Clinical experience has shown that fracture of PMMA-based bone cements is a significant factor in the failure of orthopaedic joint replacements. Earlier studies of the fracture toughness properties of bone cement have been limited to relatively large test specimens — ASTM standard test methods require the use of specimens with dimensions considerably larger that those associated with bone cement in clinical use. In this study, a miniature short-rod specimen was used to measure the fracture toughness (K IC) or two bone cements (Simplex-P and Zimmer LVC). The dimension of our mini specimens approaches the cross-section of bone cements as usedin vivo. The short-rod elastic-plastic fracture toughness test method introduced by Barker was utilized to ascertain the effect of specimen preparation and ageing in distilled water on fracture toughness. Our study indicated that slow hand-mixed specimens possess comparable fracture toughness to centrifuged specimens. After ageing in water, however, centrifuged and slow hand-mixed specimens are more fracture resistant than specimens prepared by mixing the cement quickly. An optimum void content for the bone cements studied was suggested by the experimental results; for Simplex-P bone cement it appeared to be less than 1.6% whereas it was between 1.6 and 3.6% for Zimmer LVC cement. Simplex-P bone cement also showed superior fracture toughness compared to Zimmer LVC cement after storage in water for 60 days at 37° C.
Similar content being viewed by others
References
K. J. BUNDY and R. W. PENN,J. Biomed. Mater. Res. 21 (1987) 773.
M. T. MANLEY, L. S. STERN and J. GURTOWSKI, —ibid.19 (1985) 563.
R. D. BECKENBAUGH and D. M. ILSTRUP,J. B. Jt. Surg. A60 (1978) 306.
T. A. GRUEN, G. M. McNEICE and H. C. AMSTUTZ,Clin. Orthop. Relat. Res. 141 (1979) 17.
M. MARTENS, E. AERNOUDT, P. DEMEESTER, P. DUCHEYNE, J. C. MULIER, R. DELANGH and P. KESTELIJN,Acta Orthop. Scand. 45 (1974) 693.
E. A. SALVATI, V. C. IM, P. AGLIETI and P. D. WILSON Jr,Clin Orthop. 121 (1976) 74.
F. A. WEBER and J. CHARNLEY,J. B. Jt. Surg. B57 (1975) 297.
R. D. CROWINSHIELD and J. R. TOLBERT,J. Biomed. Mater. Res. 17 (1983) 819.
S. RAAB, A. M. AHMED and J. W. PROVAN, —ibid.15 (1981) 159.
R. M. STAUTTER,J. B. Jt. Surg. A64 (1982) 983.
J. F. PARK, A. F. VON RECUM and G. E. GRATZICK,Dev. Artif. Org. 7 (1979) 41.
M. PATERSON, P. FULFORD and R. DENHAM,J. B. Jt. Surg. B68 (1986) 392.
H. C. AMSTUTZ, K. L. MARKOLF, G. M. McNEICE and T. A. GRUEN, in “The Hip” (Mosby, St Louis, 1976).
A. S. CARLSSON, C. F. GENTZ and J. STENPORT,Acta Orthop. Scand. 48 (1977) 650.
S. C. BAYNE, E. P. LAUTENSCHLAGER and C. L. COMPERE,J. Biomed Mater. Res. 9 (1975) 27.
S. SAHA and S. PAL, —ibid.18 (1984) 435.
C. M. RIMNAC and T. M. WRIGHT,Trans. 31st Ann. Meeting Orthop. Res. Soc. 10 (1985) 326.
M. H. STONE, R. WILKINSON and I. G. STOTHER,Trans. 13th Ann. Meeting Soc. Biomater. 10 (1987) 171.
J. R. de WIGN, I. J. J. H. SLOOFF and F. C. M. DRIESSENS,Acta Orthop. Scand. 46 (1975) 38.
M. JASTY, N. F. JENSEN and W. H. HARRIS,Trans. 2nd World Cong. Biomater. 10th Ann. Meet. Soc. Biomater. 7 (1984) 46.
A. S. GREENWALD, A. H. WILDE and M. B. MATEJCZYK,Orthop. Digest. 5 (1977) 16.
C. M. RIMNAC, T. M. WRIGHT and D. L. McGILL,J. B. Jt. Surg. A68 (1986) 281.
D. W. BURKE, E. I. GATES and W. H. HARRIS,Trans. 2nd World Cong. Biomater. 10th Ann. Meéting Soc. Biomater. 7 (1984) 346.
P. C. NOBLE, J. L. JAY, L. J. LINDAHL, J. MALTRY, S. M. DREEBEN and H. S. TULLOS,Trans. 13th Ann. Meeting Soc. Biomater. 10 (1987) 169.
R. L. WIXSON, E. P. LAUTENSCHLAGER and M. NOVAC,Trans. 31st Ann. Meeting Orthop. Res. Soc. 10 (1985) 327.
S. SAHA and L. WARMAN,Trans. 2nd World Cong. Biomater, 10th Ann. Meeting Soc. Biomater. 7 (1984) 48.
D. O. O'CONNOR, D. W. BURKE, J. P. DAVIES and W. H. HARRIS, —ibid.7 (1984) 45.
T. P. HARRIGAN, J. P. DAVIES, D. W. BURKE, D. O. O'CONNOR, J. JASTY and W. H. HARRIS,Trans. 13th Ann. Meeting Soc. Biomater. 10 (1987) 170.
