Abstract
The composition of the gamma phase in equilibrium with tungsten carbide has been experimentally determined at 1723 K by use of the electron microprobe. The systems studied are the ternary TiC-TaC-WC, TiC-NbC-WC, NbC-TaC-WC systems and the quaternary TiC-NbC-TaC-WC system at two TaC/NbC ratios.
Similar content being viewed by others
References
C. Chatfield,Powder Met. Int. 2 (1983) 18.
E. E. Underwood,“Quantitative Stereology” (Addison-Wesley, Massachusetts, 1970).
B. Uhrenius,CALPHAD 8 (1984) 101.
E. Rudy,J. Less Common Metals 33 (1973) 245.
W. May,Techn. Mitt. Krupp 30 (1972) 15.
I. N. Chaporova andR. F. Cheburaeva,Naucnye trudy VNIITS (12) (1973) 78.
E. Rudy, “Ternary Phase Equilibria in Transition Metal-Boron-Carbon-Silica Systems”, Part V (Air Force Materials Laboratory, Wright-Patterson AFB, Ohio, USA, 1969).
D. R. F. West, “Ternary Equilibrium Diagrams” (MacMillan, London, 1963) p. 5.
T. Johansson andB. Uhrenius,Met. Sci. 12 (1978) 83.
E. Krainer andJ. Robitsch,Planseeberf.Pulver. 15 (1967) 46.
M. Hellsing, A. Henjered, H. Nordén andH-O Andrén, in “Science of Hard Materials”, edited by R. K. Viswanadham, D. J. Rowcliffe and J. Gurland (Plenum, New York, London, 1983) p. 931.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chatfield, C. The gamma/WC solubility boundary in the quaternary TiC-NbC-TaC-WC system at 1723 K. J Mater Sci 21, 577–582 (1986). https://doi.org/10.1007/BF01145526
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01145526