The effect of procedural variables on TG, DTG and DTA curves of magnesite and dolomite

Abstract

TG, DTG and DTA curves of magnesite are dependent on procedural variables, especially sample mass, heating rate and partial pressure of carbon dioxide, in a similar manner to those of calcite [1], although the magnitude of the effect is less for magnesite. The first stage of the decomposition of dolomite varies with increasing partial pressure of carbon dioxide in an anomalous manner and hence the effects of these procedural variables (except heating rate) are not similar to those observed for magnesite and calcite. The second stage of the decomposition of dolomite is, however, strongly dependent on these procedural variables and behaves in a manner that would be predicted for a sample of calcite diluted with magnesia. A 1∶1 molar mixture of magnesite and calcite also behaves as would be predicted from the behaviour of the single carbonates but differently from that of dolomite.

Zusammenfassung

TG-, DTG- und DTA-Kurven von Magnesit sind Ähnlich wie bei Kalzit [1] abhÄngig von den Versuchsparametern, besonders von Probenmasse, Aufheizgeschwindigkeit und Partialdruck von Kohlendioxid, obwohl das Ausma\ dieses Einflusses bei Magnesit geringer ist. Der erste Schritt der Zersetzung von Dolomit Ändert sich in einer ungewöhnlichen Weise durch Erhöhung des Partialdruckes von Kohlendioxid und deshalb unterscheidet sich der Einflu\ dieser Versuchsparameter (mit Ausnahme der Probenmasse) von dem, der bei Magnesit und Kalzit beobachtet wurde. Der zweite Schritt bei der Zersetzung von Dolomit ist stark von diesen Versuchsparametern abhÄngig und verlÄuft so, wie man es für eine mit Magnesia verdünnte Kalzitprobe voraussagen würde. Eine Gemisch aus Magnesit und Kalzit im VerhÄltnis 1∶1 verhÄlt sich ebenso, wie man es auf Grund des Verhaltens der einfachen Karbonate voraussagen würde, unterscheidet sich jedoch von dem des Dolomits.