Polymer complexes, XXIII: Synthesis and physico-chemical studies on transition metal complexes of symmetric novel poly(N,N′-o-phenylenediamine)-bis(cinnamaldehyde)

Summary

New complexes derived from polymeric N,N′-o-phenylenediamine bis(cinnamaldehyde) (L) with Cu^II, Co^II, Ni^II, Zn^II, UO ^II₂ , and Pd^II were prepared and characterized by elemental analysis, magnetic susceptibilities and spectroscopic (IR, far-IR,¹H-NMR,¹³C-NMR and EPR) studies. A bidentate methine nitrogen atoms coordination of the ligand is assigned in the isolated complexes. The stereochemistries of the polymer complexes have been studied with using magnetic and spectroscopic measurements. Analytical data show 2:1 or 1:1 (ligand:metal) stoichiometry with water molecules coordinated to the Zn^II ion, as evidenced from IR and thermal analysis (DTA). The ligand was tested as a corrosion inhibitor for copper; the limiting concentration of the ligand to give maximum efficiency (60%) is 10⁻³ mol dm⁻³ at 25°C.

Zusammenfassung

Es wurden neue Komplexe von polymerem Poly(N,N′-o-phenylendiamin)bis-(zimtaldehyd) mit Cu(II), Co(II), Ni(II), Zn(II), UO₂(II) und Pd(II) hergestellt und mittels Elementaranalyse, magnetischen Suszeptibilitätsmessungen und spektroskopischen Methoden (IR, far-IR,¹H-NMR,¹³C-NMR und EPR) charakterisiert. Es wurde eine zweizähnige Methin-Stickstoff-Koordination in den Komplexen festgestellt. Die Stereochemie der Polymerkomplexe wurde mittels magnetischer und spektroskopischer Messungen untersucht. Aus den analytischen Daten, mit zusätzlichen Argumenten aus IR und thermischer Analyse (DTA), ergab sich eine 2:1 oder 1:1 (Ligand:Metall)-Stöchiometrie mit an Zn(II) koordinierten Wassermolekülen. Der Ligand wurde als Korrosionsinhibitor für Kupfer getestet: die Grenzkonzentration des Liganden zur maximalen Effizienz (60%) ist 10⁻³ mol dm⁻¹ bei 25°C.