Abstract
Mesoporous SBA-15 silicate with a high surface area was prepared by a hydrothermal method, successively modified by organic melamine ligands and then used for deposition of Pd nanoparticles onto it. The synthesized materials were characterized with infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), nitrogen physisorption, scanning electron microscopy (SEM) coupled with energy dispersive X-ray analysis (EDX), transmission electron microscopy (TEM), nuclear magnetic resonance (NMR) and inductively coupled plasma (ICP-OES). The catalyst was effectively used in the Mizoroki–Heck coupling reaction of various reactants in the presence of an organic base giving the desired products in a short reaction time and with small catalysts loadings. The reaction parameters such as the base type, amounts of catalyst, solvents, and the temperature were optimized. The catalyst was easily recovered and reused at least seven times without significant activity losses.
Graphic Abstract
![](http://media.springernature.com/lw685/springer-static/image/art%3A10.1007%2Fs10562-021-03691-9/MediaObjects/10562_2021_3691_Figa_HTML.png)
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
In the synthetic organic chemistry and production of fine chemicals C–C cross-coupling reactions are highly ranked. In generally they present a robust way for C–C bonds formation and production of the diverse molecules with high selectivity toward R–R′ compounds. Among them the Mizoroki–Heck reaction is considered as one of the most important tools for coupling of aryl and vinyl halides or triflates with the molecules possessing sp2 CH bonds such as olefins and acrylates (Scheme 1) [1, 2]. Its popularity is connected to its versatility toward many reactants and resistance to different functional groups. In most of the cases the reaction is catalyzed by palladium, nonetheless other more abundant metals can be catalytically active under specific conditions making it much more environmental friendly alternative [3, 4]. Different reagents cane be utilized in Mizoroki–Heck reactions from the less reactive bromo- and chloro-compounds on one side to non-activated alkenes on the other, thus becoming attractive for industrial productions [5]. Reaction can yield E and Z types of products, but usually the E product type is predominant [6,7,8,9]. It can be used for creating the bonds within the molecule (intra-molecular) or between different reactants (inter-molecularly). Initially the inter-molecular form of the reaction was extensively studied in the past, [10] while intra-molecular reaction was described more lately [11].
There was a long debate in the literature whether homogeneous or heterogeneous species are catalyzing the Mizoroki–Heck reaction. The most commonly agreed mechanism of this reaction comprises leaching of palladium from the catalyst surface, its participation in the catalytic cycle and re-deposition back after the reaction completion [12,13,14,15]. Such a mechanism requires a careful choice of the catalyst and the reactor. Evidently, in batch processes homogeneous palladium catalysts can be used, however, such type of catalysis comes along with an important issue of catalyst separation and reusability, whereas recovery of noble metals is very important in terms of costs and environment impact. On the other hand, easy recycling of heterogeneous catalysts is an important advantage, with a clear disadvantage related to insufficient selectivity and catalyst leaching. Development of an easily separable heterogeneous catalyst was in the focus of many research groups and brought versatile solutions [16,17,18]. For example, many efforts were put on designing a heterogenized ligand system capable of stabilizing Pd giving thereby a highly active and reusable catalyst [19]. Besides high activity, a goal is to achieve a maximum catalyst recovery level. This could be done by taking an advantage of magnetic features embedded into a palladium complex deposited on silica coatings [20].
