Abstract
Several properties of glass fibre-reinforced polymer-modified cement composites, such as strength, durability, fatigue, creep, shrinkage, freeze-thaw resistance, permeability, thermal movements and fire resistance are described.
The results obtained are mainly for glass fibre-reinforced cement containing five per cent by volume of E-glass fibres in an ordinary Portland cement/sand mixture with fifteen per cent by volume of polymer. Other composites are also considered. To indicate long-term behaviour, results of accelerated ageing tests are presented.
Résumé
Des recherches effectuées au Laboratoire Central de D.S.M. ont abouti en 1975 à la mise au point d'un ciment renforcé de fibres de verre et modifié au polymère (PGRC). Ce nouveau matériau est commercialisé depuis 1979.
Le PGRC est constitué de fibres de verre E, ciment, agrégats et d'un polymère: Le polymère est mélangé au ciment et aux granulats sous forme d'une dispersion aqueuse. Le polymère qui s'infiltre dans l'espace compris entre les filaments constitués par les faisceaux de fibres de verre, y forme un film qui protège le verre contre les agressions physiques et chimiques.
Le PGVC est caractérisé par un vieillissement beaucoup moins prononcé que le GVC renforcé au verre E ou AR.
Depuis la mise au point du PGVC une étude approfondie a été effectuée pour en déterminer les propriétés, et cet article a pour objet de donner un aperçu des résultats les plus importants de cette étude des propriétés mécaniques, de la durabilité et des propriétés physiques les plus intéressantes du PGVC.
Les propriétés mécaniques traitées ici sont: la résistance à la traction, résistance à la traction en flexion, résistance au cisaillement interlaminaire et résistance à la pression ainsi que les propriétés de fluage et de fatique.
Le comportement au vieillissement du PGVC a été examiné dans différentes conditions: en milieu sec (20°C et 65% R.H.), humide [immergé en eau saturée de Ca(OH)2 à 20°C], sous exposition à l'air et dans les conditions de vieillissement accélérées. Les critères retenus dans les essais de durabilité ont été la résistance à la traction en flexion et la résistance au choc.
Cette étude met en évidence la meilleure résistance au vieillissement du PGVC par comparaison avec le GVC.
L'influence des variations de formule sur les propriétés du PGVC, entre autres l'influence de la concentration en verre, de la teneur en polymère et du rapport granulatciment est indiquée.
Pour conclure l'analyse des propriétés du PGVC, on donne un aperçu des propriétés physiques suivantes: retrait de séchage, gonflement à l'humidité, porosité, absorption d'eau, perméabilité à la vapeur d'eau, coefficient de dilatation thermique, conductibilité thermique et électrique, résistance au gel-dégel et comportement au feu.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Bijen J.—E-glass fibre reinforced polymer modified cement. Proceedings Congress, The developing Success of GRC, London, October 1979.
Bijen J.—New developments in the field of glass-fibrereinforced cement, polymer-modified, glass fibre-reinforced cement, Cement 3, 1980.
Brouwer J. B., Bijen J.—Possible applications of Forton glass-fibre-reinforced cement in building construction, 1980, Bouw 22, '80, pp. 40–41.
Bijen J.—Glass fibre reinforced cement; improvements by polymer addition, Proceedings Advanced Cement Composites, Symposium American Material Society Annual Meeting, Boston Mass., November 1980. Materials Research Society, pp. 239–249. Mat. Res. Soc. University Park PA 16802, pp. 239–249.
Oosterhof R. G.—An alternative glass-fibre-reinforced material, Symposium Reinforplast 80, Brussels, 27–28 May 1980.
Proctor B. A.—Properties and performance of GRC, Concrete International '80, Fibrous concrete, April 80, pp. 69–86.
Recommended practice for glass-fibre-reinforced concrete panels. J. Prestressed Concrete Institute PCI, Vol. 26, No. 1, Jan.–Feb. 1981.
Prender M., Maenning W.—Zur Problematik der Dauerschwingfestigkeit metallischer Werkstoffe Eng. Fracture Mechanics, Vol. 8, 1976, pp. 39–67.
Aveston J., Cooper G.A., Kelly A.—Conf. Proc. Properties of fibre Composites, Nat. Phys. Lab., No. 1971, pp. 15–26.
Dingley R.G.—The structure and properties of hydraulic cement pastes modified by polymer latex, Thesis Un. of Southampton, April 1974.
Bartos P.—Analysis of the pull-out tests on fibres embedded in brittle matrices. J. Mat. Sci., Vol. 15, 1980, pp. 3122.
Singh B., Walton P.L., Stucke M.S.—Test methods used to measure the mechanical properties of fibre cement composites at the Building Research Establishment, RILEM symp. 1978 ed. R. W. Swamy, Constr. Press. Ltd, pp 377–387.
Litherland K.L., Oakley D.R., Proctor B.A.—The use of accelerated ageing, procedures to predict the longterm strength of GCR composites, Proceedings Advanced Cement Composites, Symposium American Material Society Annual Meeting. Boston Mass., November 1980. Materials Research Society, pp. 239–249. Mat. Res. Soc. University Park PA 16802, pp. 61–74.
RILEM tentative recommendations, CPC 11.3.Absorption of water by immersion under vacuum.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bijen, J., Jacobs, M. Properties of glass fibre-reinforced polymer-modified cement. Matériaux et Constructions 15, 445–452 (1982). https://doi.org/10.1007/BF02473615
Issue Date:
DOI: https://doi.org/10.1007/BF02473615