Abstract
In this paper, a rapid optical method for characterizing plasmonic (gold) nanoparticle (AuNP) adhesion is presented. Two different methods were used for AuNP preparation: the well-known Turkevich method resulted in particles with negative surface charge; for preparing AuNPs with positive surface charge, stainless steel was used as reducing agent. The solid surface for adhesion was provided by a column packed with pristine or surface-modified glass beads. The size of the nanoparticles was studied by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS); the surface charge of the components was determined by streaming potential measurements. The characterization of adhesion was performed in a flow system by UV-Vis spectroscopy. During the adhesion experiments, the role of the surface charge, the particle size, and the pH were studied, as well as the adhered amount of gold nanoparticles and the surface coverage values. The latter was estimated by theoretical calculations and defined by the quotient of the measured and the maximal adhered amount of nanoparticles, which could be determined by the cross-sectional area of the NPs and the specific surface area of the glass beads. The results are verified by the polarization reflectometric interference spectroscopy (PRIfS) method: silica nanoparticles with diameters of a few hundred (d~450) nanometers were immobilized on the surface of glass substrate by the Langmuir–Blodgett method, the surface was modified similar to the 3D (continuous flow packed column) system, and gold nanoparticles from different pH solutions were adhered during the measurements. These kinds of modified surfaces allow the investigation of biomolecule adsorption in the same reflectometric setup.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Plasmonic particles are widely investigated due to their optical trapping capabilities. In the last few decades, several fields of application arose, including sensitized solar cells [1], optical circuits [2], and analytical methods, such as surface-enhanced raman spectroscopy and surface plasmon resonance spectroscopy [3, 4]. Visible-light photocatalysis also deserves a mention: the presence of Au or Ag nanoparticles can tune the bandgap energy of semiconductors like anatase TiO2, which is originally excitable by near-UV electromagnetic radiation [5,6,7].
As the popularity of this field grew, many simple and scalable methods have been published discussing the preparation of plasmonic nanostructures, including, for example, bottom-up solvent-phase syntheses [8, 9] and top-down lithographic methods [10], which both offer good control over morphological properties and functionalization. While there are many plasmonic materials to apply including Al, Pt, or Ag, the use of Au dominates these fields [11].
In most of their sensing applications, plasmonic metal nanoparticles require an adhesion layer made of another metal such as Cr or Ti to promote their binding to common substrates like glass [12]. The adhesion can be improved for example by thermal annealing [13] or binding the nanoparticles to the surface covalently [14]. Although the adhesive forces between the plasmonic particles and glass are generally weak, porous glass substrates with high specific surface area were proven to be effective in sensing capability enhancement [15]. If the adhesion takes place at a solid/liquid (S/L) interface, one must consider the effect of surface charges of both the particles and the substrate and the particle-particle interactions. Kállay and his co-workers extensively studied the pH- and functionalization-dependent adhesion strength, kinetics, and stability of colloidal and nanoparticles in continuous-flow packed column systems. Using continuously rinsed packed columns, they provided information on the interaction energy profiles and diffusion characteristics of their model systems, studying the particle attachment and detachment kinetics [16,17,18,19,20]. As the concentration of plasmonic Au nanoparticles is easily traceable and the stability of their dispersions is strongly dependent on their chemical environment (pH, ionic strength, complexing agents, etc.) [21], they could be excellent test subjects in such model systems.
In this paper, we present a methodology to characterize pH-, shape-, and functionalization-dependent adhesion strength of model AuNPs as plasmonic nanoparticles, and theoretically any other plasmonic metal and even metal-oxide nanoparticles in simple continuous flow systems. As the modern enhanced oil recovery processes (EOR) utilize metal-oxide nanoparticles beside surfactants and polymers to further increase the oil recovery rate [22, 23], the presented methodology could potentially be helpful during the optimization of novel EOR processes. Furthermore, in this work also the polarization reflectometric interference spectroscopy (polarization RIfS, PRIfS) method [24] is used to verify the results. The concept of the PRIfS technique is similar to the well-known label-free optical analytical methods, such as RIfS [25,26,27,28,29,30,31,32,33,34,35,36] and surface plasmon resonance (SPR) [37,38,39,40]. To the best of our knowledge, this is the first report of applying PRIfS technique for the characterization of nanoparticle adhesion in an aqueous flow system.
Experimental
Materials
Preparation of gold nanoparticles
Negatively surface charged gold nanoparticles [AuNP(−)] with an average diameter of 14 nm were synthesized by the well-known Turkevich method [41]. Positively surface charged AuNP(+) with an average diameter of 51 nm were synthesized by the method presented in [42]. The pH of the AuNP(−) gold sol (pH = 5) was adjusted by adding c = 0.1 M HCl (for pH = 3) or c = 0.1 M NaOH (for pH = 7 and 9) solutions to the original sol.
