Abstract
Objectives
Disinfection of alginate impression materials is a mandatory step to prevent cross-infection in dental clinics. However, alginate disinfection methods are time-consuming and exert a negative impact on accuracy and mechanical properties. Thus, this study aimed to prepare disinfecting agents (CHX and AgNO3) and silver nanoparticles reduced by a natural plant extract to produce a self-disinfecting dental alginate.
Methods
Conventional alginate impression material was used in this study. Silver nitrate (0.2% AgNO3 group) and chlorohexidine (0.2% CHX group) solutions were prepared using distilled water, and these solutions were later employed for alginate preparation. Moreover, a 90% aqueous plant extract was prepared from Boswellia sacra (BS) oleoresin and used to reduce silver nitrate to form silver nanoparticles that were incorporated in the dental alginate preparation (BS+AgNPs group). The plant extract was characterized by gas chromatography/mass spectrometry (GC/MS) analysis while green-synthesized silver nanoparticles (AgNPs) were characterized by UV-visible (UV–vis) spectroscopy and scanning electron microscopy (SEM). An agar disc diffusion assay was used to test the antimicrobial activity against Candida albicans, Streptococcus mutans, Escherichia coli, methicillin-resistant and susceptible Staphylococcus aureus strains, and Micrococcus luteus. Agar plates were incubated at 37 ± 1 °C for 24 h to allow microbial growth. Diameters of the circular inhibition zones formed around each specimen were measured digitally by using ImageJ software.
Results
Chemical analysis of the plant extract revealed the presence of 41 volatile and semi-volatile active compounds. UV–Vis spectrophotometry, SEM, and EDX confirmed the formation of spherical silver nanoparticles using the BS extract. CHX, AgNO3, and the BS+AgNPs modified groups showed significantly larger inhibition zones than the control group against all tested strains. BS+AgNPs and CHX groups showed comparable efficacy against all tested strains except for Staphylococcus aureus, where the CHX-modified alginate had a significantly higher effect.
Conclusions and clinical relevance
CHX, silver nitrate, and biosynthesized silver nanoparticles could be promising inexpensive potential candidates for the preparation of a self-disinfecting alginate impression material without affecting its performance. Green synthesis of metal nanoparticles using Boswellia sacra extract could be a very safe, efficient, and nontoxic way with the additional advantage of a synergistic action between metal ions and the phytotherapeutic agents of the plant extract.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Many materials are available nowadays to take primary and secondary impressions for patients in dental clinics [1]. The choice of an impression material for a particular situation is mainly dependent on the treatment protocol and the operator’s preference. Meanwhile, hydrocolloids and elastomeric polymers are the most used impression materials for various dental treatments [2]. Hydrocolloid dental materials include both agar–agar and alginates, which are viscous liquids, present in a sol state or a gelatinous consistency.
Alginates are salts of alginic acid, a polysaccharide extracted from the cell walls of brown algae. They belong to the Phaeophyceae family, which is widespread, especially in the colder oceans of the Northern Hemisphere [3]. Dental alginates are irreversible elastic hydrocolloids that were developed in the 1940s when the agar impression material was limited [4]. Irreversible alginates consist of salts of alginic acid, calcium sulfate as a reactor, zinc oxide, potassium titanium fluoride, diatomaceous earth, and coloring or flavoring agents [5]. Alginate is provided in the form of a powder to be mixed with water and set by a chemical reaction that cross-links the carbohydrate polymer, forming a hydrogel [5].
Alginates are one of the most frequently and routinely used dental materials in every dental practice, especially at the first dental visit for a pre-treatment evaluation. Their common usage is due to their cost-effectiveness, ease of use, and fast setting time that can be even controlled by temperature [6]. Disadvantages include less accurate reproduction of details as compared with elastomeric impression materials, poor dimensional stability, and inadequate retention of non-perforated trays [7]. Moreover, hydrocolloids are hydrophilic by nature; therefore, they swell if immersed in water or disinfectant; and thus; their dimensional stability upon disinfection and storage is problematic [8].
Dental impressions present a source of cross-infection to the dentist and dental technicians since they are exposed to blood and saliva inside the oral cavity; hence, disinfection is mandatory for impression materials [9]. On the other hand, distortion can be a problem if disinfection guidelines are not strictly followed. Disinfectant sprays are used for alginate impressions, but they do produce air bubbles in the cast, thereby affecting accuracy [10]. Although immersion in disinfectants like 1% sodium hypochlorite or 2% glutaraldehyde can result in dimensional changes of only 0.1%, still the quality of the impression surface may be greatly compromised if the recommended period and other factors are not strictly controlled [11, 12].
Attempts to incorporate disinfectants into the alginate powder or mixing water were found to be an effective way of disinfection with minimal adverse effects on dimensional accuracy and surface details [13, 14]. Follow-up studies of irreversible hydrocolloid impression materials pre-impregnated with disinfectants have shown that this technique saves time, is active against oral pathogens, and demonstrates greater dimensional stability than spray and immersion techniques [15].
The antibacterial activity of metal and metal oxide nanoparticles is extensively studied in medicine [16, 17]. Silver and its compounds have been used as antimicrobial agents for various medical purposes. Silver ions are effective against bacteria, viruses, and fungi besides causing no harm to humans at low concentrations [18]. Materials with at least one external dimension of 1–100 nm are defined as nanomaterials or nanoparticles (NPs), and they have attracted increasing interest in recent years, especially in dentistry [19]. Silver nanoparticles have demonstrated unique and significantly different physical and chemical properties compared to their macroscopic counterparts. The smaller the nanoparticles, the greater the surface-to-volume ratio, dispersion, and antimicrobial efficacy [19].
