Abstract
For the determination of diffusion coefficients by using the model “diffusion into a plate” methodical examinations were carried out on samples of austenitic steel that had been nitrided in their marginal zones for 1.5 h at 1523 K.
For recording of the concentration of N as a function of the distance from the surface electron-probe microanalysis (EPMA) and the precision determination of the lattice parameters by Kossel technique were applied. Both methods yield comparable results.
Similar content being viewed by others
References
A. Kühl, D. Bergner, H.-J. Ullrich, M. Schlaubitz, P. Karduck,Mikrochim. Acta 1992,107, 295.
S. Baumgartl, et al.,Steel research 1989,60, 12, 571.
A. Freissmuth,Berg- und Hüttenmänn. Mitt. 1967,112, 197.
T. Bell, D. Kumar,Metals Technologie 1978,5, 293.
J. E. Iruman,Stainless Steel Ind. 1978,6, 21.
H.-J. Ullrich, G. E. R. Schulze,Kristall und Technik 1972,7, 207.
P. Ettmayer, H. Priemer, R. Kieffer,Metall 1969,23, 4, 307.
H.-J. Ullrich,Abhandlungen des Museums für Mineralogie und Geologie zu Dresden 1982,31, 7.
J. Bauch, H.-J. Ullrich, T. Kuttner,Wiss. Z. Techn. Univ. Dresden 1990,39, 1, 6.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ullrich, HJ., Schlaubitz, M., Bauch, J. et al. On the determination of low nitrogen concentration gradients in austenitic CrNi(Mo) steels. Mikrochim Acta 107, 329–335 (1992). https://doi.org/10.1007/BF01244488
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01244488