Preparation of the SiO2 particles
Monodisperse dav = 450-nm silica particles were prepared by the modified method of Jezequel et al. according to [43].
Surface functionalization of the glass beads
Glass beads (< 106 μm and 212–300 μm, average diameters ~ 50 and ~ 250 μm, respectively, acid-washed, Sigma–Aldrich; density 2.52 g/cm3) were used as a solid surface for gold nanoparticle adhesion experiments. Cationic polyethylenimine (PEI, branched, MW~8000, Aldrich) was used as a positively charged polyelectrolyte for functionalization (and charge alteration) of the glass beads.
Instrumental methods
Transmission electron microscopy
TEM measurements were carried out by a FEI TECNAI G2 20 X-Twin high-resolution transmission electron microscope (equipped with electron diffraction apparatus) operating at an accelerating voltage of 200 kV.
Small-angle X-ray scattering
The small-angle X-ray scattering (SAXS) curve was recorded with a slit-collimated Kratky compact small-angle system (KCEC/3 Anton-Paar KG, Graz, Austria) equipped with a position-sensitive detector (PSD 50 M from M. Braun AG Munich, Germany) containing 1024 channels 55 μm in width. CuKα radiation (λCuKα = 0.1542 nm) was generated by a Philips PW1830 X-ray generator operating at 40 kV and 30 mA.
Computed tomography
Micro-CT measurements were carried out with a Bruker SkyScan 2211 nanoTomograph instrument (source voltage, U = 110 kV; source current, I = 150 μA; pixel resolution 1.6 μm). A capillary (Markröhrchen, Hilgenberg) 2 mm in diameter was filled with the dav = 250 μm glass beads. After the reconstruction procedure (NRecon software, Bruker), CTVox and CTAn (Bruker) softwares were used to generate the 3D-rendered image and calculate the size distribution and porosity (ε).
Streaming potential
The streaming potential values of the stationary phase (glass beads), the AuNP(−)s and AuNP(+)s were measured applying a PCD-04 Particle Charge Detector (Mütek Analytic GmbH, Germany). The negative surface charge excess of the glass beads and the AuNP(−)s were neutralized by 0.01 g/100 cm3 (0.01%) polyethylene imine (PEI) and 0.01% hexadecylpyridinium chloride (HDPCl) solutions, respectively, while the positive surface charge excess of AuNP(+)s was neutralized by 0.01% sodium dodecylsulfate (NaDS) surfactant solution during particle charge titrations. The charge compensation states were achieved at streaming potentials of 0 mV. The surface charge excess values were calculated according to the following equation:
where q1 and q2 are the specific charge excess of the examined specimen and the titrant, respectively (meq/g) V2 and c2 are the volume (cm3) and the concentration (g/100 cm3) of the charge-neutralizing agent solution, V1 and c1 are the volume (cm3) and the concentration (mol/dm3) of the examined dispersion, while M1 is the molar mass (g/mol) of the examined specimen. The reversal of surface charge excess is also available by adding an excess amount of titrant to the initial dispersion.
Spectrophotometry
The visible range extinction spectra of the gold sols were recorded by an ADC1000-USB diode array spectrophotometer (Ocean Optics, Duiven, Netherlands). The data points of the extinction vs. concentration calibration curves are the average of five repeated measurements, the uncertainty of the measured extinction values is ± 0.025.
