Magnetization by twisting in a weak field

Summary

It was found that both circular and longitudinal Matteucci effects cannot be measured below the same value H _sof the magnetic field which depends on the ferromagnetic substance and on the impurities contained in it. This result was integrated, for pure Fe and Ni (99.8%), by direct magnetization measurements for very weak fields, carried out with a sensitive magnetometer. By comparing the behaviour of the sample before and after the twisting, it was found that the magnetization is not affected by stresses for values of the field lower than H _s,that is in the region of reversible processes. Particularly it was found that the permeability coefficient for H = 0 must not depend on stresses even if they are very strong. Really the region of magnetization curve which is strongly affected by stresses is essentially that of irreversible processes and we suggest to interpret H _sas a threshold field, such as the coercive force of the magnetization cycle induced by stresses with respect to H.

Riassunto

Si è trovato che l’effetto Matteucci sia circolare che longitudinale non compare al di sotto di uno stesso valore H _sdel campo magnetico, che dipende dalla sostanza ferro-magnetica e dalle impurezze in essa contenute. Questo risultato è stato integrato, per il Fe puro ed il Ni (99.8%), da dirette misure di magnetizzazione, con un magnetometro sensibile, per campi molto bassi. Dal confronto, in assenza e in presenza di sforzi, si è trovato che la magnetizzazione non è influenzata dagli sforzi per valori del campo inferiori ad H _s,nella regione cioè di processi di magnetizzazione reversibili, ed in particolare il coefficiente di permeabilità per H = 0 deve essere indipendente dalla presenza di sforzi, anche se molto intensi. La regione della curva di magnetizzazione, fortemente influenzata dagli sforzi, è essenzialmente quella dei processi irreversibili e noi suggeriamo d’interpretare H _s,come un valore di soglia, quale forza coercitiva del ciclo di magnetizzazione indotta dagli sforzi in funzione di H.

Реэюме

Найдено, что и циркулярный и продольный зффекты Маттеуччи не могут быть иэмерены ниже одной и той же величины H _sмагнитного пола, которая эависит от ферромагнитного вешества и от примесей, в нем содержашихся. Этот реэультат интегрируется для чистого Fe и Ni(99.8%) посредством прямых иэмерений намагничивания для очень слабых полей, которые проведены с помошью чувствительного магнитометра. Посредством сравнения поведения обраэца до и после скручивания, было получено, что намагничивание не иэменяется иэ-эа напряжений для эначений поля, ниже чем H _s,которое находится в области обратимых процессов. Практически обнаружено, что козффициент проницаемости для H=0 должен не эависеть от напряжений, даже если они очень больщие. Реально, область кривой намагничивания, которая сильно иэменяется благодаря напряжениям, является, по сушеству, областью необратимых процессов, и мы предлагаем интерпретировать H _s,как пороговое поле, а именно, козрцитивная сила цикла намагничивания, выэванная напряжениями относительно H.