Abstract
Polymer based composite materials have a great potential for applications in tribology as dry lubricants since the components comprising the composition may be chosen to fit to various tribological requirements. It is however well known that heat transfer and thermal effects are important for such systems. Systematic experimental studies of temperature effects are time consuming and expensive. In this work, we use a numerical homogenization approach in order to study the principal influence of key composite descriptors of fiber and particle reinforced PEEK on the homogenized heat conductivity. It turns out that the sensitivity of this key parameter on the descriptors can be nicely fitted to a regression model and thus allows for interpolation in the sense of a structure-property-relationship.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Due to increasing costs for energy and growing environmental awareness, energy and material efficiency are of ever-increasing importance in product development. One of the main causes for energy and material loss is friction in tribological contacts. In recent years, polymer-based materials have been used for various tribological applications in increasing quantities [9]. These materials combine the potential for lightweight design, dry running capability and cost-effective processing. Typically, a polymer-based tribological composite, produced by compounding, consists of a high-performance polymer which is reinforced with fibres to increase mechanical strength and wear resistance and modified with an internal solid lubricant to reduce friction [22, 30]. Further improvements of both friction and wear behavior can be achieved by the addition of hard micro- and nano-sized particles which improve the stiffness of the matrix material and interact with the carbon fibres in several ways [5, 6, 17, 29, 30].
The development of these hybrid composites is expensive and time consuming, due to the large number of experiments required to determine the tribological behavior of numerous formulations under different load conditions. Also, the tribological performance of polymer compounds is strongly dependent on the geometry of the tribological system. Consequently, results of early stage standardized tests may differ considerably from the results obtained in more application-oriented test setups. A reduction of the extend of experimental work and an improved transferability of results may be achieved using numerical methods to simulate tribological systems. This requires suitable homogenized models for the material properties, in particular for mechanical and thermal properties. In the literature, many mathematical methods for constructing effective media descriptions are available, generally called homogenization methods. These methods fall into two broad classes: Analytical homogenization methods are based on empirical observations or take advantage of physical understanding and mathematical derivations, usually asymptotic expansions. Numerical homogenization methods apply simulation techniques for the corresponding boundary value problems (e.g. for thermal conductivity or for mechanic deformation) on micro-scale Representative Volume Elements (RVE). Especially for fiber-reinforced materials, a number of research articles deal with homogenization techniques, mainly in the field of homogenization of the mechanical aspects of composites[2,3,4]. For the numeric homogenization of the Effective Thermal Conductivity (ETC) recent works deal with image-based models [10], laminates [19], cell-based models [16] and the FEM [15]. A more comprehensive review of recent work in this field was provided by Zhai et al. [28]. In this work, we propose a homogenization methodology implemented in two different numerical setups.
In the case of fillers with an aspect ratio of around 5 or above, the filler orientation inside the composite also needs to be considered. In this work a numerical homogenization method for the thermal conductivity of composites filled with fibres and particles is demonstrated. The main focus is to identify which aspects of the matrix-filler system are most relevant for the thermal properties.
In Section 2 the model for the orientation of non-spherical fillers in a composite will be discussed, since it requires some significant assumptions. The orientation distribution for any non-spherical filler phase is dominated by the production process and depends on the composition mainly via the viscosity.
In Section 3 and Section 4 the numerical homogenization approach is described and validated. The results are important to qualify the reliability of the studies performed thereafter.
In Section 5 several parameter studies are performed, to gain insight, which geometric and material properties have a large influence on the result. The investigated parameters encompass fundamental aspects, such as the gross composition of the composite or the thermal conductivity of the involved materials, as well as less well-structured properties, e.g. the length and orientation of the fibres in the composite. The gross composition of extruded composites is usually known rather accurately, but the production process may not guarantee a totally homogeneous dispersion of the filler (fibres) and other particles (agglomeration) in a polymer matrix. The thermal conductivity of the matrix material and the composite can generally be measured to a similar precision, but for the filler phases this is more difficult. E.g. for carbon fibres values ranging from 4.9 W/mK [26] to 17 W/mK [8] are reported. The length and orientation of fibres in a composite is generally difficult to assess. Even if the original length is known, the compounding and extrusion process often involves fiber cracking, so that the final length distribution in the composite is not directly available. At the end of Section 5 some minor variations of detail behavior like the size and thermal conductivity of filler particles, and issues with fiber-matrix bonding are investigated.
