Untersuchungen über die Polymorphic der VerbindungenLn ₃NbO₇

Abstract

In systems consisting of α-Nb₂O₅ and the oxides of the rare earthsLn ₂O₃ (Ln= La to Dy), a compound of formulaLn ₃NbO₇ occurs.

This compound shows polymorphous transitions, the number and temperature range for the existence of which depend on the particular lanthanide.

IfLn=La, Nd, Sm, the structure possesses orthorhombic symmetry at 1300⁰. Above this temperature a monoclinic intermediate form is observed, and in the region of the melting point a cubic fluorite-type structure-with the exception of the lanthanum compound, where this last form seems not to exist.

WhenLn=Eu, Gd, only the monoclinic and cubic forms exist between 1300⁰ and the melting point (≈ 1800°C).

Finally, the dysprosium compound exists only in the cubic fluorite-type phase throughout the whole temperature range.

Zusammenfassung

In den aus α-Nb₂O₅ und den Oxiden der Seltenen ErdenLn ₂O₃ (Ln= La bis Dy) bestehenden Systemen tritt eine Verbindung der FormelLn ₃NbO₇ auf.

Diese Verbindung zeigt polymorphe, Umwandlungen; deren Anzahl und die Lage der Existenzbereiche auf der Temperaturskala hängt von dem beteiligten Lanthanid ab.

IstLn=La, Nd, Sm, so zeigt die Struktur bei 1300⁰ orthorhombische Symmetrie. Oberhalb dieser Temperatur beobachtet man eine monokline Zwischenform und schließlich in der Nähe des Schmelzens eine kubische fluoritartige Struktur—ausgenommen bei Lanthan, bei welchem diese letztere Form nicht zu existieren scheint.

BeiLn-Eu, Gd existieren zwischen 1300⁰ und dem Schmelzpunkt (≈ 1800°C) nur die monokline und die kubische Form.

Schließlich existiert vom Dysprosium an nur die kubische fluoritartige Phase über den ganzen Temperaturbereich.