Abstract
The formation of substitutional solid solutions of the isostructural oxyhydroxides α-FeOOH-α-AlOOH (goethite-diaspore and γ-FeOOH-γ-AlOOH (lepidocrocite-boehmite) was investigated by X-ray powder diffraction technique and by thermal analysis.
The unit cell parameters of both orthorhombic structures of α-Fe1−x-AlxOOH (Pbnm) and γ-Fe1−xAlxOOH (Cmcm) decrease clearly with the increase of aluminium content up tox=0.10.
Thermal analysis reveals the sensitivity of DTA and DTG effects to the composition of solid solutions. The temperatures of topotactic formation of rhombohedral α-(Fe, Al)2O3 and of the defect-spinel γ-(Fe, Al)2O3 during the dehydroxylation of α-(Fe, Al)OOH and γ-(Fe, Al)OOH respectively increase as the aluminium concentration rises up to 10 mol%. The dehydration curves of samples with greater aluminium content exhibits the same maximumΔm/ΔT as for the 10 mol% Al-preparation, indicating indirectly the end-members of the solid solution ranges.
Zusammenfassung
Mittels Röntgendiffraktion und Thermoanalyse wurde die Bildung von Substitutions-Mischkristallen der isostrukturellen Oxyhydroxide α-FeOOH-α-AlOOH (Goethit-Diaspor) und γ-FeOOH-γ-AlOOH (Lepidokrokit-Böhmit) untersucht. Die Elementarzellenparameter beider rhombischer Strukturen von α-Fe1−xAlxOOH (Pbnm) und γ-Fe1−xAlxOOH (Cmcm) werden mit zunehmenden Aluminiumgehalt bis zux=0.10 eindeutig kleiner.
Thermoanalyse zeigt die Empfindlichkeit von DTA- und DTG-Effekten gegenüber der Zusammensetzung der Mischkristalle. Steigt die Aluminiumkonzentration bis 10 mol% an, so erhöhen sich auch die Temperaturen für die topotaktische Bildung von rhomboedrischem α-(Fe,Al)2O3 und des Defekt-Spinells γ-(Fe,Al)2O3 bei der Dehydroxylierung von α-(Fe,Al)OOH und γ-(Fe,Al)OOH. Die Dehydratationskurven von Proben mit einem größeren Aluminiumgehalt zeigen dasselbe Δm/ΔT-Maximum wie für die Proben mit 10 mol%, was indirekt auf die Grenze des Mischkristallbereiches deutet.
Similar content being viewed by others
References
D. G. Schulze, Clays Clay Miner., 32 (1984) 36.
J. M.de Villiers and T. H.van Rooyen, Clay Miner., 7 (1967) 229.
E. Wolska, Mater.Sci., Forum, 62–64 (1990) 621.
U. Schwertmann and E. Wolska, Clays Clay Miner., 38 (1990) 209.
E. Wolska and U. Schwertmann, Z.Kristallogr., 189 (1989) 223.
E. Wolska and W. Szajda, Solid State Ionic, 28–30 (1988) 1320.
M. H. Francombe and H. P. Rooksby, Clay Miner. Bull., 4 (1959) 1.
G. Brown, Associated Minerals, Crystal Structures of Clay Minerals and their X-ray Identification (Eds. G. W. Brindley, G. Brown), Mineralogical Sociery, London 1984, pp. 361–407.
J. D. Bernal, D. R. Dasgupta and A. L. Mackay, Nature, 180 (1957) 645.
E. Wolska and J. Baszynski, Phys.Stat.Sol.(a), 95 (1986) 87.
E. Wolska and W. Szajda, J.Thermal Anal., 32 (1987) 797.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wolska, E., Szajda, W. & Piszora, P. Determination of solid solution limits based on the thermal behaviour of aluninium substituted iron hydroxides and oxides. Journal of Thermal Analysis 38, 2115–2122 (1992). https://doi.org/10.1007/BF01979624
Issue Date:
DOI: https://doi.org/10.1007/BF01979624