Parallel with development of catalytically active components various types of supports were explored. Highly ordered mesoporous silica materials SBA-15 have a potential to be utilized in many different applications, catalysis being one of the most important. The reasons for it are their properties, such as high surface areas (700–1200 m2 g−1), non-toxicity, chemical and physical inertness, abundance of silanol groups capable for functionalization, along with tunable physical properties such as the pore diameter and walls thickness. SBA-15 possesses hydrothermal stability due to thick and uniform silica walls (3.1 to 6.4 nm) with a two-dimensional (2D) hexagonal (p6mm) meso-structure of the channels and a large pore size (4.6–10.0 nm). As a consequence, SBA-15 was considered as a material appropriate for simple functionalization and tuned selectivity in catalysis, as well as for deposition and release of pharmaceutically active compounds in drug delivery applications [21,22,23,24]. A typical example is design of palladium supported DHBP@SBA-15 catalyst obtained by adding 2,2-dihydroxybenzopheneone ligand to amine functionalized mesoporous silica followed by metalation with Pd(II). This yielded a highly active catalyst in Mizoroki–Heck (arylation) and hydrogenation reactions without a significant loss of activity in several reaction cycles [25].
The current work discusses design and characterization of a new catalyst derived from melamine modified SBA-15 loaded with Pd nanoparticles. The catalyst performance was optimized for the Mizoroki–Heck reaction of iodobenzene and methyl acrylate in which it displayed high activity and reusability. The scope was extended to different iodo-, bromo- and chloro-aromatic compounds.
2 Experimental
2.1 Materials
Pluronic P123, tetraethyl orthosilicate (TEOS), 3-aminopropyltriethoxysilane (APTS), melamine, paraformaldehyde, PdCl2, NaBH4, iodobenzene, ethyl acrylate and organic/inorganic bases were obtained from Sigma Aldrich and used without further purification. Other chemicals were of analytical purity grade obtained from Alfa Aesar.
2.1.1 Synthesis of SBA-15
SBA-15 was synthesized according to the following procedure found in the literature [26]. In 30 mL of water 4.0 g of P123 was dissolved, followed by adding the mixture to 120 mL of 2 M HCl solution. After the solution became homogeneous, 9.0 g of tetraethyl orthosilicate was added, and the mixture was stirred for 8 h at 40 °C. The uniform reaction mixture was transferred into a Teflon-lined stainless-steel autoclave and aged at 100 °C for 24 h. After cooling down to the room temperature, the product was filtered, washed with water and EtOH, then dried overnight at 100 °C. The white solid was calcined at 560–600 °C for 6 h to remove the template.
2.1.2 Synthesis of SBA-15/Pr-NH2
In order to functionalize mesoporous silica SBA-15 1.00 g of this material reacted under reflux conditions with 1.5 ml of 3-aminopropyltrimethoxysilane (6.5 mmol) in 50 ml dry toluene under N2 for 24 h. The product was filtered and washed three times with 40 mL diethylether and 40 mL toluene to remove unreacted reagents, followed by evaporation of the solvent giving a white powder (SBA-15/Pr-NH2) [27].
2.1.3 Cross-Linked Melamine Functionalization of SBA-15
To synthesize the cross-linked melamine functionalized SBA-15 in a 4-neck round bottom flask all amino-functionalized SBA-15 from the previous step together with melamine (2.8 mmol, 0.35 g) and paraformaldehyde (22.4 mmol, 0.68 g) was added and sonicated in 20 ml of DMF under nitrogen for 30 min. After sonication, the reaction mixture was refluxed upon stirring for 24 h at 90 ºC under nitrogen atmosphere. The mixture was cooled to room temperature and then washed with DMF, distillated water and acetone. Finally, the solid cross-linked melamine functionalized SBA-15 was dried overnight at 60 ºC [28].
2.1.4 Preparation of SBA-15/Pr-NH-CH2-Melamine-Pd(0)
To deposit the metal 1.00 g of synthesized SBA-15/Pr-NH-CH2-Melamine was first dispersed in 10 ml EtOH at room temperature. Into SBA-15 suspension 0.10 g of PdCl2 dissolved in 20 ml EtOH was added, followed by stirring for 24 h at room temperature. Limited solubility of palladium chloride in the solvent required several deposition steps until the metal precursor was completely deposited. Finally, the solid catalyst was separated by centrifugation and washed three times with EtOH and twice with dicholorometane to remove the unreacted reagents, then kept overnight at 70 ºC. Subsequently, the solid product was reduced by 25 mL of 0.1 M sodium borohydride aqueous solution to give a dark brown mixture, separated by centrifugation, washed with distilled water and EtOH [29]. Reduction with a chemical reducing agent -sodium borohydride is a well-established method for generating Pd(0) particles [30]. After drying a grey solid was obtained containing 6.0%wt Pd according to ICP-OES.
