Evolution of grain and ripple structures on the surface of aluminum parts fabricated by laser foil printing process at preheat temperatures

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

In this study, the evolution of grain and ripple structures on the surface of 6061 aluminum alloy (AA6061) parts fabricated by a laser-foil-printing (LFP) additive manufacturing process at different preheated temperatures were characterized and compared. Results indicated that the preheated temperature of the substrate plays a crucial role in the formation of grain structures, the shape of ripples, and the surface quality of aluminum parts fabricated by LFP. As the preheated temperature of the substrate elevated from room temperature to 300 °C, the grain and ripple structures formed coarser and flatter, respectively, due to the reduction in the thermal gradient and cooling rate. The grain structure was coarsened with an increasing average grain size from 74.96 to 150.5 μm measured by the electron backscattered diffraction (EBSD) technique. Meanwhile, the ripple structure was stretched and transformed from short and curved shapes to smoother, which improved the surface roughness significantly and reduced the Sa value from 21.7 to 8.5 μm in three-dimensional (3D) surface morphologies. However, when the preheated temperature reached 500 °C in LFP, the grain structure experienced a recrystallization process, resulting in the formation of finer grains compared to those observed at 300 °C. Furthermore, the surface quality was improved to a Sa value of 5.2 μm because the flowability of the melt pool was enhanced from the extended solidification time by the smallest temperature gradient and cooling rate at the highest preheat temperature, which was estimated using the finite element method (FEM). In the X-ray diffraction (XRD) patterns, the ratio of the main peak (200) to the secondary peak was gradually increased when preheated temperature elevated; however, the ratio decreased at 500 °C due to the recrystallization.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1 
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13

Similar content being viewed by others

Data availability

The raw/processed data required to reproduce these findings will be made available on email request.

References

  1. Campbell, F.C. 2006. “Manufacturing technology for aerospace structural materials.” https://doi.org/10.1016/B978-1-85617-495-4.X5000-8.

  2. Thijs L, Frederik V, Craeghs T, Humbeeck JV, Kruth J-P (2010) A study of the microstructural evolution during selective laser melting of Ti-6Al-4V. Acta Mater 58(9):3303–3312. https://doi.org/10.1016/j.actamat.2010.02.004

    Article  Google Scholar 

  3. Sun Z, Tan X, Tor SB, Yeong WY (2016) Selective laser melting of stainless steel 316L with low porosity and high build rates. Mater Des 104:197–204. https://doi.org/10.1016/j.matdes.2016.05.035

    Article  Google Scholar 

  4. Tucho WM, Cuvillier P, Atle S-K, Hansen V (2017) Microstructure and hardness studies of Inconel 718 manufactured by selective laser melting before and after solution heat treatment. Mater Sci Eng, A 689:220–232. https://doi.org/10.1016/j.msea.2017.02.062

    Article  Google Scholar 

  5. Chen B, Moon SK, Yao X, Bi G, Shen J, Umeda J, Kondoh K (2018) Comparison study on additive manufacturing and powder metallurgy AlSi10Mg alloys. JOM 70:644–649. https://doi.org/10.1007/s11837-018-2793-4

    Article  Google Scholar 

  6. Kempen K, Thijs L, Humbeeck JV, Kruth J-P (2015) Processing AlSi10Mg by selective laser melting: parameter optimization and material characterization. Mater Sci Technol 31:917–923. https://doi.org/10.1179/1743284714Y.0000000702

    Article  Google Scholar 

  7. Thijs L, Kempen K, Kruth J-P, Humbeeck JV (2013) Fine-structured aluminum products with controllable texture by selective laser melting of pre-alloyed AlSi10Mg powder. Acta Mater 61(5):1809–1819. https://doi.org/10.1016/j.actamat.2012.11.052

    Article  Google Scholar 

  8. Mehta L, Zhou T, Huynh S, Park H, Hyer ST, Song YL, Bai DD, Imholte NE, Woolstenhulme DM, Wachs, and Y.H. Sohn. (2021) Additive manufacturing and mechanical properties of the dense and crack free Zr-modified aluminum alloy 6061 fabricated by the laser-powder bed fusion. Addit Manuf 41:101966. https://doi.org/10.1016/j.addma.2021.101966

    Article  Google Scholar 

  9. Qbau N, Nam ND, Ca NX, Hien NT (2020) The crack healing effect of scandium in aluminum alloys during laser additive manufacturing. J Manuf Process 50:241–246. https://doi.org/10.1016/j.jmapro.2019.12.050

