Summary
At a basicity CaO/SiO2 of 4, solidified LD slags consist of the main mineralogical phases wüstite, dicalcium silicate, tricalcium silicate and dicalcium ferrite. During the formation of the solid slag components (establishment of a long-range order during solidification), the above-mentioned main phases will develop mixed crystals rich in sulphur, which will grow to a size of a few micrometers. By means of the microprobe it has been possible to perform microanalytical quantification of the sulphur-rich, μm-sized mixed crystals in the solidified LD slags, and to assign them to mineralogical categories. In the wüstite areas mainly FeS particles will form; in the area of the di- and tricalcium silicates (2CaO.SiO2 and 3CaO.SiO2) CaS particles occur, while in the dicalcium ferrite phase (2CaO.Fe2O3) a segregation of oxysulphides 2CaS.Fe2O3 can be observed
Zusammenfassung
Die erstarrten LD-Schlacken bestehen bei einer Basizitätszahl CaO/SiO2 von 4 aus den mineralogischen Hauptphasen Wüstit, Dicalciumsilicat, Tricalciumsilicat und Dicalciumferrit. Bei der Bildung der festen Schlackenkomponenten (Fernordnungsbildung bei der Erstarrung) scheiden sich aus den genannten Hauptphasen schwefelreiche Mischkristalle von wenigen Mikrometern aus. Mit Hilfe der Mikrosonde konnten die μm-großen schwefelreichen Mischkristalle in den erstarrten LD-Schlacken mikroanalytisch quantifiziert und mineralogisch zugeordnet werden. In den Wüstit-Bereichen bilden sich überwiegend FeS-Teilchen, im Gebiet der Di- und Tricalciumsilicate (2CaO.SiO2 und 3CaO.SiO2) treten CaS-Teilchen auf und aus dem Dicalciumferrit (2CaO.Fe2O3) scheiden sich Oxisulfide 2CaS.Fe2O3 aus.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
Literaturverzeichnis
Trömel, G., K. Koch und J. Geiseler: Arch. Eisenhüttenwes. 40 (1969), No. 2, 87–98
Koch, K., G. Trömel und J. Laspeyres: Arch. Eisenhüttenwes. 48 (1977), No. 3, 133–138
Schürmann, E., und H. Fischer: steel research 58 (1987), No. 12, 531–537
Preßlinger, H., M. Mayr, K. Antlinger und H. Hiebler. Radex-Rundschau (1989), Heft 1, 12–25
Preßlinger, H., K. Antlinger, G. Poferl und E. Maxl: Proceedings 1St Europ. Oxyg. Steelmak. Congr. EOSC'93, Düsseldorf/Neuss ( June 21–23, 1993), 198–204
Preßlinger, H.: Habilitationsschrift Montanuniversität Leoben, 1993
Preßlinger, H., M. Mayr und R. Apfolterer: steel research 70 (1999), No. 6, 209–214
Preßlinger, H., K. Antlinger, K. O. Klepp und H. Hiebler: steel research 68 (1997), No. 12, 520–527
Preßlinger, H., K. Antlinger, G. Poferl, M. Mayr und E. Maxl: Radex-Rundschau (1992), No. 1, 14–30
Preßlinger, H.: BHM 145 (2000), Heft 1, 6–13
Mills, K. C.: ISIJ intern. 33 (1993), No. 1, 148–155
Mills, K. C.: slag atlas, Verlag Stahleisen, Düsseldorf (1995), 1–8
Frohberg, M. G.: Arch. Eisenhüttenwes. 32 (1961), No. 9; 597–606
Steinmetz, E., und F. Oeters: Stahl u. Eisen 97 (1977), No. 8, 373–381
Gammal, T. El: Schlacken in der Metallurgie, Hg: K. Koch, D. Janke, Verlag Stahleisen, Düsseldorf (1984), 5–16
Oeters, F.: Metallurgie der Stahlherstellung, Verlag Stahleisen, Düsseldorf, Springer-Verlag, Berlin-Heidelberg-New York-London-Paris-Tokyo-Hong Kong, 1989
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Preßlinger, H., Fluch, J. Mikroanalytische Untersuchungen über die Einbindung von Schwefel in LD-Schlacken. Berg Huettenmaenn Monatsh 156, 281–286 (2011). https://doi.org/10.1007/s00501-011-0008-1
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s00501-011-0008-1