Abstract
A new process, which is a combination of electrophoretic deposition and pack cementation, was used to obtain MCrAlY overlay-type coatings. Using the electrophoretic-deposition process, rare-earth element is added to the deposits by using a special additive which contains yittrium, and excellent high-temperature corrosion resistance was observed after pack cementation.
Similar content being viewed by others
References
D. H. Boone,Mater. Sci. Technol. 2, 220 (1986).
J. E. Restall and M. I. Wood,Mater. Sci. Technol. 2, 225 (1986).
F. J. Honey, E. C. Keward, and V. Wride,J. Vac. Sci. Technol. A 4(6), 2593 (1986).
R. Mevrel,Mater. Sci. Eng. A 120, 13 (1989).
M. Ortner,Plating 51, 885 (1960).
J. Huminik, Jr., (ed.),High-Temperature Inorganic Coatings (Reinhold, New York, 1963).
Aluminium coating of steel,Metal Treat. Drop Forging 70, 763 (1961).
R. Morbioli,Mater. Sci. Eng. A 120/121, 373 (1989).
High-Temperature Oxidation-Resistant Coatings, Committee on Coatings, National Materials Advisory Board, Division of Engineering, National Research Council, National Academy of Sciences, National Academy of Engineering, Washington DC, 1970.
F. S. Pettit and W. Goward, inCoating for High Temperature Applications E. Lang ed. (Applied Science, London and New York, 1983), p. 341.
Xinying Lu, Ph.D. thesis, Chapter 5, University of Science and Technology Beijing (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lu, X., Zhu, R. & He, Y. Electrophoretic deposition of MCrAlY overlay-type coatings. Oxid Met 43, 353–362 (1995). https://doi.org/10.1007/BF01047035
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF01047035