J. P. DAVIES, D. W. BURKE, D. O. O'CONNOR and W. H. HARRIS,J. Orthop. Res. 5 (1987) 366.
D. O. O'CONNOR, D. W. BURKE, J. P. DAVIES and W. H. HARRIS,Trans. 31st Ann. Meeting Orthop. Res. Soc. 10 (1985) 325.
K. C. CHAN, personal communications (1988).
J. P. DAVIES, D. O. O'CONNOR, J. A. GREER and W. H. HARRIS,J. Biomed. Mater. Res. 21 (1987) 719.
J. P. DAVIES, D. O. O'CONNOR and W. H. HARRIS,Trans. 2nd World Cong. Biomater, 10th Ann. Meeting Soc. Biomater. 7 (1984) 47.
P. EYERER and R. JIN,J. Biomed. Mater. Res. 20 (1986) 1057.
E. P. LAUTENSCHLAGER, S. I. STUPP and J. C. KELLER, in “Functional Behaviour of Orthopedic Biomaterials”, Vol. II, “Applications” (CRC, Boca Raton, Florida, 1984) p. 87.
S. A. BROWN and W. L. BARGAR,J. Biomed. Mater. Res. 18 (1984) 523.
W. L. BARGAR, S. A. BROWN, H. A. PAUL, T. VOEGLI, Y. HSEIH and N. SHARKEY,J Orthop. Res. 4 (1986) 86.
A. M. AHMED, R. NAIR, D. L. BURKE and J. MILLER,J. Biomech. Engng 104 (1982) 28.
C. T. WANG and R. M. PILLIAR,J. Mater. Sci. 24 (1989) 2391.
B. POURDEYHIMI, H. D. WAGNER and P. SCHWARTZ, —ibid.21 (1986) 4468.
S. S. HAAS, G. M. BRAUER and G. DICKSON,J. B. Jt. Surg. A57 (1975) 380.
B. E. CAUSTON,J. Dent. Res. 54 (1975) 339.
A. J. C. LEE, R. S. M. LING and S. S. VANGALA,Arch. Orthop. Traumat. Surg. 92 (1978) 1.
F. A. FREITAG and S. L. CANNON,J. Biomed. Mater. Res. 10 (1976) 805.
F. LEDNICKY and Z. PELZBAUER,J. Poylm. Sci. C38 (1972) 375.
P. W. BEAUMONT and R. J. YOUNG,J. Biomed. Mater. Res. 9 (1975) 423.
P. C. NOBLE, S. M. DREEBEN, J. L. JAY and H. S. TULLOS,Trans. 13th Ann. Meeting Soc. Biomater. 10 (1987) 366.
B. E. STUBBS, L. S. METHEWS and D. A. SONSTEGARD,J. B. Jt. Surg. A57 (1975) 317.
R. G. HILL, J. F. BATES, T. T. LEWIS and N. REES,J. Mater. Sci. 19 (1984) 1904.
R. G. HILL, J. F. BATES, T. T. LEWIS and N. REES,Biomater. 4 (1983) 112.
J. SHEN, C. C. CHEN and J. A. SAUER,Polymer. 26 (1985) 511.
G. M. BRAUER and W. T. SWEENEY,Modern Plastics May (1955) 144.
C. C. CHEN, J. SHEH and J. A. SAUER,Polymer 26 (1985) 89.
D. T. TURNER, —ibid.23 (1982) 197.
C. MILIARESI, L. NICODENO, L. NICOLAIS and P. PASSENINI,J. Biomed. Mater. Res. 18 (1984) 137.
D. J. LAMB and B. ELLIS, British Division IADR Conference, paper 166 (1981).
C. T. WANG and R. M. PILLIAR, Bachelor Thesis, University of Toronto (1986).
R. P. KUSY,J. Biomed. Mater. Res. 12 (1978) 271.
D. C. SMITH,Br. Dent. J. 111 (1961) 9.
W. ROSTOKER, P. LEREIM and J. O. GALANTE,J. Biomed. Mater. Res. 13 (1979) 365.
M. A. LOONEY and J. B. PARK, —ibid.20 (1986) 555.
J. J. BENBOW,Proc. Phys. Soc. B78 (1961) 970.
A. S. HARGREAVES,J. Biomed. Mater. Res. 15 (1981) 757.
R. M. PILLIAR, R. VOWLES and D. F. WILLIAMS, —ibid.21 (1987) 145.
R. M. PILLIAR, D. C. SMITH and B. MARIC,J. Dental. Res. 65 (1986) 1308.
W. R. KRAUSE and R. S. MATHIS,Trans. 2nd World Cong. Biomater., 10th Ann. Meeting Soc. Biometer. 7 (1984) 349.
E. I. GATES, D. R. CARTER and W. H. HARRIS,Clin. Orthop. 189 (1984) 294.
S. C. WEBER and W. L. BARGAR,Biomater. Med. Dev. Art. Org. 11 (1983) 3.
R. P. ROBINSON, T. M. WRIGHT and A. H. BURSTEIN,J. Biomed. Mater. Res. 15 (1981) 203.
C. F. STARK, —ibid.13 (1979) 339.
G. C. SIH and A. T. BERMAN —ibid.4 (1980) 311.
T. M. WRIGHT and P. S. TRENT,J. Mater. Sci. 14 (1979) 503.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wang, C.T., Pilliar, R.M. Fracture toughness of acrylic bone cements. J Mater Sci 24, 3725–3738 (1989). https://doi.org/10.1007/BF02385763
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02385763