Abstract
The isobaric phase diagram of the Cu2O-CuO-Y2O3 ternary system has been investigated under 0.21 atm oxygen partial pressure mainly by thermogravimetric and differential thermal analyses. The present system was confirmed to consist of four solid phases: Y2O3, Y2Cu2O5, CuO, and Cu2O. The Y2Cu2O5 phase is formed by the peritectic reaction with Y2O3 at 1493 K. An univariant reaction, L ⇆5 Cu2O + Y2Cu2O5, appears at 1368 K. Cu2O is stable at high temperatures and transforms to CuO at 1299 K.
Similar content being viewed by others
References
M. K. Wu, J. R. Ashbum, C. J. Torng, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang, Y. Q. Wang, and C. W. Chu:Phys. Rev. Lett., 1987, vol. 58, pp. 908–10.
R. S. Roth, K. L. Davis, and J. R. Dennis:Adv. Ceram. Mater., 1987, vol. 2 (3B), pp. 303–12.
K. G. Frase and D. R. Clarke:Adv. Ceram. Mater., 1987, vol. 2 (3B), pp. 295–302.
G. Wang, S. J. Hwu, S. N. Song, J. B. Ketterson, L. D. Marks, K. R. Poeppelmeier, and T. O. Mason:Adv. Ceram. Mater., 1987, vol. 2 (3B), pp. 313–19.
K. Osamura, W. Zhang, T. Yamashita, S. Ochiai, and Bruno Predel:Z. Metallkde., 1988, vol. 79, pp. 693–95.
R. S. Roth, C. J. Rawn, J. D. Whitler, C. K. Cjiang, and W. K. Wong-Ng:J. Am. Ceram. Soc, 1989, vol. 72 (3), pp. 395–99.
W. Zhang, S. Ochiai, and K. Osamura: Proc. Annu. Meeting JIM, Apr. 1989, p. 398.
M. Arjomand and D. J. Machin:J. Chem. Soc, Dalton Trans., 1975, pp. 1061–66.
T. Ishiguro, N. Ishizawa, N. Mizutani, and M. Kato:J. Solid State Chem., 1983, vol. 49, pp. 232–36.
R. Vogel and W. Pocher:Z. Metallkd., 1929, vol. 21, pp. 333–37 and 368-71.
A.M.M. Gadalla, W.F. Ford, and J. White:J. Trans. Brit. Ceram. Soc, 1963, vol. 62, pp. 45–66.
H.S. Roberts and F.H. Smyth:J. Am. Chem. Soc, 1921, vol. 43, pp. 1061–81.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhang, W., Osamura, K. Phase diagram of Cu2O-CuO-Y2O3 system in air. Metall Trans A 21, 2243–2248 (1990). https://doi.org/10.1007/BF02647886
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02647886