Isothermal sections of the Ni–Mn–Ga ternary phase diagram at 1073 and 1273 K were investigated over a wide range of alloy compositions. The range of the β-Ni2MnGa phase, its equilibria with the γ-(Mn, Ni), α′-Ni3Ga, and γ-Ni3Ga2 phases, and the liquidus and solidus lines were determined experimentally. The aging effect on the shape memory effect (SME) of Ni2MnGa sputtered films was also investigated. The two-way SME of the constraint-aged films was confirmed by the temperature change.
Similar content being viewed by others
References
AN Vasil’ev (2003) Phys Uspekhi 46 559 Occurrence Handle1:CAS:528:DC%2BD3sXoslyhtrw%3D
M Matsumoto T Takagi J Tani T Kanomata N Muramatsu AN Vasil’ev (1999) Mater Sci Eng A 273–275 326
M Ohtsuka K Itagaki (2000) Inter J Appl Electromagn Mech 12 49
M Suzuki M Ohtsuka M Matsumoto Y Murakami D Shindo K Itagaki (2002) Mater Trans 43 861 Occurrence Handle1:CAS:528:DC%2BD38Xlt1ensbc%3D
C Wedel K Itagaki (2001) J Phase Equilibria 22 324 Occurrence Handle10.1361/105497101770338833 Occurrence Handle1:CAS:528:DC%2BD3MXks1Gntrk%3D
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ohtsuka, M., Wedel, C. & Itagaki, K. Phase Relations in the Ni–Mn–Ga Ternary System and Aging Effect on Shape Memory Properties of Ferromagnetic Ni2MnGa Sputtered Films. Monatsh. Chem. 136, 1909–1914 (2005). https://doi.org/10.1007/s00706-005-0382-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00706-005-0382-z