A rapidly solidified Al-10 wt pct Be-3 wt pet Li alloy has been produced by a melt-spinning technique. The aging behavior of the melt-spun ribbon has been characterized by a number of techniques, including differential scanning calorimetry, hardness measurements, and transmission electron microscopy. The results have shown that the aging responses of the ternary Al-Be-Li alloy are very similar to those of Al-Li binary alloys. Specifically, δ′ precipitates are formed at temperatures near 180 °C and they transform to δ at temperatures around 300 °C. Microstructural examination indicates that, in the Al-Be-Li alloy, α-Be particles are present in the matrix as independent dispersoids and, apparently, have little effect on the aging behavior of the Al-Li matrix; no new phases are present in the matrix of specimens heat treated up to 400 °C. The α-Be particles coarsen, however, above a temperature of approximately 300 °C. The growth of α-Be particles follows the classical Ostwald coarsening type of mechanism.
Similar content being viewed by others
References
R. E. Lewis: Progress Report for June–Sept. 1985, Naval Air Devel- opment Contract No. N62269-84-C-036.
E. Vidoz, D.D. Crooks, R.E. Lewis, I. G. Palmer, and J. Wadsworth:Rapidly Solidified Powder Aluminum Alloys, M. E. Fine and E. A. Starke, eds., ASTM STP No. 890, Amer. Soc. for Testing of Materials, Philadelphia, PA, 1986.
J. Wadsworth, A. Joshi, D. D. Crooks, and A. E. Vidoz:J. Mater. Sci., 1986, vol. 21, pp. 3843–49.
J. Wadsworth, A.R. Pelton, D.D. Crooks, R.E. Lewis, and A.E. Vidoz:J. Mater. Sci., 1986, vol. 21, pp. 3850–58.
J. Wadsworth, A. R. Pelton, and A. E. Vidoz:Int. Jour. Mater. Sci. Eng., 1986, vol. 80, pp. L23-L26.
A. Joshi, J. Wadsworth, and A.E. Vidoz:Scripta Metall., 1986, vol. 20, pp. 529–32.
R.J. Gest and A.R. Troiano:Corrosion, 1974, vol. 30, (8), pp. 274–79.
D. P. Hill and D.N. Williams: Final Report, Contract No. N00019- 81-C-0433, Oct. 1982.
J. G. Moncur, A.B. Campa, and P.C. Pinoli:J. High Resolution Chromotography, 1982, vol. 5, pp. 322–24.
J.B. Pethica, R. Hutchings, and W.C. Oliver:Phil. Mag., 1983, vol. 48A, (4), pp. 593–606.
Proc. 3rd Conf. on Rapid Solidification Processing, R. Mehrabian, ed., National Bureau of Standards, Gaithersburg, MD, Dec. 1982, p. 521.
H.E. Kissinger:Anal. Chem., 1957, vol. 29, pp. 1702–17.
E. Louis and C. Garcia-Cordovilla:J. Mater. Sci. Lett., 1984, vol. 19, p. 689.
S.F. Baumann and D.B. Williams:Aluminum-Lithium II, E.A. Starke, Jr. and T. H. Sanders, Jr., eds., TMS-AIME, Warrendale, PA, 1984, p. 17.
J.M. Papazian, C. Sigli, and J.M. Sanchez:Scripta Metall., 1986, vol. 20, pp. 201–06.
R.A. Oriani:Acta Metall., 1964, vol. 12, pp. 1399–1409.
D.B. Williams:Aluminum-Lithium Alloys, T.H. Sanders, Jr. and E. A. Starke, Jr., eds., TMS-AIME,Warrensdale, PA, 1981, pp. 89–100.
I.M. Lifshitz and V. V. Slyozov:J. Phys. Chem. Solids, 1961, vol. 19, p. 35.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Nieh, T.G., Pelton, A.R., Oliver, W.C. et al. Characterization of the aging response of a melt-spun Al-Be-Li alloy ribbon. Metall Trans A 19, 1173–1178 (1988). https://doi.org/10.1007/BF02662577
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02662577