Abstract
Superconducting transition temperatures (T c) were measured for a series of Mo-P-B alloys in the Mo-rich corner of the ternary system. The alloys were studied in two forms: (a) slowly cooled after induction melting, and (b) rapidly quenched in an arc hammer apparatus. The rapid quenching produced an amorphous structure, but most of the alloys also contained some crystalline material, indicating that this system is not conducive to easy glass formation. Ternary slowly cooled crystalline alloys in the concentration range 20 to 30 at % phosphorus and 10 to 20 at % boron had relatively highT c values of 9.6 to 9.9 K; higher than for either the Mo-P or Mo-B binary systems.T c values up to 9.02 K were observed for completely amorphous foils, consistent with the previously reported maximumT c values for amorphous alloys in this system. This remains the highestT c reported for a metallic glass. All of the rapidly quenched foils were brittle.
Similar content being viewed by others
References
M. M. Collver andR. H. Hammond,Phys. Rev. Lett 30 (1973) 92.
G. Bergmann,Phys. Reports 27C (1976) 161.
W. L. Johnson,J. Physique C8 (1980) 731.
C. C. Koch, D. M. Kroeger, J. O. Scarbrough andB. C. Giessen,Phys. Rev. B22 (1980) 5213.
C. C. Koch, J. O. Scarbrough, D. M. Kroeger andA. Dasgupta,Appl. Phys. Lett. 37 (1980) 451.
W. L. Johnson, “Glassy Metals” edited by H. Güntherodt and H. Beck (Springer Verlag, Heidelberg, West Germany, 1980) p. 191.
A. Kramer, W. L. Johnson andC. Cline,Appl. Phys. Lett. 35 (1979) 815.
W. L. Johnson, S. J. Poon, J. Durand andP. Duwez,Phys. Rev. B18 (1978) 206.
O. Meyer,Inst. Phys. Conf. Ser. 28 (1976) 168.
A. Inoue andT. Masumoto,Sci. Rep. Res. Inst. Tohoku Univ. Series A 29 (1981) 305.
D. M. Kroeger, W. A. Coghlan, D. S. Easton, C. C. Koch andJ. O. Scarbrough,J. Appl. Phys. 53 (1982) 1445.
D. M. Kroeger, C. C. Koch andJ. P. Charlesworth,J. Low Temp. Phys. 19 (1975) 493.
A. C. Anderson, C. C. Koch andJ. O. Scarbrough,Phys. Rev. B26 (1982) 1156.
J. J. Engelhardt,ibid. 179 (1969) 452.
R. D. Blaugher, J. K. Hulm andP. N. Yocom,J. Phys. Chem. Sol. 26 (1965) 2037.
C. H. Strudthoff, J. Reichelt andH. C. Freyhardt,Physica 107B (1981) 393.
H. S. Chen andK. A. Jackson, “Metallic Glasses”, edited by J. J. Gilman and H. J. Leamy (American Society for Metals, Metals Park, Ohio, 1978) p. 78.
W. G. Moffatt, “Handbook of Binary Phase Diagrams”, Vol. 1 (General Electric Co., New York, 1981).
G. V. Samsonov andL. L. Vereikin, “Fosfidy” Izdatel. Akad. Nauk Ukr. SSR, Kiev, 1961, reported in F. A. Shunk “Constitution of Binary Alloys”, 2nd Suppl. (McGraw-Hill Book Co., New York, 1969) p. 519.
C. M. Varma andR. C. Dynes, “Superconductivity in d- and f-band Metals”, edited by D. H. Douglass (Plenum Press, New York, 1976) p. 507.
B. Schroeder, W. L. Johnson, C. C. Tsuei, P. Chaudhari andJ. F. Graczyk,AIP Conf. Proc.,31 (1976) 353.
B. Schroeder, W. Grobman, W. L. Johnson, C. C. Tsuei andP. Chaudhari,Sol. State. Commun. 28 (1978) 631.
O. Meyer “Treatise on Materials Science and Technology”, Vol. 18, “Ion Implantation” edited by J. K. Hirvonen (Academic Press, New York, 1980) p. 415.
D. S. Easton, E. H. Henninger, O. B. Cavin andC. C. Koch, to be published.
O. Fischer,Appl. Phys. 16 (1978) 1.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Koch, C.C., Scarbrough, J.O., Kroeger, D.M. et al. Superconductivity in rapidly quenched Mo-P-B alloys. J Mater Sci 18, 759–765 (1983). https://doi.org/10.1007/BF00745574
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00745574