Interdiffusion in Co-Mn alloys

Abstract

Interdiffusion coefficient$\tilde D$ in cobalt-manganese alloys has been determined by Matano's method in the temperature range between 1133 and 1423 K on (pure Co)-(Co-30.28 at. pct Mn alloy) and (pure Co)-(Co-51.76 at. pct Mn alloy) couples. This, ∼D, has been found to increase with the increase of manganese content. However, the activation energy (∼Q) and frequency factor ($\tilde D$ ₀) show a maximum at about 10 at. pct Mn. The concentration dependence of$\tilde D$ and$\tilde Q$ has been discussed taking into account the thermodynamic properties of the alloy. The difference in$\tilde Q$ between the ferro- and paramagnetic phases in Co-5 at. pct Mn alloy has been found to be 24 kJ/mol, which is larger, than that for the diffusion of Mn⁵⁴ in this alloy. Further it has been found that the Kirkendall marker moves toward manganese-rich side, showing that manganese atoms diffuse faster than cobalt atoms. From the marker shift, the intrinsic diffusion coefficients,D _Co andD _Mn, at 33 at. pct Mn have been determined as follows:D _Co=0.22×10⁻⁴ exp(−263 kJ mol⁻¹/RT) m²/s, andD _Mn=0.98×10⁻⁴ exp(−229 kJ mol⁻¹/RT) m²/s.