TDPAC studies of Hf doped YBCO

Abstract

Time differential perturbed angular correlation measurements of the 133–482 keVγ-γ cascade of¹⁸¹Ta in Hf-doped YBa₂Cu₃O_7−x are presented. The¹⁸¹Hf precurser nuclei are incorporated into the sample by thermal neutron irradiation. Two quadrupole interaction frequencies are observed in the as-irradiated sample:v _Q1=161±10 MHz with intensityf ₁=75%, asymmetry parameterη ₁=0.32 and damping parameter Λ₁=0.42, andv _Q2=1108±40 MHz withf ₂=25%,η ₂=0.62, and Λ₂=0.60. On annealing the sample in air at various temperaturesT _a and quenching to room temperature,f ₁ remained nearly constant forT _a<600°C andv _Q1 for all annealing temperatures indicating that these are insensitive to oxygen stoichiometry. This frequency is interpreted to be due to¹⁸¹Hf substitutingY sites. BeyondT _a=600°C,f ₁ increased and reached a constant value of 90% forT _a=800°C. The value ofv _Q2 showed a slight variation between 1086 and 1160 MHz, whilef ₂ remained nearly constant at 25% forT _a<600°C. This component is identified to be due to¹⁸¹Hf substituting Cu 1 sites in the Cu-O chains of YBCO. Above 600°Cv _Q2 decreased and reached a value of 808 MHz beyond 750°C.