Summary
Resistive and magnetic measurements have been performed on some iron-nickel system alloys in order to study the martensitic transformation as a function of temperature. The analysis of the experimental results enables us to obtain some information about the mechanism of transformation. The free-energy changes accompanying the transformation of various alloys appear to cause either the organization of embryos into groups giving rise to bursts, or the activation of single embryos that control the smooth behaviour of transformation.
Riassunto
Sono state effettuate misure di resistenza elettrica e di momento magnetico in funzione della temperatura di raffreddamento su leghe di ferro-nichel allo scopo di studiare la trasformazione martensitica. L’analisi dei risultati sperimentali permette di ottenere informazioni sulla variazione di energia libera che accompagna la trasformazione martensitica delle varie leghe. Essa sembra essere responsabile sia dell’organizzazione degli embrioni in gruppi che, successivamente, si trasformano come burst, sia dell’attivazione dei singoli embrioni che permettono di ottenere un comportamento regolare nella trasformazione della lega.
Резюме
Проводятся измерения сопротивления и магнитные измерения на некоторых железо-никелевых сплавах, чтобы исследовать мартенситное преобразование, как функцию температуры. Анализ экспериментальных результатов позволяет нам получить некоторую информацию о механизме преобразования. Изменения свободной энергии, сопровождающие преобразование различных сплавов, по-видимому, вызывают либо преващение зародышей в группы, что приводит к возникновению импулясов, или активацию отдельных зародышей, что определяет плавное поведение преобразования.
Similar content being viewed by others
References
J. J. Kramer andR. K. Raheja:Techniques for investigating phase transition kinetics in metals, inTechniques of Metals Research, edited byR. F. Bunshah, Vol. IV, part I (New York, N. Y., 1970), p. 488.
Y. Nakamura:IEEE Trans. Magn.,12, 278 (1976).
M. Hansen:Constitution of Binary Alloys (New York, N. Y., 1958), p. 680.
S. S. Hsu, J. H. Chen andP. C. Clapp:Phys. Status Solidi A,50, 393 (1978).
A. W. Mc Reynolds:J. Appl. Phys.,17, 823 (1946).
M. Peschard:Rev. Met.,22, 490, 581, 663 (1925).
Y. Tino andH. Kagawa:J. Phys. Soc. Jpn.,28, 1445 (1970).
S. Chikazumi, T. Mizoguchi andN. Yamaguchi:J. Appl. Phys.,39, 939 (1968).
W. F. Schlosser:J. Phys. Chem. Solids,32, 939 (1971).
P. C. Clapp:Phys. Status Solidi B,57, 561 (1963).
H. Knapp andV. Dehlinger:Acta Met.,4, 289 (1956).
L. Kaufman andM. Cohen:Prog. Metal. Phys.,7, 165 (1958).
L. Kaufman andM. Cohen:Trans. AIME,206, 1393 (1956).
Author information
Authors and Affiliations
Additional information
Переведено редакцией
Rights and permissions
About this article
Cite this article
Bordin, G., Cecchi, G.C. & Fratucello, G.B. Remarks on the martensitic transformation in some iron-nickel alloys. Nuov Cim B 61, 338–346 (1981). https://doi.org/10.1007/BF02721334
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02721334