Conventional approaches for the production of nanoparticles (NPs) are typically expensive, toxic, complicated, and non-ecological [20]. Green nanotechnology is a recent approach, which utilizes microorganisms, plants, or their extracts as reducing and capping agents in the synthesis of AgNPs. Plants play an important role in the biosynthesis of NPs and their major advantage is that they are easily available, safe, and contain a variety of metabolites that can contribute to the reduction of silver ions [20]. Green nanoparticles exhibit distinct characteristics compared to those generated through physical and chemical means. The green process employs a bottom-up approach to create magnetic nanoparticles using biological constituents like plant extracts or bacteria to replace the costly chemical-reducing agents. The eco-friendly transformation of microparticles into NPs through green reduction is environmentally favorable, sustainable, devoid of chemicals, cost-effective, and scalable. Additionally, green synthesis leads to the recovery and recycling of valuable metal salts like gold (Au) and silver (Ag) from waste streams [21, 22]. Boswellia sacra (B. sacra) is a tree in the genus Boswellia from which frankincense oleo gum resin is collected. It is native to Oman, Yemen, and Somalia. B. sacra finest sorts are presented under the local names Houjri, Najdi, and Sahli or Shaebi, based on the region of cultivation in Oman. Houjri is the first-grade, most expensive resin that is growing in the north of the Samhan Mountains [23]. Resin essential oils contain several pharmacologically active compounds (monoterpenes, sesquiterpenes monoterpenes, sequiterpinols, and ketones) that have antimicrobial activity against important human pathogens, both bacterial and fungal organisms, such as Staphylococcus aureus, Escherichia coli, Proteus vulgaris, and Candida albicans [23].
To the best of our knowledge, Boswellia sacra (B. sacra) plant extract has never been used for the green synthesis of silver nanoparticles and has not been incorporated before or used for the disinfection of any hydrocolloid impression material in dentistry. Therefore, in our previous and present investigations, we aimed to replace the water used for the preparation of alginate with a prepared aqueous solution of B. sacra added to silver nitrate in a given concentration to biosynthesize nanoparticles for enhanced antimicrobial activity. Moreover, a 0.2% silver nitrate solution and a 0.2% CHX solution were used for the preparation of two other antimicrobial-modified groups for comparison.
Our former results which assessed our modification on alginate physical and mechanical properties showed that detail reproduction and accuracy of alginate were not negatively impacted by the different self-disinfection modifications. Moreover, elastic recovery was improved by the addition of CHX, AgNO3, and BS + AgNPs. Additionally, it was found that all groups reported tear strength values that were within the acceptable range, with CHX and BS + AgNPs showing significantly higher tear strength values compared to the control group [24].
Therefore, based on the fact that the green synthesis of metal nanoparticles using the Boswellia sacra extract did not alter the functional performance of alginate, this study aimed to chemically characterize B. sacra extract and to confirm the production of the green-synthesized nanoparticles using color change, UV–Vis spectroscopy, and scanning electron microscopy (SEM). Moreover, the effect of the modifications was tested along with control alginate against six microbial strains to confirm its efficacy.
Materials and methods
Materials
Materials and microbial strains used in the present study are listed in Table 1.
Methods
Preparation of the silver nanoparticles in Boswellia sacra (B. sacra) extract
Frankincense resin (50 g) was washed, dried, and frozen overnight. The freezing step enabled the grinding of the resin in a blender to a fine powder. Afterward, the resin powder was soaked in an ethanol/water mixture (90% water : 10% ethanol) for 3 days and extracted using a Soxhlet extractor for 7 h. Filtration of the extract was performed using Whatman’s paper 1. Afterward, the extract was stored at 4 °C until usage.
For preparation and reduction of the silver nanoparticles, 10 ml of the filtrate was added to 30 ml of 0.2% AgNO3 solution in a conical flask with continuous stirring at a speed of 400 rpm. The mixture was incubated for 3 days at room temperature in the darkness, with the solution color turning from white to brown, demonstrating the formation of AgNPs (Fig. 1).
Preparation of 0.2% silver nitrate and 0.2% CHX solutions
0.2% AgNO3 solution was prepared by adding 2 g of 99% silver nitrate powder to 250 ml of distilled water and mixing on a vortex mixer for a few minutes. Afterward, 750 ml of distilled water was added to the mixture and vortexed for another few minutes. For the 0.2% CHX solution, 2 g of chlorohexidine powder was added to 1000 ml distilled water and vortexed for 15 min for complete dissolution of the powder in the liquid.
Specimen’s preparation and grouping
A sensitive balance was used to weigh the alginate powder for each specimen to be mixed with a specific amount of the designated liquid to prepare four different groups (water (control), 0.2 % AgNo3, 0.2 % CHX, and BS+ AgNPs) for testing and comparison. Hand mixing was carried out at 23 ± 1 °C, and relative humidity until a homogenous mixture was obtained according to the manufacturers’ instructions.
