in this study using a twin-screw extruder as a flow reactor. This process enabled the continuous production of highly substituted CAPs (DStotal = 2.27 ± 0.07) from concentrated cellulose (15 wt.%) solutions in EmimOAc and DMSO (1:3, g/g). The complete dissolution and successive transesterification of cellulose with pre-mixed IPAc and VPr (2.5:0.5, molar equiv./AGU) were carried out within minutes at 80 °C in an open-air system. During the 50-min flow, CAPs (n = 9) with consistently high DSAc (1.77 ± 0.04) and DSPr (0.50 ± 0.04) were obtained in sufficient isolated yields of 77 ± 2%. This REX process succeeded in shortening the total processing time for homogeneous acylation of highly concentrated cellulose with achieving high conversion rates for IPAc and VPr (71 ± 2% and 100 ± 6%, respectively). Although this study focused on the synthesis of CAP in a lab-scale twin-screw extruder, our strategy can be applied to the large-scale production of various CMEs with further precise and technical conditioning.
Data availability statement
Not applicable.
References
Abe M, Sugimura K, Nishio Y (2016) Regioselectivity in acetylation of cellulose in ionic liquids. ChemistrySelect 1:2474–2478. https://doi.org/10.1002/slct.201600520
Amim J, Kosaka PM, Petri DFS (2008) Characteristics of thin cellulose ester films spin-coated from acetone and ethyl acetate solutions. Cellulose 15:527–535. https://doi.org/10.1007/s10570-008-9213-9
Aoki D, Nishio Y (2010) Phosphorylated cellulose propionate derivatives as thermoplastic flame resistant/retardant materials: Influence of regioselective phosphorylation on their thermal degradation behaviour. Cellulose 17:963–976. https://doi.org/10.1007/s10570-010-9440-8
Cao Y, Zhang J, He J, Li H, Zhang Y (2010) Homogeneous acetylation of cellulose at relatively high concentrations in an ionic liquid. Chin J Chem Eng 18:515–522. https://doi.org/10.1016/S1004-9541(10)60252-2
Cao Y, Li H, Zhang J (2011) Homogeneous synthesis and characterization of cellulose acetate butyrate (CAB) in 1-Allyl-3-methylimidazolium chloride (AmimCl) ionic liquid. Ind Eng Chem Res 50:7808–7814. https://doi.org/10.1021/ie2004362
Dorn S, Wendler F, Meister F, Heinze T (2008) Interactions of ionic liquids with polysaccharides-7: thermal stability of cellulose in ionic liquids and N-methylmorpholine-N-oxide. Macromol Mater Eng. https://doi.org/10.1002/mame.200800153
Edgar KJ (2007) Cellulose esters in drug delivery. Cellulose 14:49–64. https://doi.org/10.1007/s10570-006-9087-7
Fei P, Liao L, Cheng B, Song J (2017) Quantitative analysis of cellulose acetate with a high degree of substitution by FTIR and its application. Anal Methods 9:6194–6201. https://doi.org/10.1039/C7AY02165H
Fukaya Y, Hayashi K, Wada M, Ohno H (2008) Cellulose dissolution with polar ionic liquids under mild conditions: required factors for anions. Green Chem 10:44–46. https://doi.org/10.1039/B713289A
Gericke M, Fardim P, Heinze T (2012) Ionic liquids—promising but challenging solvents for homogeneous derivatization of cellulose. Molecules 17:7458–7502. https://doi.org/10.3390/molecules17067458
Gibril ME (2012) Reactive extrusion for in-situ chemical modification of cellulose with de-octenyl succinic anhydride (DDSA) in presence of Ionic liquid. Int J Eng Sci Technol 4:3572–3583
Gibril ME, Huan L, Feng LH et al (2013) Reactive extrusion process for the preparation of a high concentration solution of cellulose in ionic liquid for in situ chemical modification. RSC Adv 3:1021–1024. https://doi.org/10.1039/C2RA22296E