Section 7 concludes the numerical findings of this work on a structure-property relationship of the homogenized heat conductivity of the composites under investigation basically as a function of key characteristic parameters of the composite geometry. This relationship has been successfully tested against “worse case“ geometries not included in the fitting procedure.
2 Geometrical composite modeling
The orientation of the fibres in the composite is the most complex parameter to describe, because it cannot easily be reduced to a single number. The most direct way to obtain a RVE for homogenization, is to use an actual 3D image of the material. This approach however can only be applied to materials that actually exist (so it is not applicable in design of new materials) and it typically involves high costs (for a CT) and further difficulties if the contrast between the matrix material and the fillers is low (like carbon fibres in a polymer). Alternatively one could use a simulation of the intended production process (CFD simulation of polymer melt[21]) to predict a geometry for the system. Such a simulation would respect the influence of the production process on the geometry, but it requires a lot of material properties, and Hopmann [13] showed, that default values provided by typical CFD software packages often yield unsuitable results. The most feasible approach is to choose a suitable (parametrized) distribution for the directions of the fibres and adjust the parameters to the composite geometry. Distributions with many parameters should be avoided, because they would require a lot of data to actually estimate these parameters for a real (or even just planned) material.
A widely used assumption for injection molded parts made from ber reinforced plastics is the existence of three zones with different ber orientations along the thickness direction of the part. In the outer zones, the bres are predominantly oriented in the direction of molding due to shear of the polymer melt, while in the core they are mainly oriented perpendicular to the direction of molding due to extensional ow [11, 18]. Here, micro geometries are generated in a representative volume element (RVE) for each zone separately. As a basis for the geometry model, the direction distribution proposed by Schladitz [25] for non-woven materials is used. This model depends only on a single parameter. It represents distributions with one preferred direction while assuming symmetry in the two orthogonal directions. To relax the symmetry assumption, a second model, known as Angular Central Gaussian (ACG) [27] was also investigated. The covariance matrix dening the Gaussian distributions is assumed to be diagonal, which ts into the homogenization procedure as described in Section 3 below. In this case, the model depends on two parameters, including the model by Schladitz [25] as a special case. We note that the ACG distribution is an exact solution of the Fokker Planck equation describing the orientation density function dynamics, and represents an exact second order moment closure of the Folgar-Tucker equation, see [1, 12] for a discussion. The placement of already oriented bres and particles in the volume uses a random sequential adsorption process, see [23].
The parameters for both models could be estimated again from CFD-type simulations, see [24], or directly from material samples e.g. from microsection images. However, because only a very small number of parameters is involved, it is much simpler to quantify the influence of these parameters. Therefore the transfer of orientation information obtained for one existing compound to other compounds of moderately different composition is simpler.
For our study six different geometric parameter settings were considered, the parameters are listed in Table 1. In the last three columns the diagonal elements of the second order orientation tensor (FOT) [20] are added to give an idea how the geometries behave.
Using diagonalization and an appropriate coordinate transformation to the eigenbasis of the ACG tensor, we may assume, without loss of generality, that the coordinate axes of all RVEs used in this work represent the eigenvectors.
3 Mathematical homogenization procedure for the heat conductivity
In this work, a homogenized heat conductivity \(\lambda _{i}^{hom}\) in direction i, in a cubical RVE is calculated in the following setup:
For the sake of notation the unit cube (0, l)3 is assumed for the RVE. Inside the cube some parts are filled with fibres, and λ(x) denotes a constant symmetric temperature conductivity tensor with jumps on the interface I between the matrix and the fillers. The symbol \(\vec {n}\) shall denote the unit normal vector on I, always pointing towards one material (i.e. the matrix material), and x+ and x− denote limiting points towards a point x on I approaching x in the direction of \(\vec {n}\) and against the direction of \(\vec {n}\) respectively.