Adhesion measurement
Figure 1 shows the principle (a) and the schematic view of the adhesion measurement setup (b). The flow of the gold sol (c = 20 mg/L) is driven by a peristaltic pump (Ismatech Reglo Digital) with a flow rate of I = 500 μL/min through a stationary phase (L = 60 mm long and d = 8 mm in diameter glass tube filled with glass beads, V = 3.016 mL), while the extinction of the gold sol is measured both before (flow-in) and after (flow-out) the column with V = 400 μL flow-through cells. The difference between the flow-in and flow-out concentrations is due to the adhesion. In dilute systems the extinction of the sol is proportional to the concentration of the plasmonic particles; therefore, the former can be converted to the latter by calibration (see Electronic Supplementary Material (ESM) Fig. S1). It has to be noted that the uncertainty of ± 0.025 in the extinction value causes uncertainties of 1.47 and 3.26 mg/L in the concentration of AuNP(−) and AuNP(+) sols, respectively, during the adhesion measurements, which are indicated by the X- and Y-error bars on Fig. S1 (see ESM). During the measurement the extinction values corresponding to the characteristic plasmonic peaks are monitored in real time, the signal/noise ratio is improved by polynomial fitting, as described in [31]. The point-by-point substraction of the flow-out curve from the flow-in curve results in the difference curve (see Fig. 1). The (extinction-) difference (E) curve can be converted to mass flow (MF) by eq. (2):
where MF is the mass flow, c is the concentration and E is the extinction in a given t moment, k(c) is the slope of the c vs. E calibration curve (see ESM Fig. S1) and I is the constant flow rate (0.5 mL/min). This curve can be divided into three characteristic ranges: (1) in the first range (I. on Fig. 1) the mass flow through the flow-out cell is zero, i.e., all of the gold nanoparticles are adhered to the GB surface, the extent and rate of the adhesion process is maximal; (2) in the second regime (II. on Fig. 1) the adhesion rate decreases, more and more gold nanoparticles are passing through the stationary phase; (3) the third region (III. on Fig. 1) is the saturation range, the adhered amount of AuNPs reached the maximal adhesion capacity of the GBs, all of the particles pass through the column. The adhered amount of gold nanoparticles (mNPexp) can be obtained by the numerical integration of this mass flow curve. It has to be noted that there are two sources of inaccuracy in the flow system: on one hand, there is a path, therefore a time difference between the two flow-through cells, which was t = 170 ± 5 s depending on the space filling of the column (1-ε). The flow-out curves were corrected by this delay. On the other hand, the saturation of the concentration profile in the flow-through cells is not an instantaneous process; it takes t = 50 s, which causes ca. mNPexp = 10 μg AuNP/g GB deviation. This inaccuracy is indicated in the tables.
Thin film preparation
Langmuir films at the air/liquid interface and LB films on glass substrates (for the reflectometric interference spectroscopy measurements) were prepared in a Kibron MicroTroughS Langmuir-trough. Spreading sols were obtained by mixing the original sol with chloroform (Sigma–Aldrich, Chromasolv®, ≥ 99.9%) in the volume ratio 1:1. Glass substrates for LB films were cleaned in piranha solution and rinsed with deionized water before film preparation. The monolayer films were pulled out at constant pressure (π = 10 mN/m), only in the upstroke direction. The surface of the thin films was modified (with PEI) similarly to the 3D system.
PRIfS
Polarization reflectometric interference spectroscopy measurements were carried out according to the phenomenon and optical setup described in [24]. RIfS and PRIfS methods are hardly different, the only difference lies in the measurement techniques. While in the former case the detector measures the average of all the polarization states, the ratio of the s- and p-polarized reflected intensity is measured by using a polarizer in the latter. Therefore, the sensor response (R) is defined by the ratio of the p- and s-polarized components of the reflected light, as described in eq. (3):
Results and discussion
Characterization of the gold nanoparticles
Figure 2a shows the representative UV-Vis extinction spectra of the synthesized gold nanoparticles/sols. There is a characteristic plasmonic band at λ = 490–550 nm (with a maximum at λ = 520 nm) in the case of the monodisperse AuNP(−) sol with narrow size distribution. The plasmonic band appears at λ = 505–565 nm (with a maximum at λ = 532 nm) for the AuNP(+) sol, which corresponds to the formation of larger particles compared with the AuNP(−) sol. During the adhesion measurements in the flow system the extinction values corresponding to these wavelengths (λ = 520 and 532 nm for AuNP− and AuNP+, respectively) are monitored, because the calibration curves (i.e., extinction vs concentration, see Fig. 2b) were measured and plotted on these same wavelength values.
The size of the AuNP(−) and AuNP(+) plasmonic gold nanoparticles were determined by TEM measurements (ESM Fig. S2A-D), moreover, in the case of the AuNP(−) sample, due to its monodispersity, the results could have been confirmed by SAXS measurements (ESM Fig. S2.E). On the TEM image and size distribution diagram the nearly monodisperse character of the AuNP(−) sample with an average diameter of d = 14 ± 1 nm can be observed, however, the positively charged gold particles have a broad size distribution between 30 and 80 nm with an average of ~ 51 ± 13 nm. Furthermore, the Guinier plot [44] of the AuNP(−) sample’s SAXS curve shows the monodispersity with a diameter of d = 14.7 nm; the slight difference can be explained by the citrate as a stabilizing agent.
