Abstract
The diffusion bonding of a low steel to alumina has been studied in the present work. Thin foils of a soft metal (copper) were used to reduce the effects of the residual stresses produced in the joint by thermal expansion mismatch. The strength of the joint was found to be influenced by the bonding parameters, but principally by the oxygen content both on the surface and in the copper matrix. The diffusion bonds have been mechanically tested using a three-point bending test. Maximum bending strengths of 100 MPa were achieved by using a 0.1 mm copper foil, and bonding in a oxidizing atmosphere (P O 2=104Pa). SEM and EDS investigations have shown the presence of reaction products in the copper-alumina interface which controls the mechanical properties of the joint.
Similar content being viewed by others
References
E. M. Leone, R. N. Katz andJ. J. Burke (eds), “Ceramics of High-Performance Applications”. Vol III (Plenum, New York, 1979).
M. G. Nicholas andD. A. Mortimer,Mater. Sci. Technol. 1 (1985) 657.
ASM, “Metal Handbook” Vol 2, 9th Edn (American Society of Metals, Metals Park, OH, 1983).
J. F. Lunch, P. G. Ruderer andW. H. Duchkorth,J. Amer. Ceram. Soc. (1966).
W. E. Bordige, R. V. Allen andP. T. Whelan,J. Phys. C 47 (1986) 131.
J. T. Klomp,5 (1970) 501.
Idem. Amer. Ceram. Soc. Bull. 49 (1970) 204.
Idem. Ceram. Bull. 51 (1972) 683.
K. Suganuma, T. Okamoto andK. Kamachi,J. Mater. Sci. 22 (1987) 2702.
K. Suganuma, T. Okamoto, M. Koizumi andM. Shimida,J. Mater. Sci. Lett. 4 (1985) 648.
F. Hatekayama, K. Suganuma andT. Okamoto,J. Mater. Sci. 21 (1986) 2455.
M. G. Nicholas andR. M. Crispin,ibid. 17 (1982) 3347.
G. Yiasemides, Proceedings 2nd International Conference “Diffusion Bonding Applications” Cranfield, 28–24 March, 1990.
F. Calvo, A. Ureña, J. M. Gomez De Salazar, F. Molleda andA. J. Criado,J. Mater: Sci. 23 (1988) 1231.
F. Calvo, A. Urena, J. M. Gomez De Salazar andF. Molleda,J. Mater. Sci. Lett. 8 (1989) 137.
M. Courbiere, G. Trabelsi, D. Treheux, C. Beraud, C. Esnouf andG. Fantozzi, “High Tech Ceramics”, edited by P. Vinconzini (Elsevier, Amsterdam, 1987) p. 2599.
C. Beraud, M. Courbiere, C. Esnouf, D. Juve andD. Treheux,J. Mater. Sci. 24 (1989) 4545.
F. D. Richardson andJ. H. E. Jeffes,Proc. R. Soc. 281 (1957) 1023.
J. P. Newman, T. Zhong andY. A. Chang,Bull. Alloys Phase Diagrams 5 (1984) 2.
K. T. Jakob andC. B. Alcock,J. Amer. Ceram. Soc. 58 (1975) 192.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ureña, A., de Salazar, J.M.G. & Quiñones, J. Diffusion bonding of alumina to steel using soft copper interlayer. J Mater Sci 27, 599–606 (1992). https://doi.org/10.1007/BF02403866
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02403866