Then, the heat conduction equation and the transition and boundary conditions for the micro scale simulations used in this work for heat transfer in x-direction read:
This set of equations describe a stationary heat conduction with transition conditions between materials respecting the first law of thermodynamics, namely continuity of temperature, energy conservation and periodic boundaries. The equations for the remaining direction are easily obtained by interchanging x, y, z.
From the solution T(x), a homogenized thermal conductivity is calculated as:
All of the equations in Eq. 9 are linear in λ. Therefore a multiplication of λ with a single constant (the same for all directions and both materials) will not change the solution T(x). In Eq. 10 this will also multiply the result with the same value. For these reasons an increase in matrix conductivity by a factor c yields c times more conductivity than dividing the fiber conductivity by c.
In the same manner the equations are invariant when the length scale is changed, but now the term l in Eq. 10 changes as well, so that the homogenized conductivity is unchanged. Therefore the homogenized conductivity does not really depend on the fiber length, but only the aspect ratio.
Both properties are only strictly valid without particles in the composite. However since the sensitivity to the particle size and conductivity are rather low, as will be demonstrated later in this work, the approximation is viable.
4 Homogenization model
The matrix filler system is motivated from a polyetheretherketone (PEEK) polymer filled with HT short carbon fibres (SCF) to about 7% and up to 10% graphite particles.
The corresponding values are given in Table 2 in Section 5.
In all studies in this section use 5 different random geometry realizations based on the orientation model explained in Section 2. For studies on geometric parameters such as RVE size or fiber length separate geometries had to be created, but for parameters that effect the material properties the same geometries were used. The reported results are averages over 5 realizations of the stochastic fibre distribution, in many cases the standard deviations are displayed by error bars as well (Fig. 1).
4.1 Numerical methods
The major part of the numerical studies was performed with the commercial tool GeoDict (Math2Market GmbH, Kaiserslautern, Germany. www.geodict.de). This tool implements the solution of the thermal diffusion equation for box-shaped domains with very complex interior structure (such as hundreds of cylinders and thousands of spheres surrounded by a matrix material). The method behind the tool resolves the geometry on a regular grid, which is called voxelization in the field; this approach requires a decent resolution to capture the fillers. GeoDict is specifically developed for numerical homogenization based on RVE calculations, and directly calculates the effective thermal conductivity from a given material geometry (Fig. 2).
Another commonly used method for simulations of thermal conductivities is the finite element method (FEM). Some simulations were performed with the FEM (implemented in the open source tool calculix, http://www.calculix.de [7]) to test aspects that cannot be handled by GeoDict. The FEM has several disadvantages with respect to calculations of RVEs. At first the generation of the mesh itself is rather time-consuming, and also suffers from instabilities of the algorithms used: At the boundary of the RVE, there are many fibres and some particles that are cut by that boundary. At least for the open source mesh generator NetGen(https://sourceforge.net/projects/netgen-mesher) used in this work, these cut objects posed a major problem, so that the boundary of the RVE had to be modified slightly in order to obtain a suitable mesh for the FE solver.
4.2 Numeric validation
As a first step for numerical homogenization an investigation of the dependence on size and resolution for the RVE was performed. For these two studies the maximum particle fraction (10%) and fiber length (280μm) were used, to guarantee numerical convergence for all the intended parameter studies. The remaining parameters were kept at their default values (see Table 2 in Section 5). In the voxelised representations of the geometries used, the volume fraction of the fibres was respected to up ± 0.01% (except for the box size of 250μm, where it was 0.03%) by the voxelization. The particle volume fraction differed slightly more, up to 0.2%. The studies afterwards all have similar uncertainty bounds.
The RVE for homogenization should likely be larger than the fiber length, therefore geometry samples of 2503, 3503, 5003 and 7003 μm were created and used for homogenization at a constant resolution (voxel size= 1μm). The results are shown in Fig. 3.
The dependence on the RVE size is rather small, this is likely because both the geometry and the homogenization were performed under complete periodic boundary conditions. Based upon these results a RVE size of 3503μm was considered sufficient for further calculations involving fibres.