Characterization of the glass beads
Determining the size distribution of the used glass beads contributes to the accurate estimation of the specific surface area, the surface coverage (Θ) of the AuNPs and space filling of the stationary phase. Size distributions of the smaller (~ 50 μm) and larger (~ 250 μm) glass beads were determined by optical microscopy (ESM Fig. S3.a). The average diameter of the smaller fraction is 55.7 ± 9.2 μm and it is 273.7 ± 37.6 μm for the larger glass beads (ESM Fig. S3.b). Therefore, for practical reasons the notations of the used glass beads will be GB56 and GB274, respectively. Similarly, the notations of the surface-modified samples are GB56(+) and GB274(+), respectively. The size distribution of the GB274 glass beads was verified by micro-CT measurements: ESM Fig. S3c shows the 3D-rendered volume of the capillary filled by GB274 spheres, while ESM Fig. S3d represents the selected volume of interest (VOI) for further calculations (red: GB274, blue: void). Based on μCT measurements the size distribution of the larger fraction was determined (which hardly differs from the optical microscopy results), as well as, the average porosity of the stationary phase was calculated (ε = 36.8%, ESM Fig. S3e). This data is consistent with the values presented later, namely the porosity of the different stationary phases determined by mass measurement.
Streaming potential measurements
The specific surface charge excess value of the AuNP(−) particles was calculated according to charge compensation method described in Chapt. 2.2. The charge compensation required 295 μL of 0.01% HDPCl solution, which according to our equation gives a specific surface charge excess value of −4.18 × 10−2 meq/g, while the value of the independently determined ζ-potential is −43.2 mV. In the case of AuNP(+) particles, 0.01% NaDS solution was used during the surface charge measurements: the volume of the solution required for charge neutralization turned out to be 9.5 mL, indicating a specific surface charge value of 1.64 eq/g, while the ζ-potential was 47.6 mV.
The surface charge excess of the GB56 glass beads, used as adhesion surfaces was also reversed applying excess amount of PEI (0.01 wt. PEI solution). In this case, the consumed 350 μL of 0.01% HDPCl solution during charge compensation measurements indicated the specific surface charge value of −1.96 × 10−5 meq/g. However, this charge neutralization method cannot be applied on GB274 glass beads because of the fast sedimentation of the beads.Therefore, we assumed lower specific surface charge excess values (for geometric reasons, assuming that the same amount (mass) of the larger GBs has a smaller total surface area), keeping the same amount of used PEI as in the case of the smaller GB56 glass beads during the surface charge reversal process.
Theoretical calculations
Theoretical calculations were performed to estimate the specific surface area (Asφ, m2/g) of the glass beads and the cross-sectional surface area (asNP, m2/g) of the gold nanoparticles. The ratio of these two values is in correlation with the maximal (monoparticular) surface coverage (Θ) of the AuNP/GB system. The specific surface area of a spherical particle depending on the particle diameter can be determined by eq. (4):
where A is the surface area and V is the volume of a particle, 2r = d is the particle diameter [nm], ρ is the particle density (g/cm3, ρSiO2 = 2.32 g/cm3) and φ = 0.9069 (reducing the area with the glass beads’ contact points in 3D), assuming hexagonal and monoparticular adhesion of spherical particles (see ESM Fig. S5a and b). Similarly, the cross-sectional surface area of a particle with a diameter of d [nm] and density of ρ (g/cm3, ρAu = 19.3 g/cm3) can be determined by eq. (5) (ESM Fig. S5c):
where Ap is the projection area of a sphere. The (theoretically calculated) maximal monoparticular (Θ = 1) adhered amount of nanoparticles can be determined by the ratio of these two values, as described by eq. (6). The results are presented in Table 1.
Adhesion in equilibrium
The adhesion of the gold nanoparticles on the surface of GB274(+) glass beads was investigated in equilibrium conditions (in a non-flow system), as described in [45], at different pH values.
Before measurement the GB274(+) samples were placed into an oven at 373 K for 4 h. Measured amounts (m = 0.5 ± 0.009 mg) of heat-treated GB274(+) sample was placed into vessels followed by introduction of the pre-prepared AuNP(−) gold sols (V = 10 mL) with known concentrations (N = 5, c0 = 20, 40, 50, 60 and 80 mg/L; three series were investigated at different pH values: pH = 3, 5 and 7). The vessel was closed and equilibrated for 5 h with slight magnetic stirring, while the equilibrium pH value was checked and corrected to the initial value in every hour. The change in the concentration of the gold sol due to adsorption was determined by UV-Vis photometry, measuring the extinction values of the supernatant (ce). The amount corresponding to the decrease in concentration (c0-ce) is equal to the specific adhered mass of AuNP(−)s (mNPexp, mg/g).
The surface coverage can be calculated as the ratio of this value and the theoretically calculated maximally adhered amount: Θ = mNPexp/ mNPmp,th. Table 2 shows the systematic increase of the adhered amount (and the surface coverage) due to the pH decrease, which result was verified by the flow system measurements.
