Abstract
Mixed mode I/III toughness tests were performed on a Ni-Cr-Mo-V rotor steel that exhibited very high mode I toughness. The minimum toughness occurred under mixed mode loading conditions. The influence of mode III loading on total toughness is analyzed in terms of incompatibility effects at particles ahead of the crack tip.
Similar content being viewed by others
References
M. Yoda:Eng. Fract. Mech., 1979, vol. 13, pp. 647–56.
R. C. Shah: ASTM STP 560, ASTM, Philadelphia, PA, 1974, pp. 29-52.
N. Tsangarkis:Eng. Fract. Mech., 1984, vol. 19, pp. 903–09.
E. K. Tschegg and S. Suresh:Metall. Trans. A, 1988, vol. 19A, pp. 3035–44.
M. T. Miglin, J. P. Hirth, and A. R. Rosenfield:Int. J. Fract., 1983, vol. 22, pp. R65–67; M. T. Miglin, I.H. Lin, J.P. Hirth, and A. R. Rosenfield: ASTM STP 791, ASTM, Philadelphia, PA, 1984, pp. 11-353-69.
Z. H. Liu and W. Shen:Int. J. Tract., 1984, vol. 25, pp. R21–29.
J. G. Schroth, J. P. Hirth, R. G. Hoagland, and A. R. Rosenfield:Metall. Trans. A, 1987, vol. 18A, pp. 1061–72; J. G. Schroth, R. G. Hoagland, J. P. Hirth, and A. R. Rosenfield:Scripta Metall., 1985, vol. 19, pp. 215-19.
M. Manoharan, J. P. Hirth, and A. R. Rosenfield:Scripta Metall., 1989, vol. 23, pp. 763–66 and 1647.
L. P. Pook:Eng. Fract. Mech., 1971, vol. 3, pp. 205–18.
A. R. Rosenfield and W. H. Duckworth:Int. J. Fract., 1987, vol. 32, pp. R59–62.
U. S. Suresh and E. K. Tschegg:J. Am. Ceram. Soc, 1987, vol. 70, pp. 726–33.
Y. Ueda, K. Ikeda, T. Yao, and M. Aoki:Eng. Fract. Mech., 1983, vol. 18, pp. 1131–58.
G. T. Hahn, M. F. Kanninen, and A. R. Rosenfield:Annu. Rev. Mater. Sci., 1972, vol. 2, pp. 381–404.
K. A. Taylor: Bethlehem Steel Corporation, Bethlehem, PA, pri-vate communication, 1987.
M. Manoharan, J. P. Hirth, and A. R. Rosenfield:J. Test. Eval., 1990, vol. 18, pp. 106–14.
A. R. Rosenfield: Report No. AFML-TR-74-129, Part I, Appen-dix J, Air Force Materials Laboratory, Dayton, OH, 1974.
Annual Book of ASTM Standards, ASTM, Philadelphia, PA, 1988, vol. 03-01, pp. 686-700.
K. H. Schwalbe and D. Hellman:J. Test. Eval., 1981, vol. 9, pp. 218–21.
J.R. Rice, P.C. Paris, and J.G. Merkle: ASTM STP 536, ASTM, Philadelphia, PA, 1973, pp. 231-45.
J.G. Merkle and H.T. Corten:J. Pressure Vessel Technol., 1974, vol. 96, pp. 286–92.
P.C. Paris, H. Tada, A. Zahoor, and H. Ernst: ASTM STP 668, ASTM, Philadelphia, PA, 1979, pp. 5-36.
R. L. Bodnar: Bethlehem Steel Corporation, Bethlehem, PA, pri-vate communication, Oct. 1988.
M. Tanaka: Japan Steel Works, Muroran, Japan, private com-munication, Nov. 1988.
T. Goldenberg, T. D. Lee, and J. P. Hirth:Metall. Trans. A, 1978, vol. 9A, pp. 1663–71.
O. A. Onyewuenyi and J. P. Hirth:Metall. Trans. A, 1982, vol. 13A, pp. 2209–18.
S. C. Chang and J. P. Hirth:Metall. Trans. A, 1985, vol. 16A, pp. 1417–25.
V. B. Rajan and J. P. Hirth:Metall. Trans. A, 1987, vol. 18A, pp. 335–40.
C.F. Shih: ASTM STP 560, ASTM, Philadelphia, PA, 1974, pp. 187–210.
J. R. Rice: inMechanics of Solids, H.G. Hopkins and M. J. Sewell, eds., Pergamon, Oxford, 1982, pp. 539–62.
F.A. McClintock:J. Appl. Mech., 1958, vol. 25, pp. 582–88.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Raghavachary, S., Rosenfield, A.R. & Hirth, J.P. Mixed mode I/III fracture toughness of an experimental rotor steel. Metall Trans A 21, 2539–2545 (1990). https://doi.org/10.1007/BF02646999
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02646999