Mechanical, electrical, and thermal properties of irradiated low-density polyethylene by electron beam

  • Original Paper
  • Published:
Polymer Bulletin Aims and scope Submit manuscript

Abstract

The effect of electron-beam (EB) irradiation on the mechanical, electrical, and thermal properties of low-density polyethylene (LDPE) was studied The LDPE was irradiated by using 3 MeV EB machine at doses ranging from 25 to 250 kGy in air at room temperature and analyzed for mechanical, thermal, and electrical properties. It was revealed by differential scanning calorimetry analysis that the crystallinity of the EB-radiated LDPE decreased slightly as verified by a marginal reduction in the densities, enthalpy, and melting points. Thermogravimetric analysis test showed that the thermal degradation of LDPE improved by increasing irradiation. The results obtained from both gel content and hot set tests, indicating whether the applicable LDPE has been properly cross-linked or not, showed that under the EB irradiation conditions employed, the cross-linking of the LDPE samples occur mainly in the amorphous region, and the cross-linking density at each irradiation dose depends almost on the amorphous portions of the LDPE. A significant improvement in the tensile strength of the neat LDPE samples was obtained upon EB up to 250 kGy with a concomitant decline in elongation at break. The results on the electrical properties revealed that the surface resistance, volume resistivity, and dielectric strength of the LDPE increase with irradiation dose and reaches a maximum at a 250 kGy irradiation dose. No considerable change of breakdown voltage, dielectric constant, and dielectric loss factor were observed with increasing irradiation dose. The enhancement in the heat deformation, hardness, and thermal aging properties of LDPE upon EB irradiation, suggests that irradiated LDPE is more thermally and mechanically stable than virgin LDPE.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13

Similar content being viewed by others

References

  1. Youssef HA, Ali ZI, Zahran AH (2001) Electron-beam structure modification of poly (vinyl chloride) wire coating. J Polym Degrad Stab 74:213–218

    Article  CAS  Google Scholar 

  2. Liu H, Fang Z, Peng M, Shen L, Wang Y (2009) The effects of irradiation cross-linking on the thermal degradation and flame-retardant properties of the HDPE/EVA/magnesium hydroxide composites. J Radiat Phys Chem 78:922–926

    Article  CAS  Google Scholar 

  3. Ramazani S, Rahimi A, Frounchi M, Radman S (2008) Investigation of flame retardency and physical–mechanical properties of zinc borate and aluminum hydroxide propylene composites. J Mater Des 29:1051–1056

    Article  Google Scholar 

  4. Gheysari D, Behjat A, Haji-Saeid M (2001) The effect of high-energy electron-beam on mechanical and thermal properties of LDPE and HDPE. J Eur Polym 37:295–302

    Article  CAS  Google Scholar 

  5. Dadbin S, Frounchi M, Haji Saeid M, Gangi F (2002) Molecular structure and physical properties of E-beam crosslinked low-density polyethylene for wire and cable insulation applications. J Appl Polym Sci 86:1959–1969

    Article  CAS  Google Scholar 

  6. Gheysari D, Behjat A (2001) Radiation crosslinking of LDPE and HDPE with 5 and 10 MeV electron-beams. J Eur Polym 37:211–216

    Article  Google Scholar 

  7. Ziaie F, Anvari F, Ghaffari M, Borhani M (2005) Dose rate effect on LDPE cross-linking induced by electron-beam irradiation. J Nukleonika 50(3):125–127

    CAS  Google Scholar 

  8. Hassanpour S, Khoylou F, Jabbarzadeh E (2003) Thermal degradation of electron-beam crosslinked polyethylene and (ethylene–vinylacetate) blends in hot water. J Appl Polym Sci 89:2346–2352

    Article  CAS  Google Scholar 

  9. Dadbin S, Frounchi M, Sabet M (2005) Studies on the properties and structure of electron-beam crosslinked low-density polyethylene/poly [ethylene-co-(vinyl acetate)] blends. J Polym Int 54:686–691

    Article  CAS  Google Scholar 

  10. Akin Sener A, Demirhan E (2008) The investigation of using magnesium hydroxide as a flame retardant in the cable insulation material by cross-linked polyethylene. J Mater Des 29:376–1379

    Google Scholar 

  11. Youssef HA, Magdy MS, Hanan ME (2007) Characterization of LDPE and LDPE/EVA blends crosslinked by electron-beam irradiation and foamed with chemical foaming agent. J Polym Res 14:351–357

    Article  CAS  Google Scholar 

  12. Sharif J, Hanisah SS (2000) Radiation effects on LDPE/EVA blends. J Radiat Phys Chem 58:191–195

    Article  CAS  Google Scholar 

  13. Ratnam CT, Abdullah Z, Ismail H (2006) Electron-beam irradiation of EVA/ENR blend. Polym Plast Technol Eng 45:555–559

    Article  CAS  Google Scholar 

  14. Ghaffari M, Ziaie F (2007) Effect of additives on thermal properties of electron-beam irradiated LDPE foam. J Nukleonika 52(1):35–38

    CAS  Google Scholar 

  15. Dalai S, Wenxiu C (2002) Radiation effects on LDPE/EVA blends. J Appl Polym Sci 86:1296–1302

    Article  CAS  Google Scholar 

  16. Hassan MA (2004) Effect of incorporation of butyl acrylate–iron chelate resin on the flammability properties of Mg(OH)2-LDPE compositions. J Polym Plast Technol Eng 43(5):1487–1501

    Article  CAS  Google Scholar 

  17. Hippi U, Mattila J, Korhonen M, Seppälä J (2003) Compatibilization of polyethylene/aluminum hydroxide (PE/ATH) and polyethylene/magnesium hydroxide (PE/MH) composites with functionalized polyethylenes. Polymer 44:1193–1201

    Article  CAS  Google Scholar 

  18. Borhani M, Mirjalili G, Ziaie F, Bolorizadeh MA (2007) Electrical properties of EVA/LDPE blends irradiated by high energy electron-beam. J Nukleonika 52(2):77–81

    CAS  Google Scholar 

  19. Ziaiea F, Borhanic M, Mirjalilib G, Bolourizadeh MA (2007) Effect of crystallinity on electrical properties of electron-beam irradiated LDPE and HDPE. J Radiat Phys Chem 76:1684–1687

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Faculty of Chemical Engineering, Universiti Teknologi MARA (UiTM), Shah Alam, Selangor, Malaysia

    Maziyar Sabet

  2. Department of Polymer Engineering, Faculty of Chemical and Natural Resources Engineering, Universiti Teknologi Malaysia, Skudai, Johor Bahru, Malaysia

    Azman Hassan

  3. Malaysian Nuclear Agency, Bangi, Kajang, Malaysia

    Chantara Thevy Ratnam

Authors
  1. Maziyar Sabet
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Azman Hassan
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Chantara Thevy Ratnam
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Maziyar Sabet.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Sabet, M., Hassan, A. & Ratnam, C.T. Mechanical, electrical, and thermal properties of irradiated low-density polyethylene by electron beam. Polym. Bull. 68, 2323–2339 (2012). https://doi.org/10.1007/s00289-012-0741-y

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00289-012-0741-y

Keywords

Search

Navigation