Adhesion in a flow system
Charge dependency
Figure 3 shows the results of the surface charge dependency experiments in the case of AuNP/GB56: −/+, ±, −/− and +/+ pairs. As expected, both the time and the extent of the adhesion are negligible in the case of the uniformly charged units: the adhered mass of AuNPs is in the few μg/g range, while the adhesion time is less than 15 min. Slightly stronger interaction was observed for the AuNP(+)/GB56(−) pair, and a significant adhesion interaction was found between the AuNP(−)s and GB56(+)s. The results are summarized in Table 3. Having regard to the extremely high adhered amount of AuNP(−) particles due to the strong attraction between the negatively charged AuNPs and the PEI modified, therefore positively charged GBs even at pH = 7 value, and assuming that decreasing the pH will cause a significant increase in the adhered amount of gold nanoparticles, the pH dependency experiments were carried out by using the GB274(+) glass beads, because they have lower surface energy and specific surface charge.
pH dependency
For the investigation of the pH dependency of the adhesion process gold sols of 20 mg/ml concentration were used, at different pH levels (pH = 3, 5, 7, and 9) on the larger (GB274) glass beads. A rapid increase in the adhesion time was observed with the decreasing pH, while with increasing the pH the amount of adhered gold greatly decreased, which can be explained by the pendant -NH2 groups of the PEI, which covers the surface of the glass beads becoming increasingly protonated with the decreasing pH, while the –COOH and –COO− groups of the citrates that covers the gold nanoparticles are neutrally or slightly negatively charged (pKA = 2) [21], thus allowing the formation of a strong interaction. Obviously, the increasing pH causes a deprotonation on the –NH2 groups of the PEI, the net positive charges are compensated by the negative surface charges of the glass beads, thus the adhesion interaction weakens. There is also a visually detectable color change of the adhered gold at different pH levels (Fig. 4): at pH = 9 the color barely changes, at pH = 7 and 5 the specific wine red color of the citric gold nanoparticles could be observed, with a deeper color at the lower pH, which indicated the larger amount of adhered gold, while at pH = 3 the color became dark purple, which can be an evidence of the strong aggregation of the particles on the surface of the glass beads (the degree of gold nanoparticle aggregation both in the sol and on the surface can be checked by the color, i.e. by the shape of the extinction spectra. During the measurements no change was observed, neither in the flow-in nor in the flow-out branch, indicating an unchanged aggregation state and nanoparticle size, except in the case of pH = 3, but only for the adhered NPs, not in the sol). The state of the column shows that this process did not saturated even after more than 300 min. The results are summarized and compared with the data obtained from the experiments carried out in the equilibrium conditions in Table 4. The result of the static and dynamic investigations are in a good agreement, the slight differences in the surface coverage values can be explained by the inaccuracy of the measurement.
Reflectometric interference spectroscopy measurements
The experiments in the aqueous flow system (bulk, 3D) were verified by polarization reflectometric interference spectroscopy (PRIfS) measurements, with the difference that the surface for the adhesion was not GB, but a thin film formed by d = 450 nm SiO2 particles. After the preparation of the thin film the surface was modified by PEI by dip-coating technique [31]. Given the fact that this method is based on thin film technique, both the flow rate and the concentration of the AuNP(−) sol were reduced compared with the previously presented flow-system. The flow rate in these experiments was I = 50 μL/min and the concentration of the gold sol was 2 mg/L. Figure 5 shows the results: similarly to the results presented in Ch. “pH dependency”, significantly increasing adhered amounts of AuNP(−)s and adhesion process times were observed with the decrease in pH, as expected. The explanation is the same: the decreasing pH causes a protonation on the –NH2 groups of the PEI; thus, the adhesion interaction between the protonated –NH3+ groups and the AuNP(−)s intensifies.
Conclusions
In this work a model experiment of adhesion of gold nanoparticles on glass bead solid surfaces was presented, addressing the effect of the charge state of the components (±, −/+, −/−, +/+), the glass bead size (d = 56 and 274 μm) and the pH (= 3, 5, 7, and 9) on the adhesion process in both (static) equilibrium and (dynamic) flow systems. The dynamic measurements were carried out in a liquid-flow platform, which consists of a column containing glass beads as a solid phase, with a concentration detection on both ends, which allows the investigation of the adhered amount of gold nanoparticles and the strength of the adhesion. The size of the glass beads seemed to have a significant effect on the amount of adhered gold: with the increasing size, the adhered amount decreased, due to the smaller surface energy and charge density of the larger glass beads. The investigation of the effect of charge served the expected results: the interaction between the equally charged component was negligible, while the interaction of the opposing charges was significantly stronger, especially in case of the AuNP(−) and the PEI-modified glass beads, due to the protonatable groups of the polymer. A similar effect was observed in the case of the pH dependency investigation, where the decrease of the pH resulted in a rapid increase of the protonation of the polyelectrolyte, as well as the adhered amount of gold and the level of aggregation. The result of the static and dynamic investigations were in good agreement, despite the non-equilibrial nature of the dynamic system; therefore, the adhesion of these components seems to be irreversible. The slight differences in the surface coverage values can be explained by the inaccuracy of the measurement. During the static measurements, a precipitation reaction occurred in the case of the gold sol produced by a metal-matrix reduction reaction, which prohibited the measurement of adhesion; however, in the case of the gold sol reduced and stabilized by citrate and the PEI-modified glass beads, the adhesion was easily observable and the outcome showed good agreement with the results of the dynamic measurements. In this case, the precipitant formation was restrained by the brief interaction of the nanoparticles and the glass beads, which prevented the occurrence of the surface reaction. The results of the 3D measurements were verified by using reflectometric interference technique: both the adhered amount of AuNP(−)s and the adhesion process time were significantly increased with the decrease in pH of the gold sol, because the decreasing pH causes a protonation on the –NH2 groups of the PEI, thus the adhesion interaction between the –NH3+ groups and the AuNP(−)s intensifies.
