Abstract
An investigation has been conducted to describe the effect of Ti grain refiner or Sr modifier on the microstructure of an Al-11.3 wt.%Si alloy produced by the Ohno horizontal continuous casting process so as to obtain directional solidification at high cooling rates. Experimental results demonstrated that the directionality of the primary grains were promoted by the addition of 0.2 to 0.4%Ti or by the addition of 0.02%Sr, whereas the addition of 0.6%Ti suppressed this directionality. Feathery grains were promoted by the addition of 0.2%Ti, while these feathery grains were suppressed when over 0.4%Ti or when 0.02%Sr was added. The addition of Ti also resulted in increased coarsening of the eutectic Si in these Al-11.3 wt.%Si alloys.
Similar content being viewed by others
References
M. D. Hanna, S. Lu and A. Hellawell,Metall. Trans. A. 15, 459 (1984).
D. Apelian, J. Allen Cheng,Prvc. of the AFS/CMI Conference, p. 179, AFS, California, USA (1986).
J. L. Carvajal, C. Casado, J. F. Mojica, S. Valtierra,Proc. of AFS 3rd International Conference on Molten Aluminum Processing, p. 141, AFS, Orlando, Florida, USA (1992).
H. Soda, F. Chabchoub, W. H. Lam, S. A. Argyropoulos and A. Mclean,Cast Metals 4, 12 (1991).
A. Ohno,J. of Metals 38, 14 (1986).
Y. J. Lee, H. H. Jo and M. H. Kim,J. Kor. Inst. Met. & Mater. 31, 361 (1984).
A. T. Joenoes and J. C. Gruzleski,Cast Metals 2, 62 (1991).
L. Backerud, E. Krol and J. Tamminen,Solidification Characteristics of Aluminum Alloy, vol. 1, p. 39, Scanaluminum, Norway (1986).
A. L. Kearney, Avery Kearney and Company,Metal Handbook, vol. 2, p. 171, ASM International, Ohio (1990).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, M.H., Jung, C.H., Jo, H.H. et al. The effects of Ti and Sr on the microstructures of Al-11.3 wt.%Si alloys produced by the ohno continuous casting process. Metals and Materials 6, 235–240 (2000). https://doi.org/10.1007/BF03028217
Issue Date:
DOI: https://doi.org/10.1007/BF03028217