Abstract
The superplasticity of the Ti- 6Al- 6V- 2Sn alloy for different temperatures was evaluated by single-sheet free blowing. The optimal superplastic temperature for the Ti- 6Al- 6V- 2Sn alloy was found to be 850 °C. Diffusion bonding of Ti- 6Al- 6V- 2Sn and 304 stainless steel was carried out in a vacuum. The interface of both bonded alloys was examined by EPMA. The concentration profile of Ni exhibited a peak at the interlayer and a valley adjacent it, whereas that of Cr exhibited a peak where Ni showed the valley. X- ray diffraction (XRD) analyses showed that the Fe 2 Ti, NiTi, and CrMn Intermetallic compounds and the Cr element formed at the interface. The thickness profiles of the blown specimens were measured and compared with theoretical calculations.
Similar content being viewed by others
References
A. Arieli and A. Rosen,Metall. Trans. A, Vol 8 (No. 10), 1977, p 1591
H.E. Friedrich, R. Furlan, and M. Kullick, Superplastic Forming/Diffusion Bonding on the Way to the Production Stage for Ti and Al,Proc. Conf. on Superplasticity and Superplastic Forming, C.H. Hamilton and N.E. Paton, Ed., Blaine, Aug 1988, The Metallurgical Society of AIME, 1988, p 649
R.C. Davis, D.M. Royster, and T.T. Bales, Superplastically Formed Titanium Hat-Stiffened Panels,NASA Tech. Briefs, Vol 14 (No. 1), 1990, p 63–64
A.R. Ragab,Met. Technol., Vol 10, 1983, p 340
H. Kato, M. Shibata, and K. Yoshikawa,Mater. Sci. Technol., Vol 2, 1986, p 405
S. Hinotani,The Sumitomo Search, No. 44, Dec 1990, p 346
B. Aleman, I. Gutierrez, and J.J. Urcola,Mater. Sci. Technol., Vol 9, 1993, p 633
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shyu, J., Chuang, T. Diffusion bonding/superplastic forming of Ti-6Al-6V-2Sn/SUS 304 stainless steel/Ti-6Al-6V-2Sn. JMEP 5, 84–88 (1996). https://doi.org/10.1007/BF02647274
Issue Date:
DOI: https://doi.org/10.1007/BF02647274