Glasser WG (2004) Prospects for future applications of cellulose acetate. Macromol Symp 208:371–394. https://doi.org/10.1002/masy.200450416
Guiao KS, Gupta A, Tzoganakis C, Mekonnen TH (2022) Reactive extrusion as a sustainable alternative for the processing and valorization of biomass components. J Clean Prod 355:131840. https://doi.org/10.1016/j.jclepro.2022.131840
Hinner LP, Wissner JL, Beurer A, Nebel BA, Hauer B (2016) Homogeneous vinyl ester-based synthesis of different cellulose derivatives in 1-ethyl-3-methyl-imidazolium acetate. Green Chem 18:6099–6107. https://doi.org/10.1039/C6GC02005D
Hirose D, Kusuma SBW, Ina D, Wada N, Takahashi K (2019) Direct one-step synthesis of a formally fully bio-based polymer from cellulose and cinnamon flavor. Green Chem 21:4927–4931. https://doi.org/10.1039/C9GC01333D
Huang K, Wang B, Cao Y et al (2011) Homogeneous preparation of cellulose acetate propionate (CAP) and cellulose acetate butyrate (CAB) from sugarcane bagasse cellulose in ionic liquid. J Agric Food Chem 59:5376–5381. https://doi.org/10.1021/jf104881f
Kakuchi R, Yamaguchi M, Endo T et al (2015) Efficient and rapid direct transesterification reactions of cellulose with isopropenyl acetate in ionic liquids. RSC Adv 5:72071–72074. https://doi.org/10.1039/C5RA14408F
Kakuchi R, Ito R, Nomura S et al (2017) A mechanistic insight into the organocatalytic properties of imidazolium-based ionic liquids and a positive co-solvent effect on cellulose modification reactions in an ionic liquid. RSC Adv 7:9423–9430. https://doi.org/10.1039/C6RA28659C
Kondo T (1997) The assignment of IR absorption bands due to free hydroxyl groups in cellulose. Cellulose 4:281–292. https://doi.org/10.1023/A:1018448109214
Kostag M, Gericke M, Heinze T et al (2019) Twenty-five years of cellulose chemistry: innovations in the dissolution of the biopolymer and its transformation into esters and ethers. Cellulose 26:139–184. https://doi.org/10.1007/s10570-018-2198-0
Kujawa J, Rynkowska E, Fatyeyeva K et al (2019) Preparation and characterization of cellulose acetate propionate films functionalized with reactive ionic liquids. Polymers 11:1217. https://doi.org/10.3390/polym11071217
Maim CJ, Mench JW, Kendall DL, Hiatt GD (1951) Aliphatic acid esters of cellulose. Properties Ind Eng Chem 43:688–691. https://doi.org/10.1021/ie50495a034
Martínez-Bustos F, Aguilar-Palazuelos E, Galicia-García T (2012) Thermoplastic behavior of biopolymers during extrusion. In: Vania Regina Nicoletti Telis (ed) Biopolymer Engineering in Food Processing, Taylor & Francis, Florida, pp 243–270
Milotskyi R, Szabó L, Fujie T et al (2021) Low waste process of rapid cellulose transesterification using ionic liquid/DMSO mixed solvent: towards more sustainable reaction systems. Carbohydr Polym 256:1–9. https://doi.org/10.1016/j.carbpol.2020.117560
Minnick DL, Flores RA, Destefano MR, Scurto AM (2016) Cellulose solubility in ionic liquid mixtures: temperature, cosolvent, and antisolvent effects. J Phys Chem B 120:7906–7919. https://doi.org/10.1021/acs.jpcb.6b04309
Ngo T (2019) Cellulose to nanocelluloses: production, properties and applications. Nova Science Publishers, New York
Pinkert A, Marsh KN, Pang S, Staiger MP (2009) Ionic liquids and their interaction with cellulose. Chem Rev 109:6712–6728. https://doi.org/10.1021/cr9001947
Schenzel A, Hufendiek A, Barner-Kowollik C, Meier MAR (2014) Catalytic transesterification of cellulose in ionic liquids: sustainable access to cellulose esters. Green Chem 16:3266–3271. https://doi.org/10.1039/C4GC00312H
