Abstract
Previously we have reported the existence of small-amplitude charge pulses in crosslinked Polyethylene (XLPE) and epoxy resin with a mobility several orders of magnitude higher than that found for the incoherent charge transport relevant to the steady state current. Here the relationship of this phenomenon to mechanical relaxation in the material is investigated by using a series of epoxy resin nanocomposites based on a resin that has its flexibility increased above that of the fully cured glassy epoxy network by the addition of a suitable flexibilizing chemical. Differential Scanning Calorimetry (DSC) measurements show that the stiffness of the nanocomposite is progressively increased as the nanoparticle concentration increases. Pulsed Electro-Acoustic (PEA) measurements reveal that both positive and negative fast charge pulses exist in the unfilled epoxy at 45 and 70°C under a field of 10 kV/mm with mobility 5×10−10 to 9×10−10 m2 V−1 s−1, amplitude between 2×10−5 and 3.6×10−5 C m−2 and repetition rates between 8 and 12 s−1. These values are reduced progressively as the nanoparticle concentration is increased from 0% in the unfilled epoxy. A β-mode mechanical relaxation is identified in the loss modulus by Dynamical Mechanical Analysis (DMA), whose activation energy moves to higher values with increasing nanoparticle concentration. It is shown that the repetition rates of both positive and negative pulses have similar values and are correlated with the β-mode activation energy; a similar correlation is found for the activation energy of the mobility of positive pulses. The correlation of the activation energy of the mobility of negative pulses and that of the β-mode is weaker although both show a progressive increase with nanoparticle concentration. The modification of the fast charge pulse properties by the mechanical stiffness of the epoxy nanocomposite is discussed in terms of the theory presented previously for their formation and transport.
Similar content being viewed by others
References
D.A. Seanor, Electrical Properties of Polymers (Academic Press, London, 1982)
L.A. Dissado, G.C. Fothergill, Electrical Degradation and Breakdown in Polymers (Peregrinus Press, Stevenage, 1992)
G.C. Montanari, IEEE Trans. Dielectr. Electr. Insul. 11, 56 (2004)
T. Takada, IEEE Trans. Dielectr. Electr. Insul. 6, 519 (1999)
G.C. Montanari, IEEE Trans. Dielectr. Electr. Insul. 7, 309 (2000)
D. Fabiani, G.C. Montanari, L.A. Dissado, C. Laurent, G. Teyssedre, IEEE Trans. Dielectr. Electr. Insul. 16, 241 (2009)
D. Fabiani, G.C. Montanari, L.A. Dissado, J. Phys. Conf. Ser. 183, 012010 (2009)
D. Fabiani, G.C. Montanari, L.A. Dissado, in IEEE Conference on Solid Dielectrics (ICSD) (IEEE, Piscataway, 2010), p. 309
D. Fabiani, G.C. Montanari, E. Siracusano, L.A. Dissado, in IEEE Conference on Electric Insulation and Dielectric Phenomena (CEIDP) (IEEE, Piscataway, 2009), p. 31
J.-K. Yuan, W.-L. Li, S.-H. Yao, Y.-Q. Lin, A. Sylvestre, J. Bai, Appl. Phys. Lett. 98, 032901 (2011)
K. Gupta, P.C. Jana, A.K. Meikap, J. Appl. Phys. 109, 123713 (2011)
V. Tomer, G. Polizos, A. Randall, E. Manias, J. Appl. Phys. 109, 074113 (2011)
L.A. Dissado, G.C. Montanari, D. Fabiani, J. Appl. Phys. 109, 064104 (2011)
H. Koerner, D. Misra, A. Tan, L. Drummy, P. Mirau, R. Vaia, Polymer 47, 3426 (2006)
L. Hardy, I. Stevenson, G. Boiteux, G. Seytre, A. Schönhals, Polymer 42, 5679 (2001)
T.J. Lewis, J.P. Llewellyn, M.J. van der Sluijs, IEE Proc. A, Sci. Meas. Technol. 140, 385 (1993)
P. Chen, D. Wang, Epoxy Resin and Application (Chemical Industry Press, Beijing, 2004)
X. Huang, Y. Zheng, X. Jiang, Y. Yin, IEEE Trans. Dielectr. Electr. Insul. 17, 635 (2010)
D. Fabiani, G.C. Montanari, A. Dardano, G. Guastavino, L. Testa, M. Sangermano, in IEEE Conference on Electrical and Insulating Dielectric Phenomena (CEIDP 2003) (IEEE Press, Piscataway, 2008), p. 710
Z. Ranjbara, S. Rastegar, Prog. Org. Coat. 72, 40 (2011)
F.-L. Jin, S.-J. Park, Mater. Sci. Eng. A, Struct. Mater.: Prop. Microstruct. Process. 478, 406 (2008)
M. Sangermano, F. Deorsola, D. Fabiani, G.C. Montanari, G. Rizza, J. Appl. Polym. Sci. 111, 2541 (2009)
L.H. Sperling, Introduction to Physical Polymer Science, 4th edn. (Wiley, New York, 2006)
R.H. Boyd, Polymer 5, 1123 (1985)
J.P. Crine, IEEE Trans. Electr. Insul. 22, 169 (1987)
Acknowledgements
The authors would like to thank Dr. Krivda for providing the test specimens and Prof. Saccani for helping with DSC and SEM experiments.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Montanari, G.C., Xu, M., Fabiani, D. et al. The effect of mechanical relaxation on ultra-fast charge pulses in flexible epoxy resin nanocomposites. Appl. Phys. A 107, 539–551 (2012). https://doi.org/10.1007/s00339-012-6845-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-012-6845-2