As a second step the influence of the resolution was tested, for the now fixed RVE size of 3503μm. For this study only the first 2 geometry samples for the box size of 350μm were used. Different voxel sizes can be applied to one and the same geometry, such that there is no random variation involved in this step. The results for voxel sizes of 2, 1, 0.7 and 0.5 μm are shown in Fig. 4. There is a clear trend visible in these results. From these results a voxels size of 0.5μm is not significantly better than 1μm but it increases the numeric effort by a factor of 8.
As a result of these studies all further calculations were performed at a box size of 350μm and a voxel size of 1 μm. A smaller voxel size or an extrapolation based upon multiple voxel sizes could be employed to obtain more accurate results, but we recommend to confirm at first that the all the parameters of the geometry and materials are known at a sufficiently high precision so that higher accuracy in discretizations are worth to be used at all.
As a separate test numerical homogenization based upon the FE method was performed for three out of the five geometries generated for the standard case (i.e. without particles and at fiber length 210μm). These FEM calculations used about 9 million 4-node tetraeder elements (with linear shape functions) built from about 1.5 million nodes. For the remaining two geometries the mesh generation failed, despite the modifications to the boundary. The results differ from those obtained from GeoDict by at most 7%. Due to the aforementioned manipulation of the geometry at the boundary and the different numerical solver techniques employed, differences in this range are to be expected.
5 Parameter study
In this section the influence of different input parameters referring either to the assumed geometry or the assumed input material properties is studied.
5.1 Length of the fibres
At first an analysis with respect to the fiber length was performed for four different fiber lengths of 70, 140, 210, and 280 μm. In all cases the fibre diameter was 7μm so the cases correspond to aspect ratios of 10, 20, 30, and 40. The remaining parameters are as given in Table 2.
The results are transferable to fibres of different diameter with the same aspect ratio, by scaling relations (see Section 3).
The corresponding results are shown in Fig. 5. The sensitivity is much higher for short fibres than for long ones.
5.2 Volume fraction
The most basic parameter describing a composite is the composition, i.e. the fraction of volume occupied by fibre or particles. The results for fiber volume fractions from 5% to 9% and graphite volume fractions from 0% to 10% are shown in Fig. 6. Again the remaining parameters are kept as in Table 2. The results can be described by a linear model
quite well as decicted in Fig. 6.
The R-squared (R2) measure for the fit is above 99% and the maximum deviation between the linear fit and the results is below 1.6%. Additionally the offset values (ai) are very close to the matrix value of 0.23 W/mK and the discrepancies are comparable to the discrepancy between 1- and 2-direction. For this reason the linear fit can be expected to be valid without restrictions for smaller volume fractions of fibres as well. This result could be advantageous for material design even though the fit coefficients have been determined by numeric simulations (Table 3).
5.3 Conductivity of input materials
Another very important parameter is the conductivity of the input materials, especially of the fibre and the matrix material.
In Fig. 7 the conductivity of the composite is shown as a function of the conductivity of the matrix for the base geometry described in Table 2. A variation of the matrix conductivity can be due to different matrix materials, a temperature dependence in the matrix material properties (quite common for typical materials) or additional micro particles that have been homogenized into the matrix in a separate step. There is only a small non-linear effect in the range shown, but for smaller matrix conductivity this can be expected to increase. The coefficients for the linear fits in Fig. 7 are about
From the same data it is also possible to calculate the effect of the fiber material conductivity by a scaling law (see Eq. 10). For short HT carbon fibers, literature reports conductivity values from 4.9 [26] to 17 W/mK [8], therefore 5 - 20 W/mK seems to be a reasonable range of investigation. The results appear in Fig. 8, again a significant effect is seen.
In contrast, the precise value of conductivity for spherical inclusions has only low influence as long as it is significantly larger than the matrix conductivity. This effect is already included in the right part of Fig. 6. A change of thermal conductivity of graphite from 142 W/mK to only 14.2 W/mK lowers the conductivity in 1 and 2 direction only by about 2.5%, whereas a change of volume from 10% to 5% lowers the conductivity in that directions by 12%. For the 3 direction the numbers are lower but of similar ratio.
