Abstract
The structure of reaction-sintered silicon nitride is studied using scanning electron and optical microscopy at various stages during nitriding, for a range of nitriding and compacting conditions. The strength is then evaluated and interpreted in terms of the microstructure. It is found that fracture always occurs in a brittle manner by the extension of the largest pores. The effects of prolonged annealing in air above 1000† C on both the structure and strength are investigated. At 1400† C, cristobalite is formed. If the temperature is then maintained above 250† C, the strength is enhanced, but below this temperature the oxide layer cracks and reduces the strength.
Similar content being viewed by others
References
N. L. Parr and E. R. W. May, Proc. Brit. Ceram. Soc. 7 (1967) 81.
D. J. Godfrey, Metals and Materials (1968) 305.
D. E. Stoddart and R. P. graham, Materials Towards the 70's (1969) 20.
P. Grierson, K. H. Jack, and S. Wild, Ministry of Defence Contract N/CP.61/9411/67/4B/MP.387, Progress Report No. 1, (1968).
P. L. Pratt, “Mechanical Properties of Engineering Ceramics”, edited by W. W. Kriegel and H. Palmour (Interscience Publishers, New York, 1961) p. 507.
D. S. Thompson, and P. L. Pratt, Proc. Brit. Ceram. Soc. 6 (1966) 37.
Idem, “Sciencs of Ceramics”, Vol. 3, edited by G. H. Stewart (Academic Press Inc., London, 1967) p. 33.
E. Glenney and T. A. Taylor, Powder Metallurgy 1–2 (1958) 189.
D. E. Lloyd, “Special Ceramics”, Vol. 4, edited by P. Popper (Academic Press Inc., London, 1968) p. 165.
G. C. Deeley, J. M. Herbert, and N. C. Moore, Powder Metallurgy 8 (1961) 145.
N. L. Parr, R. Sands, P. L. Pratt, E. R. W. May, C. R. Shakespeare, and D. S. Thompson, ibid 8 (1961) 145.
A. G. Evans and R. W. Davidge, J. Nucl. Mt. 33 (1969) 249.
R. W. Davidge and G. Tappin, J. Mater. Sci. 3 (1968) 165.
A. G. Evans and R. W. Davidge, Phil. Mag. 20 (1969) 373.
R. W. Davidge and G. Tappin, Proc. Brit. Ceram. Soc. 15 (1970) in press.
T. R. Wilshaw, private communication.
W. F. Brown and J. E. Srawley (ASTM 1967) STP 410, p.13.
A. G. Evans, D. Gilling, and R. W. Davidge, J. Mater. Sci. 5 (1970) 187.
D. M. Marsh, Proc. Roy. Soc. A279 (1964) 420.
A. S. Tetelman and A. J. Mcevily, “Fracture of Structural Materials” (John Wiley and Sons Inc., New York, 1967) p. 64.
R. A. Sack, Proc. Phys. Soc. 58 (1946) 729.
R. W. Davidge, unpublished data.
R. J. Lumby and R. F. Coe, Proc. Brit. Ceram. Soc. 15 (1970) in press.
U. R. Evans, “The Corrosion and Oxidation of Metals”, First Supplementary Vol. (Arnold, London, 1968).
W. D. Kingery, “Introduction to Ceramics” (John Wiley and Sons Inc, New York, 1960) 483.
B. A. Proctor, I. Whitney, and J. W. Johnson, Proc. Roy. Soc. A297 (1967) 534.
R. M. Spriggs, J. B. Mitchell, and T. Vasilos, J. Amer. Ceram. Soc. 47 (1964) 323.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Evans, A.G., Davidge, R.W. The strength and oxidation of reaction-sintered silicon nitride. J Mater Sci 5, 314–325 (1970). https://doi.org/10.1007/BF00552282
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00552282