References
Mokari G, Heidarzadeh H. Efficiency enhancement of an ultra-thin silicon solar cell using plasmonic coupled core-shell nanoparticles. Plasmonics, Published online. 2019. https://doi.org/10.1007/s11468-018-0891-3.
Dragoman D, Vladescu E. Ring-shaped plasmonic logic gates. Plasmonics. 2019;14:71–8. https://doi.org/10.1007/s11468-018-0779-2.
Agarwal NR, Tommasini M, Ciusani E, Lucotti A, Trusso S, Ossi PM. Protein-metal interactions probed by SERS: lysozyme on nanostructured gold surface. Plasmonics. 2018;13:2117–24. https://doi.org/10.1007/s11468-018-0728-0.
Hottin J, Wijaya E, Hay L, Maricot S, Bouazaoui M, Vilcot JP. Comparison of gold and silver/gold bimetallic surface for highly sensitive near-infrared SPR sensor at 1550 nm. Plasmonics. 2012;8:619–24. https://doi.org/10.1007/s11468-012-9446-1.
Abed J, Alexander F, Taha I, Rajput N, Aubry C, Jouiad M. Investigation of broadband surface plasmon resonance of dewetted Au structures on TiO2 by aperture-probe SNOM and FDTD simulations. Plasmonics. 2018;14:205–18. https://doi.org/10.1007/s11468-018-0794-3.
Merai L, Deak A, Sebok D, Csapo E, Kolumban TS, Hopp B, et al. Photoreactive composite coating with composition dependent wetting properties. Express Polym Lett. 2018;12:1061–71. https://doi.org/10.3144/expresspolymlett.2018.93.
Farbod M, Khademalrasool M, Talebzadeh MD. Plasmon-enhanced photocatalysis based on Ag plasmonic nanospheres and ZnO nanoparticles: synthesis and study mechanisms governing the plasmonic photocatalytic performance. Plasmonics. 2016;12:759–69. https://doi.org/10.1007/s11468-016-0323-1.
Veres Á, Rica T, Janovák L, Dömök M, Buzás N, Zöllmer V, et al. Silver and gold modified plasmonic TiO2 hybrid films for photocatalytic decomposition of ethanol under visible light. Catal Today. 2012;181:156–62. https://doi.org/10.1016/j.cattod.2011.05.028.
Lu X, Rycenga M, Skrabalak SE, Wiley B, Xia Y. Chemical synthesis of novel plasmonic nanoparticles. Annu Rev Phys Chem. 2009;60:167–92. https://doi.org/10.1146/annurev.physchem.040808.
Choi B, Iwanaga M, Miyazaki HT, Sakoda K, Sugimoto Y. Emission-enhanced plasmonic substrates fabricated by nano-imprint lithography. Proc Spie. 2014. https://doi.org/10.1117/12.2037190.
Wu N. Plasmonic metal-semiconductor photocatalysts and photoelectrochemical cells: a review. Nanoscale. 2018;10:2679–96. https://doi.org/10.1039/c7nr08487k.
Roxworthy BJ, Toussaint KC. Plasmonic nanotweezers: strong influence of adhesion layer and nanostructure orientation on trapping performance. Opt Express. 2012;20:9591–603. https://doi.org/10.1364/oe.20.009591.
Karakouz T, Maoz BM, Lando G, Vaskevich A, Rubinstein I. Stabilization of gold nanoparticle films on glass by thermal annealing. ACS Appl Mater Interfaces. 2011;3:978–87. https://doi.org/10.1021/am100878r.
Lamy de la Chapelle M, Shen H, Guillot N, Frémaux B, Guelorget B, Toury T. New gold nanoparticles adhesion process opening the way of improved and highly sensitive plasmonics technologies. Plasmonics. 2012;8:411–5. https://doi.org/10.1007/s11468-012-9405-x.
