Temperature dependence of the differential susceptibility of cobalt in strong magnetic fields

Abstract

A curve showing a characteristic double maximum was obtained for the temperature dependence of the differential susceptibility of cobalt in strong magnetic fields; all sections of this curve could be interpreted on the basis of the theory of the rotation processes. The temperature of the minimum between the two maxima calculated fromSucksmith andThomson’s [13] measurement on monocrystals is found to be in good agreement with the temperature pertaining to the experimentally determined minimum of the differential susceptibility of a polycrystalline sample. The effect of thea⇆β phase transformation on the differential susceptibility is studied.

Резюме

Для температурной зависимости дифференциальной восприимчивости кобальта в сильных магнитных полях были получены особые кривые с двумя максимумами. Разные части этих кривых могут быть объяснены на основе теории процессов вращения. При температуре 294 °C имеется резкий локальный минимум дифференциальной восприимчивости. На основе измерений Саксмита и Томсона [13], проведенных на монокристалле кобальта, авторами была расчитана теоретическая кривая дифференциальной восприимчивости поликристаллического образца в температурном интервале 240–350 °C при 1332 Ое. Сравнение экспериментальной кривой с теоретической показывает, что в непосредственной окрестности 290 300 °C согласие очень хорошее. На теоретической кривой локальному минимуму дифференциальной восприимчивости соответствует 293 °C, что отличается от экспериментального значения только на один градус. В последней части работы было исследовано влияние фазового преваршения кобальта на ход кривой дифференциальной восприимчивости.