Chemical analysis of plant extract mixture (GC/MS)
One milliliter of BS extract was injected to analyze its chemical constituents at the Agriculture Research Center, Giza, Egypt using a gas chromatograph (GC) (Agilent Technologies 7890A) attached with a mass spectrometer (MS) (MSD, Agilent 7000). The GC was equipped with a polar Agilent HP-5%-phenyl methyl poly siloxane and a capillary column of 0.25-mm inner diameter, and 0.25-μm film thickness. The injector temperature was set at 200 °C while the detector temperature was set at 250 °C. Helium was the carrier gas with a linear velocity of 1 ml/min. Mass spectra had an acquisition mass range of 50–800 m/z and an interface temperature of 250 °C. The quantification of components was carried out using a percent relative peak area. Active compounds were identified by comparing their relative retention times with authentic compounds and by computer matching with the NIST and WILEY library as well as by relating the spectral data with those described in the literature [25].
Characterization of the Ag nanoparticles
Color change and ultraviolet-visible (UV–Vis) spectroscopy
Bioreduction of the prepared mixture was observed by monitoring the color changes from white to dark brown visually and by using UV–visible spectrophotometer (UviLine 9400, Schott, Mainz, Germany). Spectroscopy absorption analysis was performed by measuring 1 ml aliquots at different time intervals. Samples were scanned in the 200–700 nm range, with a scanning speed of 475 nm/min, and at 1-cm optical path at room temperature. UV–vis absorption spectra measurements started 1 h after incubating the AgNO3 solution with B. sacra extract and distilled water was used as a blank reference [26, 27].
Scanning electron microscopy (SEM)
The structures, sizes, and shapes of the nanoparticles were examined using a scanning electron microscope (SEM, Philips XL 30, Philips, Eindhoven, The Netherlands). A thin film of the prepared BS+SNPs solution was placed on a carbon-coated copper grid and allowed to dry in the air for 1 h. The SEM operated at 10 kV and magnifications of 1200×, and 2000×, using spot size 3. The measurements of the different spherical particles and clusters were taken using Image J software (Wayne Rasband (NIH), Version 1.53k) [28].
Antimicrobial activity analysis
Agar well diffusion assays were used to assess the antimicrobial activity against Streptococcus mutans (S. mutans), methicillin-resistant Staphylococcus aureus (MRSA), Escherichia coli (E. coli), Candida albicans (C. albicans) and Micrococcus luteus (M. luteus), and Staphylococcus aureus (S. aureus). Müller–Hinton agar plates were overlaid with 0.1 ml of suspensions of the indicator strains that had been adjusted to an OD600 of 0.1 using a UV–Vis spectrophotometer (UviLine 9400). After 10 min, the suspensions were removed by pipetting and the plates were left to dry for 20 min.
For each modification, three replicates of freshly mixed alginate were prepared according to the manufacturer’s instructions using sterile plastic spatulas. Wells (5-mm diameter) were punched into each agar plate using a sterile cork borer to receive the freshly mixed, unset different alginate samples. The antimicrobial activities of the tested samples were assessed after incubating the plates (Heraeus GmbH & Co. KG, Hanau, Germany) at 37 ± 1 °C for 24 h [29]. The diameters of the circular inhibition zones formed around each specimen were measured digitally. High-resolution digital pictures of all Petri dishes were taken using a Canon T3i (Canon Corp, NY, USA) digital single-lens reflex camera with an 18–55 mm lens, which allowed a magnification of up to 35×. The camera was fixed on a tripod to standardize the shooting angle and to standardize the distance between the camera lens and plates. Additionally, a base was prepared with reference points to ensure standardization of the plates’ placement. High-resolution digital pictures were transferred to a computer, and ImageJ (Wayne Rasband (NIH), Version 1.53k) software was used to measure inhibition zones. Pictures were rescaled and the value of each inhibition zone was taken three times [30].
Statistical analysis
Results are presented as mean and standard deviation (SD). The Shapiro–Wilk normality test was used to examine whether the variables follow a normal distribution. All quantitative variables showed parametric distribution; therefore, one-way analysis of variance (ANOVA) was used for comparison between the groups. Tukey’s post hoc test was used employed for pairwise comparison between the groups when the ANOVA test was significant. The significance level was set at p ≤ 0.05. Statistical analysis was performed using Minitab 17.1.0 for Microsoft Windows.
Results
Chemical analysis
Gas chromatography/mass spectrometry revealed the presence of 41 volatile and semi-volatile active compounds (Table 2).
Characterization of the Ag nanoparticles
Color change and UV-visible spectroscopy analysis
The biological synthesis of AgNPs using B. sacra extract as a reducing and stabilizing agent was confirmed primarily by the color change from white to light brown and then dark brown. Silver nanoparticle surface plasmon excitation causes the color change in the solution, which is the key and notable evidence for the formation of Ag NPs. Several UV–Vis absorption spectra were measured after 0, 2, 4, 24, and 48 h and 3-day intervals (Fig. 2). An absorption peak localized at 300 nm was observed which is supposed to be related to B. sacra extract. Furthermore, the absorption spectra showed a maximum absorbance peak at 440 nm which is related to the localized surface plasmon resonance of AgNPs. A gradual increase in the intensity (2.119, 2.281, 2.449, and 2.906 a.u) as a function of time was also observed, indicating an increase of the biosynthesized AgNPs with the maximum intensity being observed after 3 days.
Scanning electron microscopy
The morphological images of Ag NPs produced by green synthesis are shown in Figs. 3 and 4. The results indicate the presence of spherical nanoparticles, as well as clusters of spherical nanoparticles with different diameters ranging from 50 to 100 nm.
