Abstract
A new type of precipitate (designated L-J phase) with two variants was observed within the (DO3 + L21) matrix in a Cu2.2Mn0.8Al alloy. Transmission electron microscopy examinations indicated that the L-J phase has an orthorhombic structure with lattice parametersa = 0.413 nm,b = 0.254 nm andc = 0.728 nm. The orientation relationship between the L-J phase and the matrix is (100)L-J//(011) m , (010)L-J//(111) m and (001)L-J//(211) m . The rotation axis and rotation angle between two variants of the L-J phase are [021] and 90 deg. The L-J phase has never been observed in various Cu-Al, Cu-Mn, and Cu-Al-Mn alloy systems before.
Similar content being viewed by others
References
M. Bouchard and G. Thomas:Acta Met., 1975, vol. 23, pp. 1485–500.
Ye.G. Nesterenko, I.A. Osipenko, and S.A. Firstov:Fiz. Metal. Metalloved., 1969, vol. 27, pp. 135–40.
Ye.G. Nesterenko, I.A. Osipenko, and S.A. Firstov:Fiz. Metal. Metalloved., 1969, vol. 28, pp. 987–92.
Ye.G. Nesterenko, I.A. Osipenko, and S.A. Firstov:Fiz. Metal. Metalloved., 1973, vol. 36, pp. 702–10.
V.P. Zalutskiy, Ye.G. Nesterenko, and I.A. Osipenko:Fiz. Metal. Metalloved., 1970, vol. 28, pp. 627–33.
Ye.G. Nesterenko and I.A. Osipenko:Fiz. Metal. Metalloved., 1973, vol. 36, pp. 1212–18.
R. Kozubski and J. Soltys:J. Mater. Sci. Lett., 1983, vol. 2, pp. 141–43.
B. Dubois and D. Chevereau:J. Mater. Sci., 1979, vol. 14, pp. 2296–302.
R. Kozubski and J. Soltys:J. Mater. Sci., 1982, vol. 17, pp. 1441–46.
R. Kozubski and J. Soltys:J. Mater. Sci., 1983, vol. 18, pp. 1689–97.
T. Yamane, H. Okamoto, and J. Takahashi:Z. Metallkde., 1980, vol. 71, pp. 813–17.
R. Kozubski, J. Soltys, and R. Kuziak:J. Mater. Sci., 1983, vol. 18, pp. 3079–86.
R. Kozubski, J. Soltys, J. Dutkiewicz, and J. Morgiel:J. Mater. Sci., 1987, vol. 22, pp. 3843–46.
J. Soltys, M. Stefaniak, and J. Holender:Phil. Mag., 1984, vol. 49B, pp. 151–58.
M.G. Mendiratta, S.K. Ehlers, and H.A. Lipsitt:Metall. Trans. A, 1987, vol. 18A, pp. 509–18.
E. Persson:Z. Physik, 1929, vol. 57, pp. 115–33.
D.P. Oxley, R.S. Tebble, and K.C. Williams:J. Appl. Phys., 1963, vol. 34, pp. 1362–64.
W. Vandermeulen and A. Deruyttere:Metall. Trans., 1973, vol. 4, pp. 1659–64.
A.T. Balcerzak and S.L. Sass:Metall. Trans., 1972, vol. 3, pp. 1601–05.
D. Srivastava, P. Mukhopadhyay, E. Ramadasan, and S. Banerjee:Metall. Trans. A, 1993, vol. 24A, pp. 495–501.
W.G. Brammer, Jr. and C.G. Rhodes:Phil. Mag., 1967, vol. 16, pp. 477–86.
R. Strychor and J.C. Williams:Solid → Solid Phase Transformations, AIME, Warrendale, PA, 1982, pp. 249–53.
K. Otsuka, H. Sakamoto, and K. Shimizu:Trans. JIM, 1979, vol. 20, pp. 244–54.
K. Otsuka, H. Sakamoto, and K. Shimizu:Metall. Trans. A, 1981, vol. 12A, pp. 595–605.
Y. Murakami, L. Delaey, and G.S. Dullenkopf:Trans. JIM, 1978, vol. 19, pp. 317–25.
M. De Bondt and A. Deruyttere:Acta Met., 1967, vol. 15, pp. 993–1005.
L. Delaey, A.J. Perkins, and T.B. Massalski:J. Mater. Sci., 1972, vol. 7, pp. 1197–215.
J.W. Edington:The Operation and Calibration of the Electron Microscope, 1985, vol. 1, pp. 80–81.
J.W. Edington:The Operation and Calibration of the Electron Microscope, 1985, vol. 1, pp. 42–43.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jeng, S.C., Liu, T.F. L-J phase in a Cu2.2Mn0.8Al alloy. Metall Mater Trans A 26, 1353–1365 (1995). https://doi.org/10.1007/BF02647586
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02647586