Pshenova AS, Sidorov AI, Antropova TV, Nashchekin AV. Luminescence enhancement and SERS by self-assembled plasmonic silver nanostructures in nanoporous glasses. Plasmonics. 2018;14:125–31. https://doi.org/10.1007/s11468-018-0784-5.
Haque MF, Kallay N, Privman V, Matijevic E. Magnetic effects in particle adhesion: I. Kinetics of hematite deposition on stainless steel. J Colloid Interface Sci. 1990;137:36–47. https://doi.org/10.1016/0021-9797(90)90041-L.
Kallay N, Biskup B, Tomic M, Matijevic E (1986) Particle adhesion and removal in model systems: X. The effect of electrolytes on particle detachment. J Colloid Interface Sci 114:357–362. doi: https://doi.org/10.1016/0021-9797(86)90421-2
Kallay N, Torbic Z, Golic M, Matijevic E. Determination of the isoelectric points of several metals by an adhesion method. J Phys Chem. 1991;95:7028–32.
Ryde N, Kallay N, Matijevic E. Particle adhesion in model systems: part 14. – experimental evaluation of multilayer deposition. J Chem Soc Faraday Trans. 1991;87:1377–81.
Kallay N, Tomić M, Biškup B, Kunjašić I, Matijević E. Particle adhesion and removal in model systems: XI. Kinetics of attachment and detachment for hematite - glass systems. Colloid Surf. 1987;28:185–97. https://doi.org/10.1163/156856190X00234.
Csapó E, Sebők D, Makrai Babic J, Supljika F, Bohus G, Dékány I, et al. Surface and structural properties of gold nanoparticles and their biofunctionalized derivatives in aqueous electrolytes solution. J Dispers Sci Technol. 2014;35:815–25. https://doi.org/10.1080/01932691.2013.817314.
Zaid HM, Latiff NRA, Yahya N, Soleimani H, Shafie A. Application of electromagnetic waves and dielectric nanoparticles in enhanced oil recovery. J Nano Res. 2014;26:135–42. https://doi.org/10.4028/www.scientific.net/JNanoR.26.135.
Ragab AMS. Investigating the potential of nanomaterial for enhanced oil recovery: state of art. J Sci Technol. 2015;6:25–40.
Janovák L, Dékány I, Sebők D. The theoretical concept of polarization reflectometric interference spectroscopy (PRIFS): an optical method to monitor molecule adsorption and nanoparticle adhesion on the surface of thin films. Photonics. 2019;6:76. https://doi.org/10.3390/photonics6030076.
Gauglitz G, Krause-Bonte J, Schlemmer H, Matthes A. Spectral interference refractometry by diode array spectrometry. Anal Chem. 1988;60:2609–12. https://doi.org/10.1021/ac00174a015.
Gauglitz G, Brecht A, Kraus G, Mahm W. Chemical and biochemical sensors based on interferometry at thin (multi-) layers. Sensors Actuators B Chem. 1993;11:21–7. https://doi.org/10.1016/0925-4005(93)85234-2.
Reichl D, Krage R, Krummel C, Gauglitz G. Sensing of volatile organic compounds using a simplified Reflectometric interference spectroscopy setup. Appl Spectrosc. 2000;54:583–6.
Hänel C, Gauglitz G. Comparison of reflectometric interference spectroscopy with other instruments for label-free optical detection. Anal Bioanal Chem. 2002;372:91–100.
Zimmermann R, Osaki T, Gauglitz G, Werner C. Combined microslit electrokinetic measurements and reflectometric interference spectroscopy to study protein adsorption processes. Biointerphases. 2007;2:159–64.
Rau S, Gauglitz G. Reflectometric interference spectroscopy (RIfS) as a new tool to measure in the complex matrix milk at low analyte concentration. Anal Bioanal Chem. 2012;402:529–36. https://doi.org/10.1007/s00216-011-5470-9.
Sebők D, Dékány I. ZnO2 nanohybrid thin film sensor for the detection of ethanol vapour at room temperature using reflectometric interference spectroscopy. Sensors Actuators B Chem. 2015;206:435–42. https://doi.org/10.1016/j.snb.2014.09.087.
Sebők D, Janovák L, Kovács D, Sápi A, Dobó D, Kukovecz Á, et al. Room temperature ethanol sensor with sub-ppm detection limit: improving the optical response by using mesoporous silica foam. Sensors Actuators B Chem. 2016;243:1205–13. https://doi.org/10.1016/j.snb.2016.12.097.
Kumeria T, Parkinson L, Losic D. A nanoporous interferometric micro-sensor for biomedical detection of volatile sulphur compounds. Nanoscale Res Lett. 2011;6:634. https://doi.org/10.1186/1556-276X-6-634.