Antimicrobial activity
Agar diffusion tests were performed in triplicates. The variables showed a parametric distribution, and thus, one-way ANOVA was used to test the antimicrobial effect of BS+Ag (AgNPs), CHX, AgNO3, and control groups against the six different microbial strains followed by Tukey’s post hoc test for pairwise comparison between the tested groups (Figs. 5 and 6). The ANOVA indicated that there was a statistically significant antibacterial effect of the three modified groups’ alginates against all strains, F(4, 30) = 63.23, p-value < 0001. Post hoc comparison using Tukey’s test indicated that the three modified groups’ mean values showed significantly higher antibacterial activities than the control (Fig. 5).
Mean values (Fig. 6) against these strains were as follows: S. aureus (control = 4.2 mm, SD ± 0.2; BS+AgNPs = 11.0 mm, SD ± 1.3; CHX= 13.5 mm, SD ± 0.1; AgNO3 = 8.8 mm, SD ± 0.3), M. luteus (control = 7.8 mm, SD ± 2.2; BS+AgNPs = 15.2 mm, SD ± 1.2; CHX = 19.6 mm, SD ± 0.8; AgNO3 = 15.4 mm, SD ± 0.9), whereas S. mutans (control = 0.0 mm, SD ± 0.0; BS+AgNPs = 5.0 mm, SD ± 0.5; CHX = 11.4 mm, SD ± 0.6; AgNO3 = 4.3 mm, SD ± 0.2) and MRSA (control = 5.0 mm, SD ± 0.9; BS+AgNPs = 10.9 mm, SD ± 0.6; CHX = 12.7 mm, SD ± 1; AgNO3 = 9.4 mm, SD ± 1.2). Furthermore, against E. coli, there was a statistically insignificant difference between the mean values of BS+AgNP (M = 7.5 mm, SD ± 1.9) and AgNO3 (M = 5.9 mm, SD ± 2), whereas, CHX (M = 11.8 mm, SD ± 0.2) showed the highest mean values. No significant differences were observed between the three modified groups against C. albicans (control = 0.0 mm, SD ± 0.0; BS+AgNPs = 12.8 mm, SD ± 2.2; CHX = 12.0 mm, SD ± 0.4; AgNO3 = 14.5 mm, SD ± 2.4).
Discussion
Alginate impressions are regularly contaminated with patients’ blood and saliva, thus acting as a potential medium for the transfer of infectious microorganisms and viruses between patients, operators, and dental auxiliaries [9]. The presence of numerous microbes, including streptococci, staphylococci, Candida, Pseudomonas aeruginosa, and MRSA on alginate impressions and gypsum casts has been documented and can be a cause of infections in dental clinics [31]. Since alginates undergo syneresis and imbibition according to the surrounding conditions, post-setting disinfection by spraying or immersion often compromises the accuracy of alginate impressions [32].
The difficulties associated with disinfecting irreversible hydrocolloid impression materials have directed this study to develop a self-disinfecting dental alginate material by mixing alginate powder with silver nanoparticles synthesized by Boswellia sacra extract. On the other hand, dental alginate was modified with 0.2% CHX and 0.2% silver nitrate solutions as well for self-disinfection. The three modified groups were tested and compared with unmodified dental alginate as a control.
In the present study, a color change was observed over time after mixing BS extract and silver nitrate solution. The color change resulted from the excitation of surface plasmon resonance (collective movement of free electrons in the silver when light falls on it) due to the reduction of Ag2+ ions to Ag 0 by biomolecules such as phenols, flavonoids, ketones, tannins, and proteins present in BS extract [33]. These phytochemicals contain hydroxyl and ketone groups that induce the reduction of Ag ions to form appropriate nuclei that grow during the development phase into spherical AgNPs [34].
Furthermore, UV–Vis spectrophotometry confirmed the formation of AgNPs by yielding a bell-shaped spectrum after the different time intervals. The broad plasmon band may be due to the presence of plant metabolites in the solution, which may adsorb the light in this spectrophotometric range as well. The peak was observed at 440 nm, and an absorbance between 400 and 460 nm is always characteristic for the formation of silver nanoparticles [35]. It is worth mentioning that spherical nanoparticles show only a single SPR band and the number of peaks increases with an increasing range of particle shapes [36, 37]. SEM magnified images of samples have shown that the particles were mostly spherical with a size distribution in the range of 50 to 100 nm. Agglomerated AgNPs were also present, which may be a sign of sedimentation [38].
The antimicrobial activity of the modified groups was tested using agar diffusion assays against different microbial strains including four Gram-positive bacteria (S. aureus, methicillin-sensitive and resistant, S. mutans, and M. luteus), one Gram-negative bacterium (E. coli) and a yeast (C. albicans). The three modified groups were significantly more active than the unmodified alginate against all microbial strains. Results showed that the BS+AgNPs group differed insignificantly from AgNO3 only against all strains except S. aureus. On the other hand, the antimicrobial activity of BS+AgNPs was comparable to the CHX group against C. albicans and MRSA. CHX showed significantly higher activity than all other groups against S. mutans, S. aureus, E. coli, and M. luteus. The unmodified alginate also showed a reproducible weak antibacterial activity against both S. aureus strains and M. luteus, which might be due to the presence of zinc ions in the alginate powder.
The results are in agreement with several studies, which reported that the incorporation of disinfecting agents such as silver nanoparticles, quaternary ammonium compounds, chlorhexidine, iodine, bisguanidine compounds, and ammonium chloride into the impression materials eliminates the need for separate disinfection of the impression after removal from the mouth [39, 40]. Our results showed also that BS+AgNPs were efficient against an MRSA which is an antibiotic-resistant strain and thus might have the potential to be used in medicine. Profound antimicrobial activities of green-synthesized AgNPs were previously reported by Vanlalveni et al. [41], Akhtar et al [42], and Tahmasebi et al. [43].
