Abstract
The oxidation behavior of SUS430 stainless steel was studied in moist atmospheres\((P_{H_2 O} = 3.4 \times 10^3 Pa, P_{O_2 } = 20 \sim 12.6 \times 10^3 Pa)\) at 873 K. The mass gain during oxidation was measured by using a thermobalance. An abnormal rapid oxidation occurred after an incubation period which increased with increasing oxygen partial pressure. The product on the surface was identified as α-Fe2O3 of whisker-like morphology by X-ray diffraction and scanning electron microscopy. The abnormal oxidation was not observed under high-oxygen partial pressures. The results of the experiments conducted in various atmospheres were analyzed and are discussed.
Similar content being viewed by others
References
C. W. Tuck, M. Odgers, and K. Sachs,Werkst. Korros. 17, 34 (1966).
C. W. Tuck, M. Odgers, and K. Sachs,Corros. Sci. 9, 271 (1969).
P. L. Surman,Corros. Sci. 13, 113 (1973).
J. Baud, A. Ferrier, J. Manenc, and J. Bénard,Oxid. Met. 9, 69 (1975).
A. Rahmel and J. Tobolski,Corros. Sci. 5, 333 (1965).
C. T. Fujii and R. A. Meussner,J. Electrochem. Soc. 111, 1215 (1964).
A. Rahmel and J. Tobolski,Werkst. Korros. 16, 662 (1965).
W. E. Boggs,J. Electrochem. Soc. 118, 906 (1971).
I. Kvernes, M. Oliveira, and P. Kofstad,Corros. Sci. 17, 237 (1977).
R. E. Ruther and S. Greenburg,J. Electrochem. Soc. 111, 1116 (1964).
D. Caplan and M. Cohen,Corrosion 15, 141t (1959).
K. Ledjeff, A. Rahmel, and M. Schorr,Werkst. Korros. 30, 767 (1979).
C. E. Lowell and D. L. Deadmore,Oxid. Met. 7, 55 (1973).
Y. Ikeda and K. Nii,Boshoku Gijutsu (in Japanese) (Corrosion Engineering)31, 156 (1982).
T. Kawasaki, S. Sato, and Y. Ono,Boshoku Gijutsu (in Japanese) (Corrosion Engineering)31, 172 (1982).
H. Fujikawa, Y. Shida, N. Fujino, and J. Murayama,Boshoku Gijutsu (in Japanese) (Corrosion Engineering)31, 164 (1982).
H. Konno, T. Shigekuni, H. Tamura, and M. Nagayama,Boshoku Gijutsu (in Japanese) (Corrosion Engineering)34, 670 (1985).
R. L. Tallman and E. A. Gulbransen,J. Electrochem. Soc. 115, 770 (1968).
K. Honda, T. Atake, and Y. Saito,High Temp. Corros. Adv. Mater. Protect. Coat., Y. Saito, B. Önay, and T. Maruyama, eds. (Elsevier Science Publishers, 1992), p. 67.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Honda, K., Maruyama, T., Atake, T. et al. Oxidation behavior of sus430 stainless steel in moist atmospheres at 873 k. Oxid Met 38, 347–363 (1992). https://doi.org/10.1007/BF00665659
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00665659