    Article  Google Scholar 

  10. Bradford RL, Cao L, Don Klosterman F, Herman LF, Browning C (2021) A metal–metal powder formulation approach for laser additive manufacturing of difficult-to-print high-strength aluminum alloys. Mater Lett 300:130113. https://doi.org/10.1016/j.matlet.2021.130113

    Article  Google Scholar 

  11. Benoit MJ, Whitney MA, Zhu SM, Zhang D, Field MR, Easton MA (2023) The beneficial effect of minor iron additions on the crack susceptibility of rapidly solidified aluminum alloy 6060 toward additive manufacturing applications. Mater Charact 205:113287. https://doi.org/10.1016/j.matchar.2023.113287

    Article  Google Scholar 

  12. Louvis E, Fox P, Sutcliffe CJ (2011) Selective laser melting of aluminium components. J Mater Process Technol 211(2):275–284. https://doi.org/10.1016/j.jmatprotec.2010.09.019

    Article  Google Scholar 

  13. Uddin SZ, Murr LE, Terrazas CA, Morton P, Roberson DA, Wicker RB (2018) Processing and characterization of crack-free aluminum 6061 using high-temperature heating in laser powder bed fusion additive manufacturing. Addit Manuf 22:405–415. https://doi.org/10.1016/j.addma.2018.05.047

    Article  Google Scholar 

  14. Buchbinder D, Meiners W, Norbert P, Wissenbach K, Schrage J (2014) Investigation on reducing distortion by preheating during manufacture of aluminum components using selective laser melting. J Laser Appl 26(1):012004. https://doi.org/10.2351/1.4828755

    Article  Google Scholar 

  15. Joghan HD, Hahn M, Tekkaya AE (2023) Effect of preheating during laser metal deposition on the properties of laminated bending dies. Intl J Adv Manuf Technol 125:157–168. https://doi.org/10.1007/s00170-022-10697-z

    Article  Google Scholar 

  16. Hung CH, Sutton A, Li Y, Shen Y, Tsai HL, Leu MC (2019) Enhanced mechanical properties for 304L stainless steel parts fabricated by laser-foil-printing additive manufacturing. J Manuf Process 45:438–446. https://doi.org/10.1016/j.jmapro.2019.07.030

    Article  Google Scholar 

  17. Li Y, Shen Y, Hung CH, Leu MC, Tsai HL (2018) Additive manufacturing of Zr-based metallic glass structures on 304 stainless steel substrates via V/Ti/Zr intermediate layers. Mater Sci Eng, A 729:185–195. https://doi.org/10.1016/j.msea.2018.05.052

    Article  Google Scholar 

  18. Hung CH, Turk T, Sehhat MH, Leu MC (2022) Development and experimental study of an automated laser-foil-printing additive manufacturing system. Rapid Prototyp J 28(6):1013–1022. https://doi.org/10.1108/RPJ-10-2021-0269

    Article  Google Scholar 

  19. Hung CH, Chen WT, Sehhat MH, Leu MC (2021) The effect of laser welding modes on mechanical properties and microstructure of 304L stainless steel parts fabricated by laser-foil-printing additive manufacturing. Intl J Adv Manuf Technol 112:867–877. https://doi.org/10.1007/s00170-020-06402-7

    Article  Google Scholar 

  20. Chen C, Shen Y, Tsai HL (2022) A foil-based additive manufacturing technology for metal parts. J Manuf Sci Eng 139(2):024501. https://doi.org/10.1115/1.4034139

    Article  Google Scholar 

  21. Hung CH, Li Y, Sutton A, Chen WT, Gong X, Pan H, Tsai HL, Leu MC (2020) Aluminum Parts Fabricated by Laser-Foil-Printing Additive Manufacturing: Processing, Microstructure, and Mechanical Properties. Materials 13(2):414. https://doi.org/10.3390/ma13020414

    Article  Google Scholar 

  22. Wang YX, Hung CH, Pommerenke H, Wu SH, Liu TY (2024) Fabrication of crack-free aluminum alloy 6061 parts using laser foil printing process. Rapid Prototyping J. https://doi.org/10.1108/RPJ-10-2023-0370