The antimicrobial activity of BS+AgNPs could be due to the synergistic action of both the plant extract and AgNPs. Different phytochemical constituents were identified by gas chromatography/mass spectrometry in this and a previous study [44]. Terpenoids (e.g., boswellic acids, cymene-7-ol, L-pinocarveol, carveol, and cis-sesquisabinene hydrate) were detected in considerable amounts in the B. sacra extract. Although the antibacterial mode of action of terpenes remains mostly unknown, it has been reported that most terpenoids act by partitioning into the membrane, increasing its permeability and dissipating proton motive force [45].
Carveol, for example, has been shown to affect the membrane integrity in E. coli and S. aureus and induce leakage of potassium from S. aureus cells [46]. Moreover, alkaloids (e.g., quinidine), sterols (e.g., stigmasterol), flavonoids (e.g., vitexin), phenols (e.g., cis-p-Mentha-2, 8-dien-1-ol), and saponins (e.g., squalane) were detected. Many of these secondary plant compounds have long-established antimicrobial activities, e.g., saponins damage the bacterial cell membrane [47], stigmasterol is bacteriostatic for MRSA [48], and vitexin inhibits biofilm formation of P. aeruginosa and alters the surface properties of S. aureus) [49].
Silver in a nanometre scale of less than 100 nm is toxic to a wide range of microorganisms [50]. Although the exact mechanism of silver nanoparticles’ antibacterial effects has not been completely clarified, various antibacterial actions have been proposed [51]. Silver nanoparticles can penetrate bacterial cell walls, damage the cytoplasmic membrane, and even result in cell lysis [50]. There is also an influence of the particle size and shape on the release of silver ions since AgNPs with spherical or quasi-spherical format are more susceptible to silver release, due to their larger surface area [51]. Moreover, Gram-negative bacteria are more susceptible to silver nanoparticles than Gram-positive strains. The cell walls of Gram-positive bacteria are composed of a thick peptidoglycan layer of linear polysaccharide chains cross-linked by short peptides, thus forming a more rigid structure leading to difficult penetration of the AgNPs compared to the Gram-negative bacteria, where the cell wall possesses thinner peptidoglycan layers [52, 53].
Silver nitrate, which is a suspension of sub-microscopic silver ions, can significantly reduce the duration and severity of many bacterial infections [54]. Silver is an inert metal but it is biologically active in an aqueous environment in which it is present in an ionic soluble state (Ag+) [55]. One of the main advantages of silver is its oligo dynamic effect, of having high microbicidal capacity in water at a very low concentration (one part per million) [55]. One of the important mechanisms of Ag+ toxicity is the ability of silver ions to interact with the bacterial inner membrane and impair its integrity. Additionally, silver ions target the SH groups on proteins, disrupt their disulfide bonds, and inactivate dehydratases by breaking down 4Fe-4S clusters [56]. A recent study showed that in S. aureus, silver ions target proteins involved in glycolysis, pentose phosphate cycle, and defense against ROS [57].
The toxicity of silver nitrate is dosage-dependent; oral ingestion of more than 2 g of silver nitrate can be fatal [54]. Silver nitrate rapidly reacts with chloride yielding extremely non-soluble silver chloride that causes a fatal electrolyte imbalance. However, the dosage of silver nitrate used in this study (0.2%) is very low, and for the BS+AgNPs group, it was even lower. One milliliter of 0.2% silver nitrate solution contains 0.002 g silver nitrate. A 38-ml solution that is used to make a full arch impression contains 0.08 mg silver nitrate and is equivalent to 0.33% of a fatal dose. In addition, it should be taken into consideration that silver nitrate was not used in a free form or ingested, but instead, it went through a chemical reaction and is enclosed in a gel that is used topically inside the mouth and not in a liquid form.
Chlorhexidine in the present study was used as it has a proven antimicrobial activity against various microbial strains [58]. The selected concentration of CHX (0.2%) is believed to be effective for oral disinfection and plaque inhibition with no serious side effects [58, 59]. The positively charged chlorhexidine works actively against bacteria by binding to the negatively charged sites on the bacterial cell wall causing destabilization of the cytoplasmic membrane and may affect membrane proteins [60, 61]. The bacterial uptake of chlorhexidine is very fast, typically functioning within 20 s. For C. albicans (fungus), the mechanism of action is almost the same in that the fungus uptakes chlorhexidine rapidly and damages the integrity of the cell wall and the plasma membrane resulting in leakage and cell death [62].
It is important to note that impression materials that come into contact with contaminated saliva and blood can pose a substantial risk of cross-contamination, not only with bacteria and fungi but also with highly contagious viruses like hepatitis B, hepatitis C, herpes, and HIV. As a result, there are plans to conduct further research to assess the effectiveness of the green-modified alginate against these viruses.
Conclusions
Within the context of this study, it can be concluded that the usage of Boswellia sacra plant extract was effective for the biosynthesis of AgNPs in a simple, inexpensive, and ecologically friendly way at room temperature. The analysis of the BS extract confirmed the presence of different organic compounds that can act as reducing and stabilizing agents for the biosynthesis of AgNPs. Furthermore, the antimicrobial activity of dental alginate was enhanced by the incorporation of 0.2% CHX, 0.2% AgNO3, and green-synthesized AgNPs against all tested microbial strains. Future work involving testing the effect of the three used antimicrobial agents on the dimensional accuracy, detail reproduction, tear strength, elastic recovery, setting time, and flow of alginate is in progress.
