Abstract
The R-curve method was used to characterize the stable crack growth and the unstable ductile fracture of 3 mm thick polycarbonate sheets. In order to delimit the field of application of this method, several parameters describing the crack growth resistance were employed. The effect of specimen size and geometry was also studied. Besides limitations linked to test specimens size, the different parameters used are shown to aptly describe the tearing process of this material. When the plane stress region is dominant, the J-integral appears to be as a parameter well adapted to characterize ductile fracture.
Résumé
On a utilisé la méthode de la courbe R pour caractériser la croissance stable d'une fissure et la rupture ductile instable dans le cas de feillards de polycarbonate de 3 mm d'épaisseur. Afin de délimiter le champ d'application de cette méthode, on a utilisé divers paramètres décrivant la résistance à la propagation de la fissure. Les effets de la taille de l'éprouvette et de sa géométrie ont été également étudiés. On montre que les différents param`etres utilisés indiquent les limitations propres à la taille des éprouvettes et décrivent bien le processus d'arrachement qui caractérise le comportement de ce matériau. Lorsqu'il y a prédominance d'une région d'état plan de tension, l'intégrale J apparaît être un paramètre bien adapté à la caractérisation d'une rupture ductile.
Similar content being viewed by others
References
J.G. Williams, Fracture Mechanics of Polymers, Ellis Horwood-Wiley (1984).
M.K.V. Chan and J.G. Williams, International Journal of Fracture 23 (1983) 145–159.
S. Hashemi and J.G. Williams, Polymer Engineering Science 26 (1986) 760–767.
R.K. Singh and K.S. Parihar, Journal of Materials Science 21 (1986) 3921–3926.
G.R. Irwin, “Fracture Testing of High Strength Sheet Materials under Conditions Appropriate for Stress Analysis”, report 5486, U.S. Naval Research Laboratory (1960).
J.M. Krafft, A.M. Sullivan and R.W. Boyle, in Proceedings of Crack Propagation Symposium, Cranfield, Vol. 1 (1961) 8–28.
ASTM Committee E24, Task Group E24.01, Tentative Recommended Practice for R-Curve Determination. ASTM E 561-78T.
W.F. Brown and J.E. Strawley, ASTM STP 410, ASTM (1966).
E. Pauchet, Thèse de Docteur-Ingénieur, Institut National Polytechnique de Lorraine (1985).
D.E. McCabe and J.D. Landes, Transactions of the ASME 100 (1978) 258–268.
P.S. Theocaris and E.E. Gdoutos, Experimental Mechanics (1975) 169–177.
D.R. Rice, in Fracture: An Advanced Treatise, H. Liebowitz (ed.) Vol. 2., Academic Press, New York (1968) 191–311.
S.J. Garwood, J.N. Robinson and C.E. Turner, International Journal of Fracture 11 (1975) RCR 528–530.
J.R. Rice, P.C. Paris and J.G. Merkle, ASTM STP 536, ASTM (1972) 231–245.
J.A. Begley and J.D. Landes, ASTM STP 514, ASTM (1972) 1–33.
S. Shimizu and S. Kawano, in Advances in Fracture Research, Proceedings of the Fifth International Conference on Fracture, Cannes, D. François (ed.), Vol. 4, Pergamon Press (1981) 1675–1682.
H. Parvin and J.G. Williams, International Journal of Fracture 11 (1975) 963–972.
H. Parvin and J.G. Williams, Journal of Materials Science 10 (1975) 1883–1888.
R.A.W. Fraser and J.M. Ward, Polymer 19 (1978) 220–224.
V. Kumar and C.F. Shih, ASTM STP 700, ASTM (1980) 406–438.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Schmit, F., Bouvart, D. & Francois, D. Ductile fracture characterization of polycarbonate by the R-curve method. Int J Fract 43, 83–96 (1990). https://doi.org/10.1007/BF00036178
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00036178