2.2 Characterization
Modification of SBA-15 by organics was monitored by infrared spectroscopy (Mattson ATI Genesis FTIR Spectrometer). The specific surface area and the pore size were studied by N2 physisorption performed on Sorptometer 1900 (Carlo-Erba Instruments). The structure of SBA-15 derived material coupled with elemental analysis was investigated by scanning electron microscopy (Zeiss Leo—1530 Gemini) with a Thermo-NORAN vantage X-ray detector. Palladium nanoparticles size distributions and SBA-15 channels dimensions were investigated by transmission electron microscopy (TEM) performed on LEO 912 OMEGA (EFTEM) with acceleration voltage 120 kV and LaB6 electron source. Thermogravimetric analysis (TGA) was conducted with a Linseis STA PT 1000 instrument using a scanning rate of 10 °C min−1. The palladium content in solid samples was determined by inductively coupled plasma optical emission spectroscopy (ICP-OES), with Optima 4300 DV optical atomic emission spectrometer (Perkin Elmer). CP MAS 13C NMR spectrum of the catalyst was made with a Bruker AVANCE-III HD 400 MHz spectrometer. The sample was spun at 9 kHz spin rate in a Bruker 1H broadband double-resonance 4 mm CP MAS probe with the proton 90° high-power pulse of 2.9 µs and the contact time of 2 ms. The recovery delay time was 2 s and 30,000 scans were accumulated.
Low‐angle XRD in the 2θ range 0.7–10° was conducted with Philips X‐Pro (scanning rate 1° min−1) instrument operating at room temperature and equipped with an X‐ray radiation source using Cu Kα (λ = 0.15406 nm).
The reaction yield was followed by HP 6890 Series gas chromatograph (GC) equipped with the flame ionization detector and HP-5, 5% phenyl methyl siloxane capillary column (30.0 m, 320 µm, 0.25 µm). The injection temperature was 280 °C while the gas flow rate was 9.5 ml min−1. The aliquots were diluted and mixed with an internal standard solution of hexadecane.
2.3 Mizoroki–Heck Coupling
In general Mizoroki–Heck reaction was performed by using 1.0 mmol of iodobenzene, 1.5 mmol methyl acrylate, 1.5 mmol triethylamine (Et3N), 0.001 g SBA-15/Pr-NH-CH2-Melamine-Pd(0) as a catalyst (0.28 mol % Pd to aryl halide) and 1.0 ml of dimethylformamide (DMF) as a solvent at 120 °C for 15 min. The reaction was carried out in glass vial tubes supplied with a magnetic stirrer and heated by an oil bath, while the reaction progress and the halide consumption was monitored by TLC. Upon completion, the aliquots were analyzed with GC and the catalyst was separated from the slurry by filtration. The reaction mixture was washed with diethyl ether and ethyl acetate. The organic phase was separated after evaporation of the solvent under reduced pressure and the pure product was obtained by the plate chromatography on silica.
3 Results and Discussion
3.1 Catalyst Synthesis and Characterization
SBA-15 was synthesized via the hydrothermal method from TEOS and pluronic P123 polymer. After calcination, SBA-15 was functionalized by amine groups and modified by melamine and paraformaldehyde under sonication. After grafting the surface of SBA-15 by organic groups, PdCl2 was deposited on the surface and then reduced to Pd(0) by NaBH4 giving the final catalyst SBA-15/Pr-NH-CH2-Melamine-Pd(0) as illustrated in Scheme 2.