Data availability
The datasets used and/or analyzed during the current study are available from the corresponding author upon reasonable request.
References
Punj A, Bompolaki D, Garaicoa J (2017) Dental impression materials and techniques. Dent Clin N Am 61:779–796. https://doi.org/10.1016/j.cden.2017.06.004
van Noort R (2007) Introduction to dental materials, 3rd edn. Mosby, Elsevier, pp 191–195
Saji S, Hebden A, Goswami P, Du C (2022) A Brief review on the development of alginate extraction process and its sustainability. Sustainability 14:5181. https://doi.org/10.3390/su14095181
Shen C, Rawls HR (2013) Phillips’ science of dental materials, 18th edn. Elsevier/Saunders, St. Louis
Cervino G, Fiorillo L, Herford AS, Laino L, Troiano G, Amoroso G, Crimi S, Matarese M, D’Amico C, Nastro Siniscalchi E, Cicciù M (2018) Alginate materials and dental impression technique: a current state of the art and application to dental practice. Mar Drugs 17:18. https://doi.org/10.3390/md17010018
Nandini VV, Venkatesh KV, Nair KC (2008) Alginate impressions: a practical perspective. J Conserv Dent 11:37–41. https://doi.org/10.4103/0972-0707.43416
Wilson HJ (1996) Some properties of alginate impression materials relevant to clinical practice. Br Dent J 121:463–467
Craig RG, Power JM (2002) Restorative dental materials, 11th edn. Mosby, St. Louis, pp 87–99
Flanagan DA, Palenik CJ, Setcos JC, Miller CH (1998) Antimicrobial activities of dental impression materials. Dent Mater 14:399–404
Sofou A, Larsen T, Owall B, Fiehn NE (2002) In vitro study of transmission of bacterial from contaminated metal models to stone models via impressions. Clin Oral Investig 6:166–170
Dorner AR, Ferraz da Silva J, Uemura ES, Borges AL, Fernandes Junior V, Yamamoto ET (2014) Effect of disinfection of irreversible hydrocolloid impression materials with 1% sodium hypochlorite on surface roughness and dimensional accuracy of dental stone casts. Eur J of General Dent 3:113–119
Muzaffar D, Braden M, Parker S, Patel MP (2012) The effect of disinfecting solutions on the dimensional stability of dental alginate impression materials. Dent Mater 28:749–755
Jones ML, Newcombe RG, Bellis H, Bottomley J (1990) The dimensional stability of self-disinfecting alginate impressions compared to various impression regimes. Angle Orthod 60:123–128
Juhasz I (2002) Experiences with the use of povidone iodine-containing local therapeutics in dermatological surgery and in the treatment of burns: testing for allergic sensitization in post-surgery patients. Dermatology 204(52–58):26
Ismail HA, Asfour H, Shikho SA (2016) A self-disinfecting irreversible hydrocolloid impression material mixed with povidone iodine powder. Eur J Dent 10:507–511. https://doi.org/10.4103/1305-7456.195172
Raffi M, Mehrwan S, Bhatti TM, Akhter JI, Hameed A, Yawar W, Masood ul Hasan M (2010) Investigations into the antibacterial behaviour of copper nanoparticles against Escherichia coli. Ann Microbiol 60:75–80
Sharma P, Goyal D, Chudasama B (2002) Antibacterial activity of colloidal copper nanoparticles against Gram-negative (Escherichia coli and Proteus vulgaris) bacteria. Lett Appl Microbiol 74:695–706. https://doi.org/10.1111/lam.13655
Balandin GV, Suvorov OA, Shaburova LN et al (2015) The study of the antimicrobial activity of colloidal solutions of silver nanoparticles prepared using food stabilizers. J Food Sci Technol 52:3881–3886. https://doi.org/10.1007/s13197-014-1455
Yazdanian M, Rahmani A, Tahmasebi E, Tebyanian H, Yazdanian A, Mosaddad SA (2021) Current and advanced nanomaterials in dentistry as regeneration agents: an update. Mini Rev Med Chem 21(7):899–918. https://doi.org/10.2174/1389557520666201124143449
Mussin J, Robles-Botero V, Casañas-Pimentel R et al (2021) Antimicrobial and cytotoxic activity of green synthesis silver nanoparticles targeting skin and soft tissue infectious agents. Sci Rep 11:14566. https://doi.org/10.1038/s41598-021-94012-y
Yazdanian M, Rostamzadeh P, Rahbar M, Alam M, Abbasi K, Tahmasebi E et al (2022) The potential application of green-synthesized metal nanoparticles in dentistry: a comprehensive review. Bioinorg Chem Appl 2022:2311910
Mosaddad SA, Hussain A, Tebyaniyan H (2023) Green alternatives as antimicrobial agents in mitigating periodontal diseases: a narrative review. Microorganisms 11(5):1269. https://doi.org/10.3390/microorganisms11051269
Di Stefano V, Schillaci D, Cusimano MG, Rishan M, Rashan L (2020) In vitro antimicrobial activity of Frankincense oils from Boswellia sacra grown in different locations of the Dhofar Region (Oman). Antibiotics 9:195. https://doi.org/10.3390/ant
Singer L, Bourauel C (2023) Mechanical and physical properties of an experimental chemically and green-nano improved dental alginate after proven antimicrobial potentials. Gels 9(5):429. https://doi.org/10.3390/gels9050429
