The present study has been undertaken to better understand the solidification behavior of Al−Si−Fe alloys containing 7wt.% Si and 0.9wt.% Fe, with particular regard to the formation of phase during controlled solidification and influence of growth rates on intermetallic phase selection. The alloys studied were Al-7Si-0.9Fe alloys, which were produced by a modified Bridgman solidification arrangement. These alloys were solidified unidirectionally with different growth rates (1–30mm/min). The solidified microstructure of these alloys consists of the growth of primary aluminum and multiple second phase reactions.
Similar content being viewed by others
References
M. K. Surappa, E. W. Blank, and J. C. Jaquet,Solidification Processing, p. 427, The Institute of Metals, London (1987).
Y. H. Tan, S. L. Lee, and Y. L. Lin,Metall. Mater. Trans. A 26, 1195 (1995).
S. Murali, K. S. Raman, and K. S. S. Murthy,Mater. Character. 33, 99 (1994).
J. X. Dong, P. A. Karnezis, G. Durrant, and B. Cantor,Metall. Mater. Trans. A 30, 1341 (1999).
D. C. Jenkinson and L. H. Hogan,Crystal Growth 28, 171 (1975).
Z. W. Chen and W. R. Thorpe,Mater. Sci. Eng. A 221, 143 (1996).
Y. S. Choi and H. Y. Ra,J. Kor. Inst. Met. & Mater. 34, 230 (1996).
L. Ananthanarayanan and F. H. Samuel,AFS Trans. 141, 383 (1992).
K. F. Kobayashi and L. M. Hogan,J. Mater. Sci. 20, 1916 (1985).
L. M. Hogan and M. Shamsuzzoha,Solidification Processing, p. 40, The Institute of Metals, London (1987).
B. Closset and J. E. Gruzleski,Metall. Mater. Trans. A 13, 945 (1982).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Han, Y.S., Choi, J.O., Choi, C.O. et al. Intermetallic phase formation in directionally solidified Al−Si−Fe alloy. Met. Mater. Int. 10, 27–32 (2004). https://doi.org/10.1007/BF03027360
Issue Date:
DOI: https://doi.org/10.1007/BF03027360