5.4 Microstructure effects
The thermal conductivity of fibres with higher aspect ratios has a strong influence on the composite properties, but at the same time there exist different values in the literature for supposedly very similar fibres. Given this difficulties in adequately determining the isotropic fiber conductivity, it seems rather unlikely that anisotropic behaviour could be measured reliably. In our numeric studies a reduction of the fibre conductivity in the fibre orthogonal directions by a factor of 10 led to a reduction of composite conductivity by less than 4% (2% in the preferred direction). This calculations were performed by the FEM, because GeoDict cannot deal with anisotropic thermal conductivity. Given the overall accuracy obtained by the FEM for homogenization this effect can be considered insignificant.
Additionally SCF are often coated to improve their contact to the matrix material, but this coating will be missing at the ends if the fibres are cracked during processing. Due to this the fibres may not actually be in contact with the matrix at their ends. This behavior was model by adding strongly isolating semi-spheres (below 1% of matrix conductivity) to the fibre ends. Again the effect on the thermal conductivity of the composite was rather small, below 1.5% in this case.
A further study was performed with the diameter of the graphite particles changed from 9μ m to 18 μ m at constant volume fraction. These effects are not significant as well. The total effect was below 1% (half for preferred fiber direction) and also significantly below the obtained standard deviation (Table 4).
5.5 Orientation sensitivity
The thermal conductivity of composites with strong orientation of fibres displays a significant amount of anisotropy. However, over all cases shown in Fig. 9, the isotropic average of the thermal conductivity differs by at most 4%. This can be helpful in comparison to experimental data, because it allows to separate incorrect orientation from other errors. Due to its complex structure, orientation tends to be known at very moderate accuracy.
6 Regression model
The dependence of the thermal conductivity λhom on (i) the volume fractions (ii) fiber length and (ii) fiber orientation can be described by a single relation:
Here aii is the diagonalized Tucker orientation tensor, derived from the ACG model parameters, in the direction in which the heat transfer is simulated (Fig. 9).
This model actually has even less parameter then Eq. 11, because it handles all directions at once. The fit of the model, see table 5, is demonstrated in Fig. 10. Each individual plot only contains a part of the points such that the variables not on the axis are constant. In total the plots contain each point at least once, and demonstrate that the agreement of the fit is quite good (maximum 4% deviation).
As a validation of the model two further geometries were evaluated, one with a high volume fraction (9%) of fibers of short length (70μm) and the other with a low volume fraction (5%) of long fibers (280μm). Both of these were created at maximum fiber alignment (configuration B1 from Table 1, i.e. β = 0.1) and evaluated for three different volume fractions of graphite (as in Table 2). For these results the dependence on the graphite volume fraction vg is shown in Fig. 11.
For the geometry with fewer but longer fibers a nonlinear dependence is observed, potentially indicating the onset of a percolation effect.
The maximum relative deviation of the regression model Eq. 14 is 14% for the case with many short fibers and 8% for the long fibers. This is significantly more than for the original data used for to build the model (where it was 4%), but since this original data did by design not contain any correlation effects between length and orientation of fibers and the the test cases did deviate from the data in both at once the level of agreement is still acceptable.
7 Conclusion
Complex composite materials and their structure-property-relationships are an important area of research. In this paper, based on established structure modelling techniques, a theoretical sensitivity study of the homogenized heat conduction for double reinforced polymeric composites had been deducted and condensed into such a relationship. It turns out that linear models fit well findings in the composites under investigation. This offers the opportunity to use such structure-property relations in higher scale model approaches, for instance in tribological modeling approaches, in order to describe heat balances.
In this work, we used a ACG type geometrical model of double reinforced composites. Extensions of our approach to more sophisticated distributions with more complicated closure relations in the Folgar-Tucker equations may take advantage of the methods presented. Basically the only ingredient to be modified is an accordingly adapted stochastic fiber geometry generation method reflecting empirical closure relations, see [14]. Thus, the heat conductivity of a structure simulated by CFD-type models, like the ones used in [24], are predictable to a high accuracy using the structure-property relationship developed in this work.