Kumeria T, Kurkuri MD, Diener KR, Parkinson L, Losic D. Label-free reflectometric interference microchip biosensor based on nanoporous alumina for detection of circulating tumour cells. Biosens Bioelectron. 2012;35:167–73. https://doi.org/10.1016/j.bios.2012.02.038.
Choi HW, Takahashi H, Ooyaa T, Takeuchi T. Label-free detection of glycoproteins using reflectometric interference spectroscopy-based sensing system with upright episcopic illumination. Anal Methods. 2011;3:1366–70. https://doi.org/10.1039/C0AY00762E.
Choi HW, Sakata Y, Kurihara Y, Ooya T, Takeuchi T. Label-free detection of C-reactive protein using reflectometric interference spectroscopy-based sensing system. Anal Chim Acta. 2012;728:64–8. https://doi.org/10.1016/j.aca.2012.03.030.
Homola J, Yee S, Gauglitz G. Surface plasmon resonance sensors: review. Sensors Actuators B Chem. 1999;54:3–15. https://doi.org/10.1016/S0925-4005(98)00321-9.
Homola J. Surface plasmon resonance sensors for detection of chemical and biological species. Chem Rev. 2008;1082:462–93. https://doi.org/10.1021/cr068107d.
Vaisocherová H, Šípová H, Víšová I, Bocková M, Špringer T, Ermini ML, et al. Rapid and sensitive detection of multiple microRNAs in cell lysate by low-fouling surface plasmon resonance biosensor. Biosens Bioelectron. 2015;70:226–31. https://doi.org/10.1016/j.bios.2015.03.038.
Špacková B, Wrobel BM, Homola J. Optical biosensors based on plasmonic nanostructures: a review. Proc IEEE. 2016;104:2380–408. https://doi.org/10.1109/JPROC.2016.2624340.
Turkevich J, Stevenson PC, Hiller J. A study of the nucleation and growth process in the synthesis of colloidal gold. Discus Faraday Soc. 1951;11:55–75. https://doi.org/10.1039/DF9511100055.
Khan MM, Kalathil S, Han TH, Lee J, Cho MH. Positively charged gold nanoparticles synthesized by electrochemically active biofilm - a biogenic approach. J Nanosci Nanotechnol. 2013;9:6079–85. https://doi.org/10.1166/jnn.2013.7666.
Ábrahám N, Sebők D, Sz P, Kőrösi L, Dékány I. Two-dimensional arrangement of monodisperse ZnO particles with Langmuir–Blodgett technique. Colloid Surf A. 2011;384:80–9. https://doi.org/10.1016/j.colsurfa.2011.03.025.
Guinier A, Fournet G. Small angle scattering of X-rays. New York: John Wiley and Son; 1955.
Kanyo T, Konya Z, Berger F, Dekany I, Kiricsi I. Binary solvent mixture adsorption as a characterisation tool to determine the hydrophilic/hydrophobic properties of multiwall carbon nanotubes. Chem Commun. 2003;7:2746–7. https://doi.org/10.1039/b310066a.
Acknowledgments
Open access funding provided by University of Szeged (SZTE). The project presented in this article was supported by The Hungarian Scientific Research Fund (NKFIH OTKA) grant number PD 116224 (DS) and the UNKP-19-3 New National Excellence Program of the Ministry of Human Capacities (LM). This study was supported also by the European Union and the Government of Hungary through grants GINOP-2.3.2-15-2016-00013 and GINOP-2.3.3-15-2016-00010, The Ministry of Human Capacities, Hungary grant 20391-3/2018/FEKUSTRAT and by the János Bolyai Research Scholarship of the Hungarian Academy of Sciences.
Author information
Authors and Affiliations
Contributions
Conceptualization, methodology, software, SAXS measurements, writing—original draft preparation, D. Sebők; Synthesis, optical measurements, and evaluation, D. Sebők and D.S. Kovács; Surface modification, streaming potential measurements, L. Mérai; writing—review and editing, L. Janovák and L. Vásárhelyi; micro-CT measurement, D. Sebők; micro-CT evaluation, L. Vásárhelyi. and I. Szenti; supervision, Á. Kukovecz., I. Dékány., Z. Kónya.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Published in the topical collection Advances in Direct Optical Detection with guest editors Antje J. Baeumner, Günter Gauglitz, and Jiri Homola.
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
ESM 1
(PDF 858 kb)
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mérai, L., Janovák, L., Kovács, D.S. et al. Fast optical method for characterizing plasmonic nanoparticle adhesion on functionalized surfaces. Anal Bioanal Chem 412, 3395–3404 (2020). https://doi.org/10.1007/s00216-019-02307-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00216-019-02307-x