Abstract
The primary recrystallization textures of 11 single crystals cold rolled 70 pet were determined. The effect of crystal orientation on recrystallization behavior was investigated also and found to be large. Ah exception was found to the relationship that strong components of the recrystallization texture are rotated from the cold rolled texture by 30° about <110> axes, but generally this relationship was found to hold quite well. Evidence supporting oriented nucleation was found and discussed in terms of probable active slip systems and <110> edge dislocations.
Similar content being viewed by others
References
C. G. Dunn: Acta Metallurgica, 1953, vol. 1, p. 163.
C. G. Dunn: Acta Metallurgica, 1954, vol. 2, p. 173.
P. K. Koh and C. G. Dunn: AIME Trans., 1955, vol. 203, p. 401; Journal of Metals, February 1955.
P. A. Beck: Acta Metallurgica, 1953, vol. 1, p. 230.
W. G. Burgers and T. J. Tiedema: Acta Metallurgica, 1953, vol. 1, p. 234.
W. G. Burgers and P. C. Louwerse: Ztsch. für Physik, 1931, vol. 67, p. 605.
R. W. Cahn: Proceedings Physical Soc., London, 1950, vol. A63, p. 323.
P. A. Beck: Journal of Applied Physics, 1949, vol. 20, p. 633.
C. G. Dunn: AIME Trans., 1946, vol. 167, p. 357.
K. V. Gow and R. W. Cahn: Acta Metallurgica, 1953, vol. 1, p. 238.
A. H. Cottrell. Dislocations and Plastic Flow in Crystals, 1953. London. Oxford Univ. Press.
Y. C. Liu and W. R. Hibbard: AIME Trans., 1953, vol. 197, p. 672; Journal of Metals, May 1953.
A. H. Lutts and P. A. Beck: AIME Trans., 1954, vol. 200, p. 257; Journal of Metals, February 1954.
B. F. Decker and D. Harker: Journal of Applied Physics, 1951, vol. 22, p. 900.
Author information
Authors and Affiliations
Additional information
TP 4114E. Manuscript, Apr. 14, 1955. Philadelphia Meeting, October 1955.
Rights and permissions
About this article
Cite this article
Dunn, C.G., Koh, P.K. Primary Recrystallization Textures in Cold Rolled Si-Fe Crystals. JOM 8, 1017–1024 (1956). https://doi.org/10.1007/BF03377812
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03377812