Abbreviations
- \(\lambda _{i}^{hom}\) :
-
Homogenized heat conductivity in direction i
- λ(x):
-
Locally constant heat conductivity tensor at micro scale
- l:
-
Length of a cubical box
- x:
-
3D position vector
- x i :
-
i-component of x
- ∇:
-
Nabla operator
- υ f :
-
Volume fraction of fisbres in composite
- υ g :
-
Volume fraction of graphite particles
References
Advani SG, Tucker CL (1987) The use of tensors to describe and predict fiber orientation in short fiber composites. J Rheology 31(8):751–784. https://doi.org/10.1122/1.549945
Bellieud M, Bouchitté G (1998) Homogenization of elliptic problems in a fiber reinforced structure. Nonlocal effects. Ann Scuola Norm Sup Pisa Cl Sci (4) 26(3):407–436. https://hal.archives-ouvertes.fr/hal-01283228/
Bouchitté G, Bellieud M (2002) Homogenization of a soft elastic material reinforced by fibers. Asymp Anal 32(2):153–183. https://content.iospress.com/articles/asymptotic-analysis/asy531
Briane M, Tchou N (2001) Boundary effects in fibered-reinforced media. Comptes Rendus de l’Académie des Sciences - Series I - Mathematics 333(3):173–177. https://doi.org/10.1016/S0764-4442(01)02016-X. https://www.sciencedirect.com/science/article/pii/S076444420102016X
Chang L, Zhang H, Schlarb A (2006) On the sliding wear of nanoparticle filled polyamide 66 composites. Composites Sci Technol 66(16):3188–3198. https://doi.org/10.1016/J.COMPSCITECH.2005.02.021. https://www.sciencedirect.com/science/article/pii/S0266353805002666
Chang L, Zhang Z, Ye L, Friedrich K (2007) Tribological properties of high temperature resistant polymer composites with fine particles. Tribol Int 40(7):1170–1178. https://doi.org/10.1016/J.TRIBOINT.2006.12.002. https://www.sciencedirect.com/science/article/pii/S0301679X06003665
Dhondt G (2004) The finite element method for Three-Dimensional thermomechanical applications wiley
Ehrenstein GW (2007) Faserverbund-Kunststoffe Carl hanser verlag
Friedrich K, Zhang Z, Schlarb A (2005) Effects of various fillers on the sliding wear of polymer composites. Composites Sci Technol 65(15-16):2329–2343. https://doi.org/10.1016/J.COMPSCITECH.2005.05.028. https://www.sciencedirect.com/science/article/pii/S0266353805002009
He Y, Guo J, Yang H (2019) Image-based numerical prediction for effective thermal conductivity of heterogeneous materials: A quadtree based scaled boundary finite element method. Int J Heat Mass Transfer 128:335–343. https://doi.org/10.1016/j.ijheatmasstransfer.2018.08.099. http://www.sciencedirect.com/science/article/pii/S0017931018319975
Hegler R (1984) Faserorientierung beim Verarbeiten kurzfaserverstärkter Thermoplaste. Kunststoffe 74(5):271–277
Herzog R, Ospald F (2017) Parameter identification for short fiber-reinforced plastics using optimal experimental design. Int J Numer Methods Eng 110:703–725. https://doi.org/10.1002/nme.5371
Hopmann C, Weber M, van Haag J, Schöngart M (2015) A validation of the fibre orientation and fibre length attrition prediction for long fibre-reinforced thermoplastics. In: AIP Conference Proceedings 1664(1), 50008 https://doi.org/10.1063/1.4918412https://aip.scitation.org/doi/abs/10.1063/1.4918412
Jack D, Smith D (2004) Assessing the use of tensor closure methods with orientation distribution reconstruction functions. J Compos Mater 38(21):1851–1871. https://doi.org/10.1177/0021998304048413
Kamel F, Madani S, Kanit T (2016) Prediction of effective thermal conductivity of heterogeneous random multi-phase composites. UPB Sci Bull, Series D 78:91–100
Khan KA, Muliana AH (2009) Effective thermal properties of viscoelastic composites having field-dependent constituent properties. Acta Mechanica 209(1):153. https://doi.org/10.1007/s00707-009-0171-6
