Abstract
The accumulation of microdamage in specimens of polystyrene, Ftorlon, and high-pressure polyethylene loaded continuously to failure has been investigated. It is shown that at small specimen lifetimes the residual damage accumulates primarily in the fracture zone. Outside the fracture zone appreciable damage accumulation is observed at specimen lifetimes close to the long-term strength. The ultimate strain at various lifetimes is determined. It is shown that the strain corresponding to failure depends on the fraction of irreversible damage accumulated and is largely determined by the resistance of the polymers to fracture.
Similar content being viewed by others
Literature cited
S. N. Zhurkov and N. Narzullaev, Zh. Tekh. Fiz.,23, 1677 (1953).
L. M. Kachanov, Izv. Akad. Nauk SSSR, OTN, No. 8, 26 (1958).
S. N. Zhurkov and É. E. Tomashevskii, Zh. Tekh. Fiz.,27, 1249 (1957).
S. N. Zhurkov, V. S. Kuksenko, and A. I. Slutsker, Fiz. Tverd. Tela,11, 295 (1969).
M. I. Bessonov, Fiz. Tverd. Tela,11, 410 (1969).
V. V. Novozhilov, Prikl. Matem. i Mekhan.,29, 681 (1965).
V. N. Slikhter, Khim. i Tekhnol. Polim., No. 9, 86 (1969).
A. L. Rabinovich, in: Introduction to the Mechanics of Reinforced Polymers [in Russian], Moscow (1970), p. 207.
S. N. Zhurkov, V. S. Kuksenko, and A. I. Slutsker, Fiz. Tverd. Tela,11, 298 (1969).
V. S. Kuksenko and A. I. Slutsker, Fiz. Tverd. Tela,11, 405 (1969).
J. Bailey, Glass. Ind.,20, No. 4, 143 (1939).
S. N. Zhurkov and É. E. Tomashevskii, in: Some Problems of the Strength of Solids [in Russian], Leningrad (1959), p. 68.
A. Ya. Gol'dman, N. F. Savel'eva, and V. I. Smirnov, in: Properties of Polyester Glass-Reinforced Plastics and Methods of Property Control [in Russian], Vol. 2, Leningrad (1970), p. 249.
Additional information
“Plastopolimer” Scientific-Production Association, Leningrad. Translated from Mekhanika Polimerov, No. 3, pp. 519–524, May–June, 1972.
Rights and permissions
About this article
Cite this article
Gol'dman, A.Y., Martynov, M.A. & Il'chenko, P.A. Accumulation of submicroscopic damage in polymers under simple loading. Polymer Mechanics 8, 455–459 (1972). https://doi.org/10.1007/BF00856371
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00856371