    Article  Google Scholar 

  23. Zhang DY, Zhang P, Liu Z, Feng Z, Wang C, Guo Y (2018) Thermofluid field of molten pool and its effects during selective laser melting (SLM) of Inconel 718 alloy. Addit Manuf 21:567–578. https://doi.org/10.1016/j.addma.2018.03.031

    Article  Google Scholar 

  24. Chen HH, Lo YL, Hsu YY, Lai KL (2023) Systematic optimization of L-PBF processing parameters for Al alloy 6061 with YSZ nanoparticles. Opt Laser Technol 167:109676. https://doi.org/10.1016/j.optlastec.2023.109676

    Article  Google Scholar 

  25. Gan ZT, Lian YP, Lin SE, Kevontrez KJ, Liu WK, Wagner GJ (2019) Benchmark study of thermal behavior, surface topography, and dendritic microstructure in selective laser melting of Inconel 625. Integr Mater Manuf Innov 8:178–193. https://doi.org/10.1007/s40192-019-00130-x

    Article  Google Scholar 

  26. Riva R, Siqueira RHM, Lima MSF (2015) Crack-free autogeneous one-sided laser welding of a 6013 aluminum alloy T-joint for aircraft applications. Presented at: Lasers in Manufacturing Conference 2015. Proceedings of LIM 2015, Munich, Germany. WLT, Bochum

  27. Yusuf NK, Lajis MA, Daud MI, Noh MZ (2013) Effect of operating temperature on direct recycling aluminium chips (AA6061) in hot press forging process. Appl Mech Mater 315:728–732. https://doi.org/10.4028/www.scientific.net/AMM.315.728

    Article  Google Scholar 

  28. Wang J, Chen X, Yang L, Zhang G (2022) Effect of preheat & post-weld heat treatment on the microstructure and mechanical properties of 6061–T6 aluminum alloy welded sheets. Mater Sci Eng, A 841:143081. https://doi.org/10.1016/j.msea.2022.143081

    Article  Google Scholar 

  29. Liu WC, Li Z, Man C-S (2008) Effect of heating rate on the microstructure and texture of continuous cast AA 3105 aluminum alloy. Mater Sci Eng, A 478(1–2):173–180. https://doi.org/10.1016/j.msea.2007.05.107

    Article  Google Scholar 

  30. Hossain E, Hassan F, Mousavi SAAA, Ghahramani A (2020) Microstructural analyses of aluminum-magnesium-silicon alloys welded by pulsed Nd: YAG laser welding. Int J Miner Metall Mater 27:660–668. https://doi.org/10.1007/s12613-020-2027-y

    Article  Google Scholar 

  31. Chu Q-L, Bai R-X, Jian H-G, Lei Z-K, Hu N, Cheng Y (2018) Microstructure, texture and mechanical properties of 6061 aluminum laser beam welded joints. Mater Charact 137:269–276. https://doi.org/10.1016/j.matchar.2018.01.030

    Article  Google Scholar 

Download references

Acknowledgements

The authors would like to thank Ms. Hui–Jung Shih and Ms. Tsai-Yun Liu with the Core Facility Center of National Cheng Kung University for supporting the use of HR-SEM (Hitachi SU8000) and HR-SEM (Hitachi SU5000).

Funding

This research work was supported by the National Science and Technology Council, Taiwan, R.O.C. (grant number 111–2222-E-006–001-MY2), (grant number 111–2622-E-006–023), and (grant number 112–2622-E-006–012).

Author information

Authors and Affiliations

  1. Department of Mechanical Engineering, National Cheng Kung University, Tainan, Taiwan

    Yu-Xiang Wang, Zhen-Jie Zhao, Hsiang-Min Kuo & Chia-Hung Hung

Authors
  1. Yu-Xiang Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Zhen-Jie Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Hsiang-Min Kuo
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Chia-Hung Hung
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

Yu-Xiang Wang: methodology, investigation, formal analysis, writing—original draft; Zhen-Jie Zhao: validation, data curation; Hsiang-Min Kuo: validation, data curation; Chia-Hung Hung: conceptualization, supervision, funding acquisition, writing—review and editing.

Corresponding author

Correspondence to Chia-Hung Hung.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Wang, YX., Zhao, ZJ., Kuo, HM. et al. Evolution of grain and ripple structures on the surface of aluminum parts fabricated by laser foil printing process at preheat temperatures. Int J Adv Manuf Technol (2024). https://doi.org/10.1007/s00170-024-13742-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s00170-024-13742-1

Keywords

Search

Navigation