Lin L, Schlarb A (2016) Effect of the varied load conditions on the tribological performance and the thermal characteristics of PEEK-based hybrid composites. Tribiol Int 101:218–225. https://doi.org/10.1016/j.triboint.2016.04.025. https://ac.els-cdn.com/S0301679X16300792/1-s2.0-S0301679X16300792-main.pdf?_tid=e405f463-544e-42f7-8409-fb93f95d364a&acdnat=1522931410_ab7ffe7fc4dda61331f80a5ddd44cdb06
Menges G, Geisbüsch P (1982) Die Glasfaserorientierung und ihr Einflußauf die mechanischen Eigenschaften thermoplastischer Spritzgießteile — Eine Abschätzmethode. Colloid Polymer Sci 260(1):73–81. https://doi.org/10.1007/BF01447678. http://link.springer.com/10.1007/BF01447678
Muliana AH, Kim JS (2010) A two-scale homogenization framework for nonlinear effective thermal conductivity of laminated composites. Acta Mechanica 212(3):319–347. https://doi.org/10.1007/s00707-009-0264-2
Nguyen BN, Bapanapalli SK, Holbery JD, Smith MT, Kunc V, Frame BJ, Phelps JH, Charles L., Tucker III (2008) Fiber Length and Orientation in Long-Fiber Injection-Molded Thermoplastics — Part I: Modeling of Microstructure and Elastic Properties. J Compos Mater 42(10):1003–1029. https://doi.org/10.1177/0021998308088606
Niedziela D, Strautins U, Hosdez V et al (2010) 1st conference on multiphysics simulation - advanced methods for industrial engineering 2010. proceedings. cd-rom., vol 10
Pei XQ, Bennewitz R, Schlarb A (2015) Mechanisms of Friction and Wear Reduction by Carbon Fiber Reinforcement of PEEK. Tribology Lett 58(3):42. https://doi.org/10.1007/s11249-015-0520-7. http://link.springer.com/10.1007/s11249-015-0520-7
Redenbach C, Vecchio I (2011) Statistical analysis and stochastic modelling of fibre composites. Compos Sci Technol 71(2):107– 112
Russell T, Heller B, Jack D, Smith D (2018) Prediction of the fiber orientation state and the resulting structural and thermal properties of fiber reinforced additive manufactured composites fabricated using the big area additive manufacturing process. J Compos Sci 2:26
Schladitz K, Peters S, Reinel-Bitzer D, Wiegmann A, Ohser J (2006) Design of acoustic trim based on geometric modeling and flow simulation for non-woven. Comput Mater Sci 38(1):56–66. https://doi.org/10.1016/j.commatsci.2006.01.018. http://www.sciencedirect.com/science/article/pii/S092702560600019X
Schürmann H (2007) Konstruieren mit Faser-Kunststoff-Verbunden Springer-Verlag
Tyler DE (1987) Statistical analysis for the angular central gaussian distribution on the sphere. Biometrika 74(3):579–589. http://www.jstor.org/stable/2336697
Zhai S, Zhang P, Xian Y, Zeng J, Shi B (2018) Effective thermal conductivity of polymer composites: Theoretical models and simulation models. Int J Heat Mass Trans 117:358–374. https://doi.org/10.1016/j.ijheatmasstransfer.2017.09.067. http://www.sciencedirect.com/science/article/pii/S0017931017326790
Zhang G (2010) Structure–Tribological Property Relationship of Nanoparticles and Short Carbon Fibers Reinforced PEEK Hybrid Composites. J Polym Sci Part B: Polym Phys 48:801–811. https://doi.org/10.1002/polb.21951. https://onlinelibrary.wiley.com/doi/pdf/10.1002/polb.21951
Zhang G, Chang L, Schlarb A (2009) The roles of nano-SiO2 particles on the tribological behavior of short carbon fiber reinforced PEEK. Compos Sci Technol 69(7-8):1029–1035. https://doi.org/10.1016/J.COMPSCITECH.2009.01.023. https://www.sciencedirect.com/science/article/pii/S0266353809000207
Acknowledgements
We acknowledge financial support by the Deutsche Forschungsgemeinschaf DFG (Grant KL 1369 2-1 and SCHL 280 25-1).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interests
The authors declare that there are no conflicts of interest.
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Höller, J., Niedermeyer, J., Redenbach, C. et al. The effective thermal conductivity of double-reinforced composites. Heat Mass Transfer 56, 2847–2857 (2020). https://doi.org/10.1007/s00231-020-02897-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00231-020-02897-8