The FT-IR spectra for SBA-15, SBA-15/Pr-NH2, SBA-15/Pr-NH-CH2-Melamine, SBA-15/Pr-NH-CH2-Melamine-Pd(0) are shown in Fig. 1a. The peaks at 467, 812 and 1088 cm−1 in all samples are related to Si–O-Si bonds in SBA-15. Vibrations of the silanol groups are present at 3420 cm−1. Vibrations corresponding to NH2 bending and hydrogen-bonding of water molecules on the surface overlap at 1610 to 1640 cm−1. Asymmetric and symmetric C–H stretching of propyl chain are present at 2882 and 2936 cm−1. After functionalization of SBA-15/(CH2)3-NH2 with melamine, three new peaks were revealed at the 1361, 1515 and 1572 cm−1 showing presence of melamine on the surface of SBA-15 [31]. The spent catalyst exhibited essentially the same vibrations as the fresh one (Fig. 1b).
To confirm the structure of the organic moieties on the surface, the solid state 13C-NMR analysis was performed, as illustrated in Fig. 2. The sharp peak at ca. 167 ppm can be assigned to carbons in the aromatic chain [32]. The peak at ca. 77 ppm is related to carbon between two nitrogen atoms (NH-C-NH) [28]. Three signals at 46.6, 18.5 and 7.5 ppm showed presence of the propyl chain on the silicate. The non-hydrolyzed ethoxy group or unevaporated ethanol used for washing after functionalization with amino and melamine groups were also observed at ca. 15.5 (overlapping with carbon of the propyl chain) and at 59.1 ppm [33].
In order to study thermal stability of the materials thermogravimetric analysis of SBA-15/Pr -NH2 and the final catalyst was performed (Fig. 3). Removal of physically and chemically adsorbed water molecules is associated with a mass loss of approx. 3.2% for both samples from ambient temperature to 230 ºC. In total, the SBA-15/Pr-NH2 exhibited 10% weight losses, whereas the difference between the initial 3.2% and overall mass loss is approx. 6.6% and can be attributed to the propylamine loaded onto the SBA-15, with decomposition starting to happen above 310 ºC. In a case of SBA-15/Pr -NH-CH2-Melamine-Pd(0) sample exhibited 26.1% of weight losses, which can be attributed to the Propyl-NH-CH2-Melamine loading on the SBA-15 in addition to the initial water loss. It can be seen that the final catalyst is thermally stable to ca. 250 ºC, well above the common reaction temperatures.
Morphology of the samples was elucidated by SEM analysis of SBA-15 and the final catalyst. Figure 4 displays the SEM images of SBA-15 and SBA-15/Pr-NH-CH2-Melamine-Pd(0) materials. As follows from SEM images that the fresh SBA-15 has the rod shape which did not change after functionalization and stabilization of Pd(0) on SBA-15, indicating stability of the supporting structure during the catalyst preparation.
A qualitative overview of the elemental composition of SBA-15/Pr-NH-CH2-Melamine-Pd(0) was evaluated by EDX at random points on the surface of the catalyst and is shown in Fig. 5. The elemental measurements confirmed the presence of all expected elements in the supported catalyst. The weight % and atomic % of the elements are shown in Table 1. They should be taken, however, with precaution since the carbon content is overestimated due to the analytical approach and a necessity to use a carbon tape to deposit the powder sample prior analysis. The real loading of palladium in the catalyst was determined by ICP-OES displaying a much higher value, than obtained by EDX analysis. Nevertheless, EDX is still a valuable verification tool.
To gain more information on the structure of the catalyst and Pd size distribution TEM imaging was done. Figure 6 displays the images of SBA-15 and SBA-15/Pr-NH-CH2-Melamine-Pd(0) catalyst. Both materials exhibit uniform mesopores with a long-range order of a hexagonal array characteristic for SBA-15 materials. The dark spots in the image of SBA-15/Pr-NH-CH2-Melamin-Pd(0) with 20 to 50 nm diameter, can be attributed to the agglomerated Pd(0) nanoparticles on the channels. After selecting random spots on the TEM image of the catalyst, the average size of the particles is found to be ca. 20 nm.