Song J, Liu M, Yang Z et al (2017) Synthesis and characterization of cellulose acetate naphthoate with good ultraviolet and chemical resistance. e-Polym 17:333–340. https://doi.org/10.1515/epoly-2016-0293
Tosh B (2014) Synthesis and sustainable applications of cellulose esters and ethers: a review. Int J Energy, Sustain Environ Eng 1:56–78
Van Nguyen Q, Nomura S, Hoshino R et al (2017) Recyclable and scalable organocatalytic transesterification of polysaccharides in a mixed solvent of 1-ethyl-3-methylimidazolium acetate and dimethyl sulfoxide. Polym J 49:783–787. https://doi.org/10.1038/pj.2017.49
Wen X, Wang H, Wei Y, Wang X, Liu C (2017) Preparation and characterization of cellulose laurate ester by catalyzed transesterification. Carbohydr Polym 168:247–254. https://doi.org/10.1016/j.carbpol.2017.03.074
Wendler F, Todi LN, Meister F (2012) Thermostability of imidazolium ionic liquids as direct solvents for cellulose. Thermochim Acta 528:76–84. https://doi.org/10.1016/j.tca.2011.11.015
Willberg-Keyriläinen P, Vartiainen J, Harlin A et al (2017) The effect of side-chain length of cellulose fatty acid esters on their thermal, barrier and mechanical properties. Cellulose 24:505–517. https://doi.org/10.1007/s10570-016-1165-x
Xiao P, Zhang J, Feng Y, Wu J, He J, Zhang J (2014) Synthesis, characterization and properties of novel cellulose derivatives containing phosphorous: cellulose diphenyl phosphate and its mixed esters. Cellulose 21:2369–2378. https://doi.org/10.1007/s10570-014-0256-9
Xu A, Zhang Y, Zhao Y, Wang J (2013) Cellulose dissolution at ambient temperature: role of preferential solvation of cations of ionic liquids by a cosolvent. Carbohydr Polym 92:540–544. https://doi.org/10.1016/j.carbpol.2012.09.028
Yue Y, Zhou C, French AD et al (2012) Comparative properties of cellulose nano-crystals from native and mercerized cotton fibers. Cellulose 19:1173–1187. https://doi.org/10.1007/s10570-012-9714-4
Zhang H, Wu J, Zhang J, He J (2005) 1-allyl-3-methylimidazolium chloride room temperature ionic liquid: a new and powerful nonderivatizing solvent for cellulose. Macromolecules 38:8272–8277. https://doi.org/10.1021/ma0505676
Zhang Y, Li H, Li X, Gibril ME, Yu M (2014) Chemical modification of cellulose by in situ reactive extrusion in ionic liquid. Carbohydr Polym 99:126–131. https://doi.org/10.1016/j.carbpol.2013.07.084
Zhao Y, Liu X, Wang J, Zhang S (2013) Insight into the cosolvent effect of cellulose dissolution in imidazolium-based ionic liquid systems. J Phys Chem B 117:9042–9049. https://doi.org/10.1021/jp4038039
Acknowledgments
Not applicable.
Funding
This research was funded by the Japan Science and Technology Agency (JST) (Grant number JPMJPF2102) and supported by JSPS KAKENHI (Grant numbers 18H02253, 21K14886, and 22H02404).
Author information
Authors and Affiliations
Contributions
All authors contributed to the study conception and design. Material preparation, data collection and analysis were performed by SCH, RM, ST, ERD. I, SS, NW, and KT. The first draft of the manuscript was written by SCH, and all authors commented on previous versions of the manuscript. All authors read and approved the final manuscript.”
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no conflicts of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hernandez, S.C., Milotskyi, R., Takagi, S. et al. Continuous production of cellulose mixed esters via homogeneous reactive twin-screw extrusion catalyzed by ionic liquid. Cellulose 30, 2873–2882 (2023). https://doi.org/10.1007/s10570-023-05062-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10570-023-05062-6