Abstract
Phase pure powder and thin films of the novel ferroelectric materials SrBi2Ta2O9 (SBT) have been prepared using the organic precursors. The xero-gel formed was dried and characterized using TGA and DTA to determine the organic burn out and crystallization temperature of SBT. Powder X-ray diffraction was used systematically to check the crystallinity of SBT. Phase pure SBT powder was formed as low as 650°C and thin films at 600°C in comparison to other earlier reported work. SEM micrographs show a grain size of ≈0.1 μm and show crack free films with a film thickness of 2 μm.
Similar content being viewed by others
References
C.A. Paz de Aranjo, J.D. Archiaro, M.C. Scott, and L.D. McMillian, Pattent No. WO 93/12542 (24 June).
K. Amanuma, T. Hase, and Y. Miyasaka, Appl. Phy. Lett.66 221 (1995).
E.C. Subbarao, J. Phys. Chem. Solids23, 665 (1962).
T. Mihara, H. Yoshimura, H. Watanabe, T. Itoh, C. Paz de Arauzo, and L.D. McMillian,7th Inter. Sym. on Integrated Ferroelectrics, Calorado, March 2–22, 1995.
I.G. Ismailzade,Proc. III Conf. on Ferroelectricity (USSR Acad. Sci., USSR, Press, Moscow 1960).
D.C. Bradely, R.C. Mehrotra, and D.O. Gaur,Metal Alkoxides (Academic Press), p. 303.
S.Y. Chen, X.-F. Du, and I.-W. Chen,Mater. Res. Soc. Sym. (1995), vol. 361, p. 15.
K. Amanuma, T. Hase, and Y. Mujaialha,Mater. Res. Soc. Sym. (1995), vol. 361, p. 21.
D.P. Vijay, S.B. Desu, M. Nagata, X. Zhang and Tze. C. Chen,Mater. Res. Soc. Sym. (1995), vol. 361, p. 3.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ravichandran, D., Yamakawa, K., Bhalla, A.S. et al. Alkoxide derived SrBi2Ta2O9 phase pure powder and thin films. J Sol-Gel Sci Technol 9, 95–101 (1997). https://doi.org/10.1007/BF02439340
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02439340