The nitrogen adsorption–desorption isotherm (Fig. 7) was analyzed with the Brunauer–Emmett–Teller (BET) method for calculating the surface area of SBA-15. The BET surface area for the non-functionalized SBA-15 was calculated to be 840 m2/g. After functionalization with organic groups and deposition of palladium nanoparticles on mesoporous silica, the surface area was diminished to 575 m2/g, while the pore volume decreased from 1.10 to 0.14 cm3 g−1 confirming that the organic ligands and Pd nanoparticles are located in the pores of SBA-15. The Brunauer–Emmett–Teller (BET) surface areas and pore volumes of the SBA-15 and the final catalyst are summarized in Table 2.
The low-angle XRD spectra for SBA-15 and SBA-15/Pr-NH-CH2-Melamine-Pd(0) are shown in Fig. 8. For SBA-15, the three well-determined diffraction peaks are seen at 2θ of ca. 0.9–1.9°. Both synthesized materials exhibited a single strong peak (100) in XRD pattern followed by two additional peaks (110, 200) which can be ascribed to a hexagonal lattice. Compared with SBA-15, the peak intensity of the final catalyst is weaker, because of a poorly ordered mesophase after functionalization of the Pr-Melamine groups inside the channels.
3.2 Optimization of reaction conditions
For optimizing the reaction conditions the Mizoroki–Heck reaction of iodobenzene and methyl acrylate was used as a model reaction. Variation of most important reaction parameters such as the choice of solvents, base type, the catalyst amount and reaction temperature gave the results presented in Table 3. The initial reactants ratio with an excess of methyl acrylate was adopted in order to make up for the loss of the reactant due to evaporation [34], also avoiding palladium leaching caused by the presence of unreacted iodobenzene, due to its oxidative potential [35]. In the first set of experiments performed at a relatively low reaction temperature the optimal solvent was determined (entry 1–10). Polar aprotic solvents showed to be most effective in the reaction, out of which dimethylformamide (DMF) gave the best results and 7.9% yield. In general, the polar aprotic solvents such as DMF could lead to catalyst leaching giving thereby a higher activity [36]. With the optimal solvent and at a slightly higher temperature different organic and inorganic basses were tested (entry 11–18). Low solubility of inorganic basses in DMF makes them unsuitable for systems studied in the current work, while triethylamine led to a fully homogenous reaction slurry and gave the highest yield of the coupling product (entry 15, 77.5%) [37].
In addition to an improvement in the reaction rates utilization of triethylamine is beneficial for Pd re-precipitation [35]. In order to estimate an adequate amount of the catalyst capable of catalyzing the reaction within a reasonable time span, different catalyst loadings and reaction time were elucidated (entry 19–23). A minor increase in conversions was detected when the loading was increased, indicating that even small amounts of Pd are sufficient. In fact, lower loadings of Pd were claimed to be beneficial for improving the catalyst stability because the excess of Pd can lead to catalyst deactivation through Pd nanoparticles growth and agglomeration [38]. The catalyst loading of 0.28 mol % of palladium (entry 19, 48.4% yield) gave satisfactory results and was further used for studying the influence of different reaction temperatures (entry 24–27). As expected, a temperature increase affected positively the reaction rate, most probably because of the aril halide activation [39]. In the current case at 120 °C the full conversion was achieved within 15 min (entry 26, ˃99% yield).
