Synthesis of mesoporous silica spheres utilizing in tandem with POSS-based block copolymer and anion surfactant as dual-template
- 239 Downloads
In this work, novel mesoporous silica spheres were prepared by calcination of golf-shaped silica microspheres, which were fabricated via a typical sol-gel method by using synthetic amphiphilic block copolymer poly(acrylate isobutyl polyhedral oligomeric silsesquioxane)-b-poly(dimethylaminoethyl methacrylate co-styrene)) (PAPOSS-b-(PDMAEMA-co-PSt) and anionic surfactant sodium dodecyl sulfate (SDS) as dual-template. Firstly, three different POSS-based block copolymers were synthesized through subsequent homopolymerization of acrylate isobutyl POSS and chain extension of dimethylaminoethyl methacrylate (DMAEMA) and styrene with various feed ratios via reversible transfer radical polymerization (RAFT). These amphiphilic block polymers and SDS were utilized as cooperative template to golf-shaped silica microspheres. The electrostatic interaction between protonated PDMAEMA segments and anion surfactant as well as the strong interaction between PAPOSS segments and silicon source plays the dominant role in forming golf-shaped silica spheres. Moreover, the surface morphology of silica spheres can be tuned by varying molar ratio of PDMAEMA/PAPOSS. The resulting golf-shaped silica microspheres were further calcined to give mesoporous silica spheres which exhibited a BET surface area of 1031 m2 g−1, a total pore volume of 0.826 cm3 g−1, and a narrow pore size distribution centered at 3.20 nm.
KeywordsMesoporous silica spheres POSS-based block copolymer Golf-shaped Dual-template
This work was financially supported by the National Natural Science Foundation of China (51273164, 51673161), the Scientific and Technological Innovation Platform of Fujian Province (2014H2006, 2014I2005), Xiamen science and technology plan project (3502Z20171002), and Key Project of Fujian Department Science and Technology (2013HZ0005-1).
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 3.Lai CY, Trewyn BG, Jeftinija DM, Jeftinija K, Xu S, Jeftinija S, Lin VSY (2003) A mesoporous silica nanosphere-based carrier system with chemically removable CdS nanoparticle caps for stimuli-responsive controlled release of neurotransmitters and drug molecules. J Am Chem Soc 125(15):4451–4459CrossRefPubMedGoogle Scholar
- 16.Wang HJ, Jeong HY, Imura M, Wang L, Radhakrishnan L, Fujita N, Castle T, Terasaki O, Yamauchi Y (2011) Shape-and size-controlled synthesis in hard templates: sophisticated chemical reduction for mesoporous monocrystalline platinum nanoparticles. J Am Chem Soc 133(37):14526–14529CrossRefPubMedGoogle Scholar