Initial stages of recrystallization in aluminum of commercial purity

  • Published:
Metallurgical Transactions A Aims and scope Submit manuscript

Abstract

In commercial aluminum with a purity of 99.4 pct, the formation and growth of recrystallization nuclei were studied by techniques such asin-situ annealing in a high voltage electron microscope, transmission electron microscopy and light microscopy. Sample parameters were the initial grain size (370 and 19 microns) and the degree of deformation (50 and 90 pct reduction in thickness by cold-rolling). It was found that the initial grain boundaries and high angle boundaries within the original grains are preferential sites for recrystallization nuclei, and that the effect of such sites is enhanced by the FeAl3 particles present in the commercial aluminum as impurities. The nucleation temperatures determined by high voltage electron microscopy and transmission electron microscopy decrease markedly when the initial grain size is decreased both after 50 and 90 pct cold rolling; a less pronounced temperature decrease is obtained by increasing the degree of deformation. The size of the recrystallization nuclei, the recrystallization temperature and the recrystallized grain size are reported for the four sample states, and finally the structural and kinetic observations are discussed.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others

References

  1. W. C. Leslie, J. T. Michalak, and F. W. Aul:Iron and Its Dilute Solid Solutions, C. W. Spencer and F. E. Werner, eds., p. 119, Interscience Publ., 1963.

  2. D. T. Gawne and G. T. Higgins:J. Mater. Sci., 1971, vol. 6, p. 403.

    Article  CAS  Google Scholar 

  3. A. T. English and W. A. Backofen:Trans. TMS-AIME, 1964, vol. 230, p. 396.

    CAS  Google Scholar 

  4. F. J. Humphreys:Acta Met., 1977, vol. 25, p. 1323.

    Article  CAS  Google Scholar 

  5. P. R. Mould and P. Cotterill:J. Mater. Sci., 1967, vol. 2, p. 241.

    Article  CAS  Google Scholar 

  6. R. D. Doherty and J. W. Martin:J. Inst. Metals, 1962–63, vol. 91, p. 332.

    Google Scholar 

  7. R. D. Doherty and J. W. Martin:Trans. ASM, 1964, vol. 57, p. 874.

    CAS  Google Scholar 

  8. F. J. Humphreys and J. W. Martin:Acta Met., 1966, vol. 14, p. 775.

    Article  CAS  Google Scholar 

  9. J. W. Martin:Metallurg., 1957, vol. 5, p. 161.

    Google Scholar 

  10. F. Haessner, E. Hornbogen, and M. Mukherjee:Z. Metallkund., 1966, vol. 57, p. 171.

    CAS  Google Scholar 

  11. C. W. Corti, G. A. Fitzpatrick, and P. Cotterill:Meeting on Reaystallization in the Control of Microstructure, London, ISI/IOM, 1973.

    Google Scholar 

  12. W. Normann:Z. Metallkund., 1967, vol. 58, p. 151.

    CAS  Google Scholar 

  13. R. K. Ray, W. B. Hutchinson, and B. J. Duggan:Acta Met., 1975, vol. 23, p.831.

    Article  Google Scholar 

  14. M. J. Makin:Phil. Mag., 1968, vol. 18, p. 637.

    CAS  Google Scholar 

  15. G. Das and T. E. Mitchell:Scr. Met., 1974, vol. 8, p. 1135.

    Article  CAS  Google Scholar 

  16. B. N. Singh and T. Leffers:Scr. Met., 1974, vol. 8, p. 549.

    Article  Google Scholar 

  17. J. Lindbo and T. Leffers:Metallogr., 1972, vol. 5, p. 473.

    Article  CAS  Google Scholar 

  18. S. B. Fisher:Rad. Effects, 1970, vol. 5, p. 239.

    CAS  Google Scholar 

  19. S. P. Bellier and R. D. Doherty:Acta Met., 1977, vol. 25, p. 521.

    Article  CAS  Google Scholar 

  20. N. Hansen and B. Bay:J. Mater. Sci., 1972, vol. 7, p. 1351.

    Article  CAS  Google Scholar 

  21. P. A. Beck and P. R. Sperry:J. Appl. Phys., 1950, vol. 21, p. 150.

    Article  CAS  Google Scholar 

  22. P. A. Vandermeer and P. Gordon:Trans. TMS-AIME, 1959, vol. 215, p. 577.

    CAS  Google Scholar 

  23. L. M. Brown and W. M. Stobbs:Phil. Mag., 1971, vol. 23, p. 1201.

    CAS  Google Scholar 

  24. H. K. Sehgal, E. P. Butler, and P. R. Swann:Scr. Met., 1975, vol. 9, p. 165.

    Article  CAS  Google Scholar 

  25. J. Friedel:Dislocations, p. 104-116, Pergamon Press, 1964.

  26. N. Hansen:Acta Met., 1977, vol. 25, p. 863.

    Article  CAS  Google Scholar 

  27. W. A. Anderson and R. F. Mehl:Trans. AIME, 1945, vol. 161, p. 140.

    Google Scholar 

  28. N. Hansen:Mém. Sci. Rev. Mét., 1975, vol. 72, p. 189.

    CAS  Google Scholar 

  29. H. Yoshida, B. Liebmann, and K. Lücke:Acta Met., 1959, vol. 7, p. 51.

    Article  CAS  Google Scholar 

  30. J. W. Rutter and K. W. Aust:Trans. TMS-AIME, 1960, vol. 218, p. 682.

    CAS  Google Scholar 

  31. A. R. Jones, B. Ralph, and N. Hansen:Met. Sci., in press.

Download references

Author information

Authors and Affiliations

Authors

Rights and permissions

Reprints and permissions

About this article

Cite this article

Bay, B., Hansen, N. Initial stages of recrystallization in aluminum of commercial purity. Metall Trans A 10, 279–288 (1979). https://doi.org/10.1007/BF02658335

Download citation

  • Received:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF02658335

Keywords

Navigation