After optimizing the reaction conditions, the scope of the reaction was examined by applying the supported catalyst for the Mizoroki–Heck coupling reaction with a wide range of aryl halides (Cl, Br and I) and olefins. The results are listed in Table 4 containing also as a reference the melting points of obtained products and their comparison with the literature data. As can be seen from Table 4, although the palladium loading was as low as 0.28 mol %, excellent yields were obtained for the examined aryl iodides and bromides (entries 1 to 11). Both, activated and non-activated halides were efficiently utilized. Typically, aryl chlorides are less reactive than other halides. The same behavior was also observed in the current work under the optimal reaction conditions (entries 12 and 13). Therefore, it was concluded that the catalyst can efficiently promote the coupling reaction of aryl iodides and bromides with different olefins.
One of the most important features of heterogeneous catalysts is their recyclability. In order to estimate stability of supported SBA-15/Pr-NH-CH2-Melamine-Pd(0) for the Mizoroki–Heck reaction the performance of the recycled catalyst under optimized conditions in the reaction of iodobenzene and methyl acrylate was tested. Each reaction cycle was performed for 15 min followed by quenching the reaction by cooling to the room temperature, separating the catalyst by filtering and finally flushing several times the residue with diethyl ether and ethyl acetate. Activity of the catalyst was maintained for at least five cycles without a drop in conversion, thereafter a slight decrease was observed still showing high activity for up to the seventh cycle (Fig. 9a). Analysis of the spent catalyst after five reaction cycles also indicated the catalyst stability. FT-IR spectrum of the reused catalyst shown in Fig. 1b confirms stability of the catalyst structure exhibiting also a sharp peak at 2936 cm−1 related to solvents trapped in the catalyst.
A small decrease in conversion in the following cycle presumably can be connected with Pd leaching. More precisely, in the first cycle ca. 8% of Pd and in the second cycle ca. 5% of Pd leached into the reaction mixture. TEM analysis of the spent catalyst after five cycles revealed presence of Pd nanoparticles and confirmed catalyst stability under the studied conditions (Fig. 9b). In addition, agglomeration of the nanoparticles was detected which potentially can be another reason for a subsequent decrease in activity. After selecting random spots on the TEM image of the reused catalyst, the average size of the particles was found to be approximately 27 nm.
Comparison of the results in Table 5 for different reported catalysts used in the cross-coupling reaction of iodobenzene and methyl acrylate illustrates high activity of the catalyst developed in the current work. SBA-15/Pr-NH-CH2-Melamine-Pd(0) catalyst exhibited a remarkable activity with turnover frequency of 1429 h−1 which is a significant improvement compared to the already reported melamine based catalysts (entries 8–10) [45,46,47]. Benchmarking the current study with the literature examples can be difficult since the model reaction is often not the same. By considering analogous catalysts with melamine originating auxiliaries, such as SBA-15/CCMet/Pd(II) [48], Pd-MPMO [49], Pd/G1,2-SBA-15 [50] it can be, nevertheless, stated that in comparison with the literature reports, the current study is much more comprehensive covering the most important variables such as temperature, catalyst amounts, solvents and bases. The synthesized catalyst enabled selective processing of a vide scope of the reactants, including low reactive compounds such as non-activated bromoarenes with the use of low palladium loadings and a short reaction time, making it much more economically and environmentally desirable option.
The reaction mechanism for SBA-15/Pr-NH-CH2-Melamine-Pd(0) seems to follow the one recently proposed in the literature when after coordination of the olefin to the supported Pd(0), the base (Et3N) attacks the alkene coordinated complex to give an alkyl σ-complex. The aryl halide then oxidizes the Pd(0) center, the attached base is released and the alkene coordinates to the Pd(II) complex. Subsequent hydride elimination and removal of hydrogen halide give the desired product and regenerate the catalyst to Pd(0) [56].
