A method was developed to improve the interfacial bonding between hydroxyapatite and a biodegradable copolymer PolyactiveTM 70/30. Hydroxyapatite was first surface modified by the polyelectrolytes polyacrylic acid or poly(ethylene-co-maleic acid) in aqueous solutions. Subsequently the surface-modified hydroxyapatite was used as filler in composites with PolyactiveTM 70/30. The strength, elongation at break and elastic modulus of the composite in aqueous environment were significantly improved by this method. Based on these experimental results, it is believed that the interface improvement is due to hydrogen bonding and/or dipole interactions formed between polyelectrolyte molecules and polyethylene glycol segments in the polymer matrix. Due to the introduction of interfacial bonding by using such method, a new biodegradable bone-bonding composite can be made.
Similar content being viewed by others
References
W., Bonfield, in “Materials characteristics vs. in vivo behaviour”, edited by P., Ducheyne and J. E., Lemons, (New York Academy of Science, New York, 1988) p. 137.
K. E., Tanner, C., Doyle and W., Bonfield, in “Clinical implant materials; advances in biomaterials”, Vol. 9 (Elsevier Science, Amsterdam, 1990) p. 149.
C. C. P. M., Verheyen, J. R.De, Wijn, C. A.Van, Blitterswijk, P. M., Rozing and K.De, Groot, in “Bone-bonding biomaterials”, edited by P., Ducheyne, T., Kokubo and C. A.van, Blitterswijk (Reed Healthcare Communications, Leiderdorp, Netherlands, 1992) p. 153
M., Wang, D., Porter and W., Bonfield, Brit. Ceram. Trans. 93 (1994) 91.
W. R., Walsh, M., Ohna and N., Guzelsu, J. Mater. Sci. Mater. Med. 5 (1994) 72.
E. M., Raif and M. F., Harmand, Biomaterials 14 (1993) 978.
D., Bakker, J. J., Grote, C. M. F., Vrouenraets, S. C., Hesseling, J. R.De, Wijn, C. A.Van, Blitter-Swijk, in “Clinical implant materials”, edited by G., Heimke, U., Stoltese and A. J. L., Lee (Elsevier Science, Amsterdam, 1990) p. 99.
C. A.Van, Blitterswijk, D., Bakker, H., Lenders, J. V. D., Brink, S. C., Hesseling, P., Bovell, A. M., Radder, R. J., Sakker, M. L., Gallard, P. H., Heinze, G. J., Beumer, in “Bone-bonding biomaterials”, edited by P., Ducheyne, T., Kokubo and C. A.van, Blitterswijk (Reed Healthcare Communications, Leiderdorp, Netherlands, 1992) p. 153.
J. A., Jansen, J. E.De, Ruijter, P. T. M., Jansen and Y. G. C. J., Pquay, Biomaterials 16 (1995) 819.
K. L., Smith, A. E., Winslow and D. E., Peterson, Ind. Eng. Chem. 51 (1959) 1361.
J. C., Skinner, H. J., Prosser, R. P., Scott and A. D., Wilson, Biomaterials 7 (1986) 438.
J., Ellis, A. M., Jacson, R. P., Scott and A. D., Wilson, Biomaterials 11 (1990) 379.
F. E., Bailey and J. V., Koleske, in “Poly(etheylene oxide)”, (Academic Press, New York, 1976) Chapter 5.
R. Z., Legros, Clin. Mater. 114 (1993) 65.
R. Z., Legros, G., Daculsi, I., Orly, M., Gregoire, M., Heughebaert, M., Gineste and R., Kijkowska, in “Bone-bonding biomaterials”, edited by P., Ducheyne, T., Kokubo and C. A.van, Blitterswijk (Reed Healthcare Communications, Leiderdrop, Netherlands, 1992) p. 201.
C. A.Van, Blitterswijk, Y. P., Bovell, J., Fiach, H., Leender, I. V. D., Brink, J.De, Bruijn, in “Hydroxyapatite coated hip and knee arthroplasty”, edited by J. A., Epinette, and R. G. T., Geesink, (Expansion Scientifique Francaise, Paris, 1995) p. 33.
S. I., Stupp and G. W., Ciegler, J. Biomed. Mater. Res. 26 (1992) 169.
O. N., Tretinnikov, K., Kato and Y., Ikada, J. Biomed. Mater. Res. 28 (1994) 1365.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Liu, Q., De Wijn, J.R., Bakker, D. et al. Surface modification of hydroxyapatite to introduce interfacial bonding with polyactiveTM 70/30 in a biodegradable composite. J Mater Sci: Mater Med 7, 551–557 (1996). https://doi.org/10.1007/BF00122178
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00122178