Santana P, Miranda M, Payrol J, Silva M, Hernández V, Peralta E (2013) Gas chromatography-mass spectrometry study from the leaves fractions obtained of vernonanthura patens (Kunth) H. Rob. \Int J Org Chem 3:105–109. https://doi.org/10.4236/ijoc.2013.32011
Annamalai J, Nallamuthu T (2016) Green synthesis of silver nanoparticles: characterization and determination of antibacterial potency. Appl Nanosci 6:259–265. https://doi.org/10.1007/s13204-015-0426-6
Giri AK, Jena B, Biswal B et al (2022) Green synthesis and characterization of silver nanoparticles using Eugenia roxburghii DC extract and activity against biofilm-producing bacteria. Sci Rep 12:8383. https://doi.org/10.1038/s41598-022-12484-y
Ahsan A, Farooq MA, Ahsan Bajw A, Parveen A (2020) Green synthesis of silver nanoparticles using Parthenium hysterophorus: optimization, characterization and in vitro therapeutic evaluation. Molecules 25:3324. https://doi.org/10.3390/molecules25
Ginjupalli K, Alla RK, Tellapragada C, Gupta L, Upadhya Perampalli N (2016) Antimicrobial activity and properties of irreversible hydrocolloid impression materials incorporated with silver nanoparticles. J Prosthet Dent 115:722–728. https://doi.org/10.1016/j.prosdent.2015.11.006
Singer L, Habib SI, Shalaby HE, Saniour SH, Bourauel C (2022) Digital assessment of properties of the three different generations of dental elastomeric impression materials. BMC Oral Health 22:379. https://doi.org/10.1186/s12903-022-02419-4
Egusa H, Watamoto T, Abe K, Kobayashi M, Kaneda Y, Ashida S, Matsumoto T, Yatani H (2008) An analysis of the persistent presence of opportunistic pathogens on patient-derived dental impressions and gypsum casts. Int J Prosthodont 21:62–68
Anusavice KJ (2003) Phillips’ science of dental materials, 11th edn. WB Saunders, Philadelphia, pp 239–248
Erdoğan T, Yılmaz FF, Kıvçak B, Özyazıcı M (2016) Green synthesis of silver nanoparticles using Arbutus andrachne leaf extract and its antimicrobial activity. Trop J Pharm Res 15:1129–1136
Sharifi-Rad M, Pohl P (2020) Synthesis of biogenic silver nanoparticles (AgCl-NPs) using a Pulicaria vulgaris Gaertn. aerial part extract and their application as antibacterial, antifungal and antioxidant agents. Nanomaterials 10:638
Ghaffari-Moghaddam M, Hadi-Dabanlou R, Khajeh M et al (2014) Green synthesis of silver nanoparticles using plant extracts. Korean J Chem Eng 31:548–557. https://doi.org/10.1007/s11814-014-0014-6
Banerjee P, Satapathy MK, Mukhopahayay A, Das P (2014) Leaf extract mediated green synthesis of silver nanoparticles from widely available Indian plants: synthesis, characterization, antimicrobial property and toxicity analysis. Bioresources and Bioprocessing 1:1–10
Raut Rajesh W, Lakkakula Jaya R, Kolekar Niranjan S, Mendhulkar Vijay D, Kashid Sahebrao B (2009) Phytosynthesis of silver nanoparticle using Gliricidia sepium (Jacq.). Curr Nanosci 5:117–122
Xu J, Han X, Liu H et al (2006) Synthesis and optical properties of silver nanoparticles stabilized by Gemini surfactant. Colloids Surf A Physicochem Eng Asp 273:179–183
Omidkhoda M, Hasanzadeh N, Soleimani F, Shafaee H (2019) Antimicrobial and physical properties of alginate impression material incorporated with silver nanoparticles. Dent Res J (Isfahan) 16:372–376
Ramer MS, Gerhardt DE, McNally K (1993) Accuracy of irreversible hydrocolloid impression material mixed with disinfectant solutions. J Prosthodont 2:156–158. https://doi.org/10.1111/j.1532-849x.1993.tb00400.x
Vanlalveni C, Lallianrawna S, Biswas A, Selvaraj M, Changmai B, Rokhum SL (2021) Green synthesis of silver nanoparticles using plant extracts and their antimicrobial activities: a review of recent literature. RSC Adv 11:2804–2837
Akter S, Lee S-Y, Siddiqi MZ, Balusamy SR, Ashrafudoulla M, Rupa EJ, Huq MA (2022) Eco-friendly synthesis of silver nanoparticles by Terrabacter humi sp nov and their antibacterial application against antibiotic-resistant pathogens. Int J Mol Sci 21:9746. https://doi.org/10.3390/ijms21249746
Yazdanian M, Motallaei MN, Tahmasebi E, Tebyaniyan H, Alam M, Abbasi K, Seifalian A, Ranjbar R, Yazdanian A, Hosseini HM, Moghaddam MM (2022) Chemical characterization and cytotoxic/antibacterial effects of nine Iranian propolis extracts on human fibroblast cells and oral bacteria. Biomed Res Int:6574997. https://doi.org/10.1155/2022/6574997
Ilyas K, Singer L, Akhtar MA, Bourauel CP, Boccaccini AR (2022) Boswellia sacra extract-loaded mesoporous bioactive glass nanoparticles: synthesis and biological effects. Pharmaceutics 14:126. https://doi.org/10.3390/pharmaceutics14010126