4 Conclusions
In summary, an efficient catalyst for the Mizoroki–Heck reaction has been developed. The catalyst comprising Pd nanoparticles deposited on melamine-grafted mesoporous SBA-15 was synthesized and characterized by FT-IR, NMR, TGA, ICP-OES, nitrogen physisorption, XRD, TEM and SEM coupled with EDX. Its performance was studied in the reaction of iodobenzene and methyl acrylate while optimizing the reaction conditions. The usability of the catalyst was demonstrated for a broad scope of the reactants, displaying its efficiency in coupling iodo- and bromo-aromatics with different olefins, while its high activity enabled application of small amounts of Pd and short reaction times. The material was possible to re-use for at least seven consecutive cycles preserving its high activity.
References
Chuentragool P, Yadagiri D, Morita T, Sarkar S, Parasram M, Wang Y, Gevorgyan V (2019) Angew Chem Int Ed 58:1794–1798
Sweeney JB, Adams K, Crook R, Doulcet J, Thapa B, Tran F (2018) J Catal 360:97–101
Motevalizadeh SF, Alipour M, Ashori F, Samzadeh-Kermani A, Hamadi H, Ganjali MR, Aghahosseini H, Ramazani A, Khoobi M, Gholibegloo E (2018) Appl Organomet Chem 32:e4123
Li Y, Wang K, Ping Y, Wang Y, Kong W (2018) Org Lett 20:921–924
Yu J, Hong Z, Yang X, Jiang Y, Jiang Z, Su W (2018) Beilstein J Org Chem 14:786–795
Koy M, Sandfort F, Tlahuext-Aca A, Quach L, Daniliuc CG, Glorius F (2018) Chem - A Eur J 24:4552–4555
Bangar PG, Jawalkar PR, Dumbre SR, Patil DJ, Iyer S (2017) Appl Organomet Chem 32:1–6
Shi KJ, Shu CH, Wang CX, Wu XY, Tian H, Liu PN (2017) Org Lett 19:2801–2804
Kurandina D, Parasram M, Gevorgyan V (2017) Angew Chem Int Ed 56:14212–14216
Wang C, Xiao G, Guo T, Ding Y, Wu X, Loh TP (2018) J Am Chem Soc 140:9332–9336
Liwosz TW, Chemler SR (2012) J Am Chem Soc 134:2020–2023
Nuri A, Vucetic N, Smått JH, Mansoori Y, Mikkola JP, Murzin DY (2019) Catal Lett 149:1941–1951
Nuri A, Vucetic N, Smått JH, Mansoori Y, Mikkola JP, Murzin DY (2020) Catal Lett 150:2617–2629
Ananikov VP, Orlov NV, Beletskaya IP (2007) Organometallics 26:740–750
Jaska CA, Manners I (2004) J Am Chem Soc 126:9776–9785
Huang Y, Ma T, Huang P, Wu D, Lin Z, Cao R (2013) ChemCatChem 5:1877–1883
Zhang Q, Mao Z, Wang K, Thanh N, Phan S, Zhang F (2020) Green Chem 22:3239–3247
Wang K, Liu J, Zhang F, Zhang Q, Jiang H, Tong M, Xiao Y, Thanh N, Phan S, Zhang F, Appl ACS (2019) Mater Interfaces 11:41238–41244
Khajehzadeh M, Moghadam M (2018) J Organomet Chem 863:60–69
Zhang Q, Zhao X, Wei H-X, Li J-H, Luo J (2017) Appl Organomet Chem 31:1–9
Amarasekara AS, Owereh OS (2010) Catal Commun 11:1072–1075
Zhu Y, Kaskel S, Ikoma T, Hanagata N (2009) Microporous Mesoporous Mater 123:107–112
Zhao W, Chen H, Li Y, Li L, Lang M, Shi J (2008) Adv Funct Mater 18:2780–2788
Zhu S, Zhou Z, Zhang D, Jin C, Li Z (2007) Microporous Mesoporous Mater 106:56–61
