Abstract
The glassy precursors were fabricated by quenching the melted materials with copper plates. In the case of heating the properties of the quenched samples were changed, because as a result of solid-state reactions formation of cuprate occurs. The amorphous samples were annealed in air and transformed to the crystalline state. This process can be seen by DTA and electric resistivity behaviours. The microscopic observation of the polished surfaces show the growth of the superconducting phase Bi2Sr2CaCu2O8+x (for composition Bi-2212) and Bi2Sr2CaCu2O8+x with Bi2Sr2Ca2Cu3O10+x (for composition Bi-2223 and Bi-2234), respectively.
Zusammenfassung
Glasartige Bi-Vorstoffe werden durch Abschrecken geschmolzener Materialien mit Cu-Platten hergestellt. Beim Aufheizen ändern sich die Eingenschaften der Gläser, da Reaktionen zum Cuprat-Aufbau stattfinden. Die Proben nehmen Sauerstoff auf und wandlen sich vom amorphen in den kristallinen Zustand um, was in den DTA- und Widerstands-Kurven erkennbar ist. Mikroskopische Beobachtungen veranschaulichen den Aufbau der supraleitenden Phasen Bi2Sr2CaCu2O8+x (für die Zusammensetzung Bi-2212) und Bi2Sr2CaCu2O8+x sowie Bi2Sr2Ca2Cu3O10+x (für die Zusammensetzungen Bi-2234 und Bi-2223).
Similar content being viewed by others
References
J. Bock und S. Elschner, E. Preisler, Third International Symposium on Superconductivity, Nov. 6–9, 1990, Sendei.
Y. Abe, H. Hosono, W.-H. Lee, M. Hosoe, K. Nakamura und E. Inukai, J. Mater. Res., 8 (1993) 1.
J. Plewa, H. Altenburg, J. Hauck und D. Trinschek, Thermochim. Acta, 216 (1993) 229.
J. Plewa, G. J. Schmitz, E. Preisler und H. Altenburg, J. Thermal Anal. 39 (1993) 669.
T. Komatsu und K. Matushita, Thermochim. Acta, 174 (1991) 131.
M. De Guire, N. Bansal, D. Farell, V. Finan, C. Kim, B. Hills und C. Allen, Physica, C 179 (1991) 336.
P. Murphy, Differential Thermal Analysis, Academic Press, R. Mackenzie (Ed.), London 1972 p. 645.
A. E. Owen, Amorphous Solids and the Liquid State, N. H. March, R. A. Street, M. Tosi (Eds.), Plenum Press, New York 1986, p. 395.
E. Rössler, J. Non-Crystall. Solids, 131 (1991) 242.
F. Munakata, T. Kawano, A. Nozaki und H. Zamauchi, J. Appl. Phys. 67 (1990) 4159.
L. Plomp, A. Booy, J. A. M. van Roosmalen und E. H. P. Cordfunke, Rev. Sci. Instrum., 61 (1990) 1949.
H. Takagi, B. Batlogg, H. L. Kao, J. Kwo, R. J. Cava, J. J. Krajewski und W. F. Peck, Jr., Phys. Rev. Lett., 69 (1992) 2975.
S. Elschner, W. Becker, H. Bestgen und M. Brand, Physica C, 202 (1992) 401.
T. Ohtani, T. Okudo, A. Tamaki und T. Ueda, Jpn. J. Appl. Phys. 27 (1988) L61.
Y.-X. Chen, J. Zhang und Z. Wu, Supercond. Sci. Technol., 5 (1992) 427.
T. Komatsu, R. Sato, Y. Kuken und K. Matusita, J. Am. Ceram. Soc., 76 (1993) 2795.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Plewa, J., Cherepov, S., Kohler, D. et al. Umwandlungen glasförmiger BSCCO-Vorstoffe in den kristallinen Zustand. Journal of Thermal Analysis 45, 395–403 (1995). https://doi.org/10.1007/BF02548773
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02548773