Mahizan NA, Yang SK, Moo CL, Song AAL, Chong CM, Chong CW, Abushelaibi A, Lim SE, Lai KS (2019) Terpene derivatives as a potential agent against antimicrobial resistance (AMR) pathogens. Molecules 24:2631. https://doi.org/10.3390/molecules24142631
Lopez-Romero JC, González-Ríos H, Borges A, Simões M (2015) Antibacterial effects and mode of action of selected essential oils components against Escherichia coli and Staphylococcus aureus. Evid Based Complement Alternat Med 2015:795435. https://doi.org/10.1155/2015/795435
Li J, Monje-Galvan V (2023) Effect of glycone diversity on the interaction of triterpenoid saponins and lipid bilayers. ACS Appl Bio Mater. https://doi.org/10.1021/acsabm.2c00928
Adnan SN, Ibrahim N, Yaacob WA (2017) Transcriptome analysis of methicillin-resistant Staphylococcus aureus in response to stigmasterol and lupeol. J Glob Antimicrob Resist 48-54. https://doi.org/10.1016/j.jgar.2016.10.006
Das MC, Sandhu P, Gupta P, Rudrapaul P, De UC, Tribedi P, Akhter Y, Bhattacharjee S (2016) Attenuation of Pseudomonas aeruginosa biofilm formation by Vitexin: a combinatorial study with azithromycin and gentamicin. Sci Rep 6:23347. https://doi.org/10.1038/srep23347
Barras F, Aussel L, Ezraty B (2018) Silver and antibiotic, new facts to an old story. Antibiotics 7:79
Yin IX, Zhang J, Zhao IS, Mei ML, Li Q, Chu CH (2020) The Antibacterial, mechanism of silver nanoparticles and its application in dentistry. Int J Nanomedicine 15:2555–2562. https://doi.org/10.2147/IJN.S246764
Liao C, Li Y, Tjong SC (2019) Bactericidal and cytotoxic properties of silver nanoparticles. Int J Mol Sci 20:449. https://doi.org/10.3390/ijms20020449
Morones-Ramirez JR, Winkler JA, Spina CS, Collins JJ (2013) Silver enhances antibiotic activity against Gram-negative bacteria. Sci Transl Med 5:190ra81. https://doi.org/10.1126/scitranslmed.3006276
Gao SS, Zhao IS, Duffin S, Duangthip D, Lo ECM, Chu CH (2018) Revitalising silver nitrate for caries management. Int J Environ Res Public Health 15:80. https://doi.org/10.3390/ijerph15010080
Vila Domínguez A, Ayerbe Algaba R, Miró Canturri A, Rodríguez Villodres Á, Smani Y (2020) Antibacterial activity of colloidal silver against Gram-negative and Gram-positive bacteria. Antibiotics 9:36. https://doi.org/10.3390/antibiotics9010036
Jung WK, Koo HC, Kim KW, Shin S, Kim SH, Park YH (2008) Antibacterial activity and mechanism of action of the silver ion in Staphylococcus aureus and Escherichia coli. Appl Environ Microbiol 74:2171–2178. https://doi.org/10.1128/AEM.02001-07
Wang H, Wang M, Xu X, Gao P, Xu Z, Zhang Q, Li H, Yan A, Kao RY, Sun H (2021) Multi-target mode of action of silver against Staphylococcus aureus endows it with capability to combat antibiotic resistance. Nat Commun 12:3331. https://doi.org/10.1038/s41467-021-23659-y
Bescos R, Ashworth A, Cutler C, Brookes ZL, Belfield L, Rodiles A et al (2020) Effects of chlorhexidine mouthwash on the oral microbiome. Sci Rep 10:5254
Sari E, Birinci I (2007) Microbiological evaluation of 0.2% chlorhexidine gluconate mouth rinse in orthodontic patients. Angle Orthod 77:881–884
Järvinen H, Tenovuo J, Huovinen P (1993) In vitro susceptibility of Streptococcus mutans to chlorhexidine and six other antimicrobial agents. Antimicrob Agents Chemother 37:1158–1159
Rzycki M, Drabik D, Szostak-Paluch K, Hanus-Lorenz B, Kraszewski S (2021) Unraveling the mechanism of octenidine and chlorhexidine on membranes: does electrostatics matter? Biophys J 120:3392–3408. https://doi.org/10.1016/j.bpj.2021.06.027
McDonnell G, Russell AD (1999) Antiseptics and disinfectants: activity, action and resistance. Clin Microbio Reviews 12(1):147–179
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
L.S designed the concept and methodology, L.S investigated, collected, and analyzed the data; C.B, G.B provided the resources, visualization was done by L.S; S.K, C.S; G.B, and C.B; writing and original draft preparation were done by L.S. All authors have substantially revised the manuscript and done the final editing; all authors have read and agreed to the published version of the manuscript.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
Not applicable as this article does not contain any studies with human participants or human data or animals performed by any of the authors.
Consent for publication
This is not applicable.
Competing interest
All authors declare that there is no conflict of interest in this study.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Singer, L., Karacic, S., Szekat, C. et al. Biological properties of experimental dental alginate modified for self-disinfection using green nanotechnology. Clin Oral Invest 27, 6677–6688 (2023). https://doi.org/10.1007/s00784-023-05277-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00784-023-05277-8