Abstract
In bending strength determinations of ceramics, the fracture usually initiates from the tensile surface or the edges. The edge effect could be minimized by carefully rounding off the edges of specimens subjected to four-point bending. The effect of tensile surface polishing, polishing and rounding off the edges, and the acid treatment of the polished surface on the strength of PZT polycrystalline ceramics was determined along with the failure mechanism.
Similar content being viewed by others
References
S. C. Carniglia,J. Amer. Ceram. Soc. 55 (1972) 243.
R. W. Rice,Proc. Brit. Ceram. Soc. 20 (1972) 205.
R. C. Bradt andR. E. Tressler, “Ceramic Microstructures' 76”, Proceedings of the Sixth International Materials Symposium, edited by R. M. Fulrath and J. A. Pask (Westview Press, Boulder, Colorado, 1976) pp. 785–99.
J. A. Kuszyk andR. C. Bradt,J. Amer. Ceram. Soc. 56 (1973) 420.
D. R. Biswas andR. M. Fulrath, “Fracture Mechanics of Ceramics”, Vol. 4, edited by R. C. Bradt, D. P. H. Hasselman and F. F. Lange (Plenum Press, New York and London, 1978) pp. 933–43.
A. G. Evans, University of California, private communication.
A. G. Evans andG. Tappin,Proc. Brit. Ceram. Soc. 29 (1972) 275.
G. K. Bansal,J. Amer. Ceram. Soc. 59 (1976) 87.
D. R. Biswas, Ph.D. Thesis, University of California at Berkeley, LBL-5479 (1976).
Author information
Authors and Affiliations
Additional information
Deceased.
Rights and permissions
About this article
Cite this article
Biswas, D.R., Fulrath, R.M. Effect of surface treatments on strength of PZT polycrystalline ceramics. J Mater Sci 14, 2721–2725 (1979). https://doi.org/10.1007/BF00610645
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00610645