Lazar A, Vinod CP, Singh AP (2016) New J Chem 40:2423–2432
Zhao D, Huo Q, Feng J, Chmelka BF, Stucky GD (1998) J Am Chem Soc 120:6024–6036
Srivastava R, Srinivas D, Ratnasamy P (2006) Microporous Mesoporous Mater 90:314–326
Al Hamouz OCS, Adelabu IO, Saleh TA (2017) J Environ Manag 192:163–170
Jiang Y, Gao Q (2006) J Am Chem Soc 128:716–717
Desforges A, Backov R, Deleuze H, Mondain-Molval O (2005) Adv Funct Mater 15:1689–1695
Shahbazi A, Younesi H, Badiei A (2011) Chem Eng J 168:505–518
Jürgens B, Irran E, Senker J, Kroll P, Müller H, Schnick W (2003) J Am Chem Soc 125:10288–10300
Kim SY, Parambadath S, Park SS, Ha CS (2017) J Nanosci Nanotechnol 17:7565–7574
Liang L, Nie L, Jiang M, Bie F, Shao L, Qi C, Zhang XM, Liu X (2018) New J Chem 42:11023–11030
Zhao F, Bhanage BM, Shirai M, Arai M (2000) Chem A Eur J 6:843–848
Caporusso AM, Innocenti P, Aronica LA, Vitulli G, Gallina R, Biffis A, Zecca M, Corain B (2005) J Catal 234:1–13
Liu G, Hou M, Song J, Jiang T, Fan H, Zhang Z, Han B (2010) Green Chem 12:65–69
de Vries AHM, Mulders JMCA, Mommers JHM, Henderickx HJW, de Vries JG (2003) Org Lett 5:3285–3288
Kamilah S, Soh C, Jusoh SA, Sukeri M, Yusof M, Khairul WM, Shamsuddin M (2018) Int J Eng Technol 7:467–469
Huang S-H, Chen J-R, Tsai F-Y (2010) Molecules 15:315–330
Sun P, Zhu Y, Yang H, Yan H, Lu L, Zhang X, Mao J (2012) Org Biomol Chem 10:4512–4515
Schmidt B, Berger R (2013) Adv Synth Catal 355:463–476
Yu L, Huang Y, Wei Z, Ding Y, Su C, Xu Q (2015) J Org Chem 80:8677–8683
Górski B, Talko A, Basak T, Barbasiewicz M (2017) Org Lett 19:1756–1759
Bodaghifard MA (2019) J Organomet Chem 886:57–64
Aryanasab F, Shabanian M, Laoutid F, Vahabi H (2021) Appl Organomet Chem 2:1–12
Zhong S (2017) Turk J Chem 41:773–783
Veisi H, Kordestani D, Faraji AR (2014) J Porous Mater 21:141–148
Elavarasan S, Kala K, Muhammad I, Bhaumik A, Sasidharan M (2019) Mol Catal 476:1–10
Lou Y, Shantz DF (2017) J Mater Chem A 5:14070–14078
Han W, Liu N, Liu C, Jin ZL (2010) Chin Chem Lett 21:1411–1414
Rosol M, Moyano A (2005) J Organomet Chem 690:2291–2296
Cassez A, Kania N, Hapiot F, Fourmentin S, Monflier E, Ponchel A (2008) Catal Commun 9:1346–1351
Omar S, Abu-Reziq R (2014) J Phys Chem C 118:30045–30056
Sobhani S, Pakdin-Parizi Z (2014) Appl Catal A Gen 479:112–120
Nuri A, Mansoori Y, Bezaatpour A (2019) Appl Organomet Chem 33:1–15
Funding
Open access funding provided by Abo Akademi University (ABO).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Nuri, A., Bezaatpour, A., Amiri, M. et al. Pd Nanoparticles Stabilized on the Cross-Linked Melamine-Based SBA-15 as a Catalyst for the Mizoroki–Heck Reaction. Catal Lett 152, 991–1002 (2022). https://doi.org/10.1007/s10562-021-03691-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10562-021-03691-9