Abstract
Molecular beam epitaxial growth of the ZnSe1-xTex (x=0.44-0.47) alloy on vicinal (001) GaAs substrates tilted four, six, and nine degree-[111]A or B results in partial phase separation of the alloy with a vertical modulation between different compositions. Transmission electron microscopy images of samples grown on four degree-tilted substrates showed superlattice-like structures, with periods in the range 13.4-28.9Â. Lattice images reveal diffuse interfaces between light and dark bands. Period variations were detected in isolated regions of some samples. We present evidence that the modulation develops at the growth surface, and remains stable in the bulk at temperatures up to 450°C. Satellite spot pairs with approximate indices (h k 1 + δ) were present near the zinc-blende spots in electron diffraction patterns and x-ray diffraction data, as expected from material with a sinusoidal composition profile. The orientation of the spots reveals that the modulation vector is parallel to the growth direction, rather than to [001]. The [111]A- and B-tilted samples showed significant modulation, while the five degree-[110] and on-axis material showed no detectable modulation. The modulation wavelength did not strongly depend on growth temperature in the range examined (285–335°C). Samples showing composition modulation did not exhibit significantly altered low-temperature luminescence spectra from material with no modulation.
Similar content being viewed by others
References
M. Aven,Appl. Phys. Lett. 7, 146 (1965).
M. Aven and W. Garwacki,J. Appl. Phys. 38, 2302 (1967).
J.E. Bernard and A. Zunger,Phys. Rev. B 36, 3199 (1987).
S. Larach, R.E. Shrader and C.F. Stocker,Phys.Rev. 108,587 (1957).
A. Ebina, M. Yamamoto and T. Takahashi,Phys. Rev. B 6, 3786 (1972).
M.J.S.P. Brasil, R.E. Nahory, F.S. Turco-Sandroff, H.L. Gilchrist and R.J. Martin,Appl. Phys. Lett. 58, 2509 (1991).
J.J. Davies,Semicond. Sci. Technol. 3, 219 (1988).
S. Permogorov, A. Reznitsky, A. Naumov, H. Stolz and W. Von der Osten,J. Luminescence 40, 41, 483 (1988).
A. Naumov, S. Permogorov, A. Reznitsky and S. Verbin,J. Cryst. Growth, 101, 713 (1990).
R.E. Smallman, W. Hume-Rothery,and C. W. Haworth,The Structure of Metals and Alloys, (London: Institute of Metals, 1988), p. 118.
J.B. Boyce and J.C. Mikkelsen, Jr.,J. Cryst. Growth 98, 37 (1989).
D.B. Zax, S. Vega, N. Yellin and D. Zamir,Chem. Phys. Lett. 138, 105 (1987).
R.D. Feldman, R.F. Austin, P.H. Fuoss, A.H. Dayem, E.H. Westerwick, S. Nakahara, T. Boone, J. Menendez, A. Pinczuk, J.P. Valladares and S. Brennan,J. Vac. Sci. Technol. B 5,690 (1987).
D.M. Wood and A. Zunger,Phys. Rev. B, 40, 4062 (1989).
R.M. Biefeld., K.C. Baucom, S.R. Kurtz and D.M. Follstaedt,J. Cryst. Growth 133, 38 (1993).
T.L. McDevitt, S. Mahajan, D.E. Laughlin, W.A. Bonner and V.G. Keramidas,Phys. Rev. B 45, 6614 (1992).
P. Bellon, J.P. Chevalier, G.P. Martin, E. Dupont-Nivet, C. Thiebaut and J.P. André,Appl. Phys. Lett. 53, 567 (1988).
LT. Feruguson, A.G. Norman, B.A. Joyce, T-Y. Seong, G.R. Booker, R.H. Thomas, C.C. Phillips and R.A. Stradling,Appl. Phys. Lett. 59, 3324 (1991).
T. Yao, Y. Makita and S. Maekawa,J. Cryst. Growth 45, 309 (1978).
F.S. Turco-Sandroff, R.E. Nahory, M.J.S.P. Brasil, R.J. Martin, R. Beserman, L.A. Farrow, J.M. Worlockand A.L. Weaver,J. Cryst. Growth 111, 762 (1991).
E.M. Alekseeva, V.V. Ivanov and V.A. Sanitarov,Inorganic Materials, 26, 2659 (1990).
M. Konagai, M. Kobayashi, R. Kimura and K. Takahashi,J. Cryst. Growth 86, 290 (1988).
M. Kobayashi, N. Mino, H. Katagiri, R. Kimura, M. Konagai and K. Takahashi,J. Appl. Phys. 60, 773 (1986).
H. Kuwabara, H. Fujiyasu, M. Aoki and S. Yamada,Jpn. J. Appl. Phys. 25, L707 (1986).
G.B. Stringfellow,J. Cryst. Growth 98, 108 (1989).
S. Froyen and A. Zunger,Phys. Rev. Lett. 66, 2132 (1991).
T. Suzuki and A. Gomyo,J. Cryst. Growth, 111, 353 (1991).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ahrenkiel, S.P., Bode, M.H., Al-Jassim, M.M. et al. Microcharacterization of composition modulations in epitaxial ZnSe1-xTex . J. Electron. Mater. 24, 319–325 (1995). https://doi.org/10.1007/BF02659694
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02659694