Abstract
TiAl alloys incorporated in (0,3,5,10) wt.% TiB2 dispersoids were manufactured via mechanical alloyingspark plasma sintering (MA-SPS), and their cyclic oxidation characteristics were studied at 800, 900 and 1000°C in air. The cyclic oxidation resistance of the prepared TiAl-TiB2 composites effectively increased with increases in TiB2 content. The oxide scale formed consisted of an outer TiO2 layer, an intermediate Al2O3 layer, and an inner (Al2O3+TiO2) mixed layer. The scale adherence was relatively good, and much thinner oxide scales, when compared to TiB2-free TiAl alloys, were formed on the prepared composites. The incorporated TiB2 dispersoids oxidized to TiO2 and B2O3 which evaporated during oxidation.
Similar content being viewed by others
References
Y. W. Kim,J. of Metals 41, 24 (1989).
Y. W. Kim,J. of Metals 46, 30 (1994).
D. B. Lee, J. H. Park, Y. H. Park and Y. J. Kim,Mater. Trans. JIM.38, 306 (1997).
J. Sorensen,Structural Intermetallics (eds., R. Darolia, J. J. Lewandowski, C. T. Liu, P. L. Martin, D. B. Miracle and M. V. Nathal), p. 717, TMS, PA (1993).
S. E. Hsu, H. Y. Chou, K. L. Wang, S. C. Yang, J. Y. Wang and C. I. Chen,Structural Iintermetallics (eds., R. Darolia, J. J. Lewandowski, C. T. Liu, P. L. Martin, D. B. Miracle and M. V. Nathal), p. 749, TMS, PA (1993).
D. E. Larsen, M. L. Adams, S. L. Kampe, L. Christodoulou and J. D. Bryant,Scripta metall. mater. 24, 851 (1990).
M. Saqib, I. Weiss, G. M. Mehrotra, E. Clevenger, A. G. Jackson and H. A. Lipsitt,Metall. Trans. A 22, 1721 (1991).
K. T. Venkateswara Rao, G. R. Odette and R. O. Ritchie,Acta metall. 40, 353 (1992).
S. A. Kekare, J. B. Toney and P. B. Aswath,Metall. Trans. A 26, 1835 (1995).
S. Nourbakhsh, O. Sahin and H. Margolin,Acta metall. 43, 3035 (1995).
L. Christodoulou, P. Parrish and C. R. Crowe,High Temperature/High Performance Composites (eds., F. D. Lemkey, S. G. Fishman, A. G. Evans and J. R. Strite), p. 29, Materials Research Society, PA (1988).
S. L. Kampe, J. D. Bryant and L. Christodoulou,Metall. Trans. A 22, 447 (1991).
A. Szaruga, L. Rothenflue, R. Srinivasan and H. A. Lipsitt,Scrip. metall. mater. 26, 1565 (1992).
S. L. Kampe, P. Sadler, L. Christodoulou and D. E. Larsen,Metall. Mater. Trans. A 25, 2181 (1994).
E. S. C. Chin, K. F. Ryan and R. R. Biederman,Gamma Titanium Aluminides (eds., Y. W. Kim, R. Wagner and M. Yamaguchi), p. 451, TMS, PA (1995).
E. S. C. Chin, T. Weerasooriya, P. Woolsey and R. R. Biederman,Gamma Titanium Aluminides (eds., Y. W. Kim, R. Wagner and M. Yamaguchi), p. 425, TMS, PA (1995).
D. B. Lee, M. H. Kim, C. W. Yang, S. H. Lee, M. Yang and Y. J. Kim,Oxid. Met. (2001) in press.
H. Hashimoto,Materia 38, 68 (1999).
J. H. Won, Y. J. Kim, S. W. An and D. B. Lee,J. Kor. Inst. Met. & Mater. 36, 546 (1998).
G. H. Meier,Oxidation of Intermetallics (eds., H. J. Grabke and M. Schütze), p. 15, Wiley-VCH, New York (1997).
Y. Umakoshi, M. Yamaguchi, T. Sakagami and T. Yamane,J. Mater. Sci. 24, 1599 (1989).
S. W. An and D. B. Lee,J. Kor. Inst. Met. & Mater. 36, 1671 (1998).
D. B. Lee,Bul. Kor. Inst. Met. & Mater. 10, 312 (1997).
S. C. Choi, H. J. Cho and D. B. Lee,J. Kor. Inst. Surf. Eng. 26, 235 (1993).
R. J. Irving and I. G. Worsley,J. Less-Common Met. 16, 103 (1968).
M. G. Barandika, J. J. Echeberria, J. M. Sánchez and F. Castro,J. Mater. Chem. 8, 1851 (1998).
H. Itoh, K. Sugiura and H. Iwahara,J. Ceram. Soc. Jpn. 103, 949 (1995).
B. Cockeram and R. A. Rapp,Oxid. Met. 45, 427 (1996).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lee, D.B., Kim, M.H., Kim, S.E. et al. Cyclic oxidation behavior of TiAl composites incorporated with TiB2 dispersoids. Met. Mater. Int. 7, 143–149 (2001). https://doi.org/10.1007/BF03026952
Issue Date